Rundqvistite-(Ce), ideally Na3(Sr3Ce)(Zn2Si8O24), is a new mineral from the Darai-Pioz alkaline massif, Tien-Shan Mountains, Tajikistan. The mineral occurs as elongated grains up to 0.1 mm long and up to 0.03 mm thick embedded in quartz–pectolite aggregate in a silexite-like peralkaline pegmatite. Associated minerals are quartz, fluorite, pectolite, baratovite, aegirine, leucosphenite, neptunite, reedmergnerite, orlovite, sokolovaite, mendeleevite-(Ce), odigitriaite, pekovite, zeravshanite, kirchhoffite and garmite. The mineral is colourless with a vitreous lustre and a white streak, brittle, Dmeas. is 3.70(2) and Dcalc. is 3.709 g/cm3. Rundqvistite-(Ce) is monoclinic, space group P21/c, a = 5.1934(16), b = 7.8934(16), c = 26.011(5) Å, β = 90.02(3)° and V = 1066.3(4) Å3. The chemical composition of rundqvistite-(Ce) is SiO2 40.17, La2O3 2.64, Ce2O3 7.55, Pr2O3 0.80, Nd2O3 2.43, Sm2O3 0.33, Eu2O3 0.09, Gd2O3 0.24, Tb2O3 0.18, Dy2O3 0.21, PbO 1.03, SrO 19.83, FeO 0.37, ZnO 13.08, CaO 2.55, Na2O 8.04, total 99.54 wt.%. The empirical formula calculated on 24 O apfu (atoms per formula unit) is Na3.10Sr2.29Ca0.54Pb0.06(Ce0.55La0.19Nd0.17Pr0.06Sm0.02Gd0.02Eu0.01Tb0.01Dy0.01)Σ1.04Zn1.92Fe0.06 Si8.00O24 Z = 2. The structural formula based on refined site-occupancies is (Na2.94Sr0.06)Σ3.00 [(Sr2.23Ca0.54Pb0.06Na0.13)Σ2.96Ln3+1.04]Σ4.00[(Zn1.92Fe2+0.06)Σ1.98Si8O24], where Ln3+1.04 = (Ce0.55La0.19Nd0.17Pr0.06Sm0.02Gd0.02Eu0.01Tb0.01Dy0.01)Σ1.04. The crystal structure of rundqvistite-(Ce) was refined to R1 = 2.76% on the basis of 3184 unique reflections [F > 4σ|F|]. In rundqvistite-(Ce), the main structural unit is a (Zn2Si8O24)12– sheet parallel to (100). In the sheet, the Si and Zn tetrahedra form four-, five- and eight-membered rings. The interstitial cations at the Na and M(1–3) sites sum to [Na3(Sr3Ce)]12– apfu. The Na and M(1–3) polyhedra share common edges to form a layer. Rundqvistite-(Ce) is a structural analogue of vladykinite, ideally Na3Sr4(Fe2+Fe3+)Si8O24. Rundqvistite-(Ce) and vladykinite are related by the following substitution: [8]Ce3+ + [4](Zn2+)2 ↔ [8]Sr2+ + [4](Fe2+Fe3+). The mineral is named after Dmitry Vasilievich Rundqvist (1930–2022), a prominent Russian geologist and an expert on the geology of ore deposits, metallogeny and mineralogy of Precambrian rocks.

Hakite-(Cd), hakite-(Fe) and hakite-(Zn) are new minerals belonging to the tetrahedrite group and forming, along with hakite-(Hg), the hakite series. They have been discovered in samples collected from the Bytíz deposit, in the uranium and base-metal Příbram ore district, Central Bohemia, Czech Republic. They occur as anhedral grains, up to 300 μm in size, in a calcite gangue, associated with clausthalite, cadmoselite, hakite-(Hg) [for hakite-(Cd)], berzelianite, bukovite, bytízite, crookesite, chaméanite, eskebornite, příbramite, the not yet approved giraudite-(Hg) and giraudite-(Cu), hakite-(Hg), umangite, chalcopyrite, tetrahedrite-(Zn) and a new Cu–As selenide [for hakite-(Fe) and -(Zn)]. The three new species are black, with a metallic lustre. Mohs hardness is ca. 3½–4; calculated density is 6.019 (Hak-Cd), 6.011 (Hak-Fe) and 6.081 g.cm–3 (Hak-Zn). In reflected light, they are isotropic, pale grey with bluish (Hak-Cd) or brownish (Hak-Fe and Hak-Zn) shades. Empirical formulae of hakite-(Cd), hakite-(Fe), and hakite-(Zn) are Cu9.71Ag0.24Cd1.51Hg0.43Zn0.03(Sb3.94As0.13)Σ4.07Se11.35S1.57, Cu10.11Ag0.18Fe0.81Zn0.50Hg0.26(Sb3.72As0.41)Σ4.13Se12.65S0.12, and Cu10.03Ag0.24Zn0.61Fe0.53Hg0.45(Sb3.55As0.60)Σ4.15Se12.82S0.08, respectively. These formulae correspond to the end-member formulae Cu6(Cu4Cd2)Sb4Se13 (Hak-Cd), Cu6(Cu4Fe2)Sb4Se13 (Hak-Fe), and Cu6(Cu4Zn2)Sb4Se13 (Hak-Zn). All these new members of the hakite series are cubic, I$\bar{4}$3m, Z = 2, with unit-cell parameters a = 10.8860(6) Å, V = 1290.0(2) Å3 (Hak-Cd); a = 10.7983(4) Å, V = 1259.12(14) Å3 (Hak-Fe); and a = 10.8116(14) Å, V = 1263.8(5) Å3 (Hak-Zn). These species are isotypic with the other members of the tetrahedrite group, and their crystal structures have been refined on the basis of single-crystal X-ray diffraction data down to R1 values of 0.0230 (Hak-Cd), 0.0254 (Hak-Fe), and 0.0302 (Hak-Zn). These structural data allow us to describe the S-to-Se partitioning in hakite-series minerals and to understand the mechanisms avoiding too short Me–Se distances in these selenides.

Clogauite, ideally PbBi4Te4S3 is the new n = 1 member of the aleksite series, PbnBi4Te4Sn+2, where n is the homologue number. Clogauite is named from the type locality, the Clogau gold mine, Dolgellau Gold belt, Gwynedd, North Wales, United Kingdom. The mineral and name have been approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2023–062). The aleksite series is an accretional homologous series in which each member is derived from the same 5-atom tetradymite archetype. Clogauite crystallises in the trigonal crystal system (space group: P$\bar{3}$m1, #164). Three distinct polytypes of clogauite are recognised, corresponding to identical chemistry but different layer sequences, expressed as (57), (5559) and (557.559), respectively, in reference to the number of atoms in individual layer sequences. These are clogauite-12H, a = 4.277(4) Å, c = 23.46(14) Å, V = 371.598 Å3 and Z = 1; clogauite-24H, a = 4.278(4) Å, c = 46.88(31) Å, V = 743.053 Å3 and Z = 2; and clogauite-36H, a = 4.278(4) Å, c = 70.36(32) Å, V = 1115.283 Å3 and Z = 3. Clogauite is opaque, with a pale grey colour in reflected light. Reflectance is higher than tetradymite or galena. Bireflectance and anisotropy are strong. Structural data were determined from measurement of atomic-scale HAADF STEM imaging showing the internal arrangement of component atoms and characteristic selected area electron diffraction patterns for each polytype. The structures were then further constrained from ab initio total energy calculations and structure relaxation using density functional theory (DFT) using the measured parameters as input data. The relaxed crystal structure for each polytype was modelled to generate crystallographic information files (cif). STEM and electron diffraction simulations based on the crystallographic information data obtained from the DFT calculations show an excellent match to the empirical measurements.

Markwelchite, ideally TlPbSbS3, is a new mineral from the hydrothermal deposit of Jas Roux, Hautes-Alpes, France. It occurs as a black anhedral crystal associated closely with protochabournéite. Microhardness measurements (VHN15) gave a mean value of 197 kg/mm2 corresponding to a Mohs hardness of ~3–4. In plane-polarised incident light, markwelchite is grey in colour. Under crossed polars, it is distinctly anisotropic with greyish white to bluish rotation tints, with bright red internal reflections. Reflectance percentages (Rmin and Rmax) are: 28.5, 31.5 (471.1 nm); 28.3, 30.7 (548.3 nm); 27.9, 30.3 (586.6 nm); and 27.6, 29.8 (652.3 nm). The mean of 5 electron microprobe spot analyses gave Tl 34.67(45), Pb 31.86(25), Sb 15.06(15), As 2.37(5), S 15.35(20), total 99.31 wt.%, corresponding, on the basis of a total of 6 atoms per formula unit and structural results, to Tl1.063Pb0.964(Sb0.775As0.198)Σ0.973S3.000. Single-crystal X-ray diffraction studies revealed that markwelchite is isotypic with richardsollyite, TlPbAsS3. It is monoclinic, space group P21/c, with the following unit-cell parameters: a = 8.9144(3), b = 8.4513(3), c = 8.6511(3) Å, β = 108.723(4)°, V = 617.27(4) Å3 and Z = 4. The five strongest observed powder-diffraction lines [d in Å (Irel)(hkl)] are: 3.88 (100)($\bar{2}$11); 3.78 (90)(210); 3.29 (90)(102); 2.73 (85)($\bar{1}$13); and 2.93 (75)(022). The crystal structure can be described as formed by (100) [Me2(SbS3)]– layers sandwiching the Me1+ cations. The Me1 site has a seven-fold coordination, whereas the Me2 site has an 6+2 coordination corresponding to a distorted, bicapped trigonal prismatic coordination, and the Sb site displays a trigonal pyramidal coordination with three S atoms and Sb at the apex.

The name markwelchite honours Dr Mark D. Welch of the Natural History Museum, London, UK.

The new mineral has been approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2024–001). A discussion on the relationships between markwelchite and synthetic TlPbSbS3 is also provided.

Sulfosalt assemblages in a specimen from the Boliden Au–Cu–(As) deposit in northern Sweden, comprise micrometre to nanometre scale intergrowths of Se-rich izoklakeite and tintinaite with average formulae and calculated homologue number (N) given as: (Cu1.88Fe0.18)2.06(Pb22.92Ag1.47Cd0.01Zn0.01)24.41(Sb13.12Bi8.69)21.8(S50.19Se6.43Te0.12)56.73, N = 3.83, and (Cu1.31Fe0.74)2.05(Pb10.58Ag0.18Cd0.05Zn0.02)10.83(Sb10.2Bi5.23)15.43(S32.22Se2.46)34.7, N = 2.05, respectively. Tintinaite coexists with (Bi, Se)-rich jamesonite. High-angle annular dark field scanning transmission electron microscopy (HAADF STEM) imaging reveals chessboard structures comprising PbS and SnS modules with the number of atoms in the octahedral (M) sites counted as: n1 = 18 and n2 = 8 for tintinaite and n1 = 30 and n2 = 16 for izoklakeite. The homologue number can be calculated using the formula: N = (n1/6)–1 and N = n2/4 for PbS and SnS modules giving NTti = 2 and NIz = 4. A new N = 3 homologue, defined by n = 12 and n = 24 SnS and PbS modules, respectively, is identified as single or double units within areas with intergrowths between kobellite and izoklakeite. HAADF STEM imaging also reveals features attributable to lone electron pair micelles within the Sb-rich kobellite homologues. Atomic-resolution EDS STEM chemical mapping of Pb–Bi–Sb-sulfosalts shows a correlation with crystal structural modularity. The maps also highlight sites in the SnS modules of tintinaite in which Sb > Bi. Coherent nanoscale intergrowths between tintinaite and izoklakeite define jigsaw patterns evolving from chessboard structures and are considered to have formed during co-crystallisation of the two phases. Displacement textures and crosscutting veinlets (a few nm in width) are interpreted as evidence for superimposed syn-metamorphic deformation and are associated with the redistribution of Bi and Se. Imaging and mapping using HAADF STEM techniques is well suited to characterisation of Pb–Sb–Bi-sulfosalt phases, offering largely untapped potential to unravel the evolution of chessboard structures with applications across mineralogy but also extending into allied fields.

The new mineral theuerdankite, ideally Ag3AsO4, was found in the Alter Theuerdank Mine, Beerberg, St. Andreasberg, Goslar District, Lower Saxony, Germany. Theuerdankite occurs as aggregates of anhedral grains up to 3 mm in size, growing in cavities of strongly supergene-weathered material consisting of native silver and chlorargyrite (but with calcite present). It is dark violet, changing to reddish and black when exposed to the air and light. It has a grey to violet grey streak; when readily fresh, its streak is brownish-red. The Mohs hardness is ~2. It is brittle with no observable cleavage or parting and with a conchoidal fracture. The calculated density is 6.620 g⋅cm–3. In reflected light, theuerdankite is dark grey with a pinkish tint, with no observable bireflectance, pleochroism, or anisotropy. It shows dark red internal reflections. The reflectance values for wavelengths recommended by the Commission on Ore Mineralogy of the International Mineralogical Association are (R, %): 13.3 (470 nm), 12.8 (546 nm), 12.7 (589 nm) and 12.5 (650 nm). The empirical formula (based on 4 apfu) is Ag3.00As1.00O4. Theuerdankite is cubic, space group P$\bar{4}$3n, a = 6.144(2) Å, V = 231.93(13) Å3 and Z = 2. The six strongest powder X-ray diffraction lines are [dobs in Å, (I) hkl]: 3.0736, (22) 200; 2.7502, (100) 210; 2.5106, (55) 211; 1.7050, (36) 320; 1.6249, (44) 321; and 1.3412, (17) 421. The crystal structure of theuerdankite (R1 = 1.69% for 519 reflections having I > 3σ(I)), is isotypic to those of synthetic Ag3AsO4 and Ag3PO4. The Gram–Charlier development describing the higher-order tensors representing the atomic displacement parameters of the silver atom was implemented, documenting that silver tends to behave anharmonically in the theuerdankite structure at room temperature.

The high-pressure behaviour of inderborite [ideally CaMg[B3O3(OH)5]2(H2O)4⋅2H2O, space group C2/c with a ≈ 12.14, b ≈ 7.43, c ≈ 19.23 Å and β ≈ 90.3° at room conditions] has been studied by two in situ single-crystal synchrotron X-ray diffraction experiments up to ~10 GPa, using He as pressure-transmitting fluid. Between 8.11(5) and 8.80(5) GPa, inderborite undergoes a first-order phase transition to its high-pressure polymorph, inderborite-II (with a ≈ 11.37, b ≈ 6.96, c ≈ 17.67 Å, β ≈ 96.8° and ΔV ≈ 7.0%, space group unknown). The isothermal bulk modulus (KV0 = β−1P0,T0, where βP0,T0 is the volume compressibility coefficient) of inderborite was found to be KV0 = 41(1) GPa. The destructive nature of the phase transition prevented any structure resolution of inderborite-II or even the continuation of the experiments at pressures higher than 10.10(5) GPa. In the pressure range 0–8.11(5) GPa, the compressional anisotropy of inderborite, indicated by the ratio between the principal components of the Eulerian finite unit-strain ellipsoid, is ɛ1:ɛ2:ɛ3 = 1.4:1.05:1. The deformation mechanisms at the atomic scale in inderborite are here described. Our findings support the hypothesis of a quasi-linear correlation between the total H2O content and P-stability range in hydrated borates, as the pressure at which inderborite undergoes the phase transition falls in line with most of the hydrate borates studied at high-pressure so far.

A rounded fragment of a multicoloured tourmaline crystal (2.5 cm diameter), collected from the secondary gem deposit of Mavuco, Alto Ligoña pegmatite district, Mozambique, has been investigated using a multi-analytical approach, with the objective of reconstructing its growth history. The sample represents a core-to-rim section, perpendicular to the c axis, of a crystal characterised by a variety of colours. These change from a black core to an intermediate zone with a series of colours, yellow, blue–green and purple, to a final dark-green prismatic overgrowth. These changes are the result of a wide variation in Fe, Mn, Ti and Cu concentrations and their redox state. The black core is characterised by enrichment in Fe and Mn, with iron present in its divalent state. The yellow zone shows a progressive depletion in Fe and its colouration is caused by Mn2+ and Mn2+-Ti4+ IVCT interactions. The progressive decrease in Mn coupled with the absence of Ti, and the lack of Fe, implies that Cu2+ acts as the only chromophore in the pale blue–green zone. The dominant colour-causing agent of the purplish zone is Mn3+, denoting a change in redox environment; however, even though the amount of Cu remains significant, its chromophore effect is obscured by Mn3+. The dark-green prismatic overgrowth, characterised by a sharp increase in Fe, Mn and also Ca, is interpreted as a late-stage partial re-opening of the geochemical system. This occurrence could potentially be related to mechanical instability of the cavity in which the crystal grew.

Sperlingite, (H2O)K(Mn2+Fe3+)(Al2Ti)(PO4)4[O(OH)][(H2O)9(OH)]⋅4H2O, is a new monoclinic member of the paulkerrite group, from the Hagendorf-Süd pegmatite, Oberpfalz, Bavaria, Germany. It was found in corrosion pits of altered zwieselite, in association with columbite, hopeite, leucophosphite, mitridatite, scholzite, orange–brown zincoberaunite sprays and tiny green crystals of zincolibethenite. Sperlingite forms colourless prisms with pyramidal terminations, which are predominantly only 5 to 20 μm in size, rarely to 60 μm and frequently are multiply intergrown and are overgrown with smaller crystals. The crystals are flattened on {010} and slightly elongated along [100] with forms {010}, {001} and {111}. Twinning occurs by rotation about c. The calculated density is 2.40 g⋅cm–3. Optically, sperlingite crystals are biaxial (+), α = 1.600(est), β = 1.615(5), γ = 1.635(5) (white light) and 2V (calc.) = 82.7°. The optical orientation is X = b, Y = c and Z = a. Neither dispersion nor pleochroism were observed. The empirical formula from electron microprobe analyses and structure refinement is A1[(H2O)0.96K0.04]Σ1.00 A2(K0.52□0.48)Σ1.00 M1(Mn2+0.60Mg0.33Zn0.29Fe3+0.77)Σ1.99 M2+M3(Al1.05Ti4+1.33Fe3+0.62)Σ3.00(PO4)4 X[F0.19(OH)0.94O0.87]Σ2.00[(H2O)9.23(OH)0.77]Σ10.00⋅3.96H2O. Sperlingite has monoclinic symmetry with space group P21/c and unit-cell parameters a = 10.428(2) Å, b = 20.281(4) Å, c = 12.223(2) Å, β = 90.10(3)°, V = 2585.0(8) Å3 and Z = 4. The crystal structure was refined using synchrotron single-crystal data to wRobs = 0.058 for 5608 reflections with I > 3σ(I). Sperlingite is the first paulkerrite-group mineral to have co-dominant divalent and trivalent cations at the M1 sites; All other reported members have Mn2+ or Mg dominant at M1. Local charge balance for Fe3+ at M1 is achieved by H2O → OH– at H2O coordinated to M1.

Zipserite is a new mineral species discovered in a sample collected from the old mine dumps of the abandoned epithermal deposit Nagybörzsöny in Hungary. Zipserite occurs as anhedral to subhedral, lath-like grains, up to 500 μm in size, in hydrothermally strongly altered rocks. It is found at a contact between bismuth and bismuthinite, also associated with rare ikunolite and joséite-A. Zipserite is silvery white with a metallic lustre. Mohs hardness is ca. 2–3 and the calculated density is 7.815 g.cm–3. In reflected light, zipserite is grey–white, with colour and reflectance essentially matching those of bismuthinite. Bireflectance is weak, internal reflections not present. Anisotropy is moderately strong, with dark blue and grey colours of anisotropy. Reflectance values for the four Commission on Ore Mineralogy wavelengths of zipserite in air [Rmax, Rmin (%) (λ in nm)] are: 48.4, 46.4 (470); 47.8, 45.9 (546); 47.8, 45.8 (589); and 47.5, 45.6 (650). The empirical formula, based on electron-microprobe analyses, is (Bi4.74Pb0.31)Σ5.05(S3.38Se0.56Te0.02)Σ3.96, that can be simplified as Bi5(S,Se)4. The ideal end-member formula of zipserite is Bi5S4, which requires Bi 89.07 and S 10.93, total 100 wt.%. Zipserite possesses a fascinating crystal structure. The average structure is trigonal, with space group P$\bar{3}$m, a = 4.162(1) Å, c = 16.397(1) Å, V = 245.94(4) Å3 and Z = 2. The structure is built by the alternation of a double bismuth layer Bi2 and the Bi3S4 block which is a three octahedra thick layer. Its general formula can be expressed as Bi2 + Bi3S4, which corresponds directly to the observed stacking. At 98 K, the structure can be described using the superspace formalism with an R-centred trigonal unit cell a = 4.209(2) Å, c0 = 5.616(6) Å, a modulation vector q ≈ 4/3 c* and the superspace group R$\bar{3}$m(00γ)00. Zipserite is not only a new mineral but also the first named member of a new sub-group of compounds within the broader family of bismuth chalcogenides, characterised by complex stacking of structural units (Bi2 layers and Bi3S4 blocks). Some of these phases are being investigated as promising thermoelectric materials and synthetic analogues of zipserite could also be inspected for similar physical properties.

Qeltite (IMA2021–032), ideally Ca3Ti(Fe2Si)Si2O14, was found in gehlenite–rankinite–wollastonite paralava from a pyrometamorphic rock of the Hatrurim Complex at Nabi Musa locality, Judean Desert, West Bank, Palestine. It generally occurs as light-brown flattened crystals up to 40–50 μm in length and less than 5 μm in thickness. Its aggregates reach 100–200 μm in size. Its empirical crystal chemical formula based on 14 O is: (Ca2.96Sr0.02Mn0.01)Σ2.99Ti4+(Fe3+1.59Si0.60Al0.43Ti4+0.38Cr0.01)Σ3.01(Si1.99P0.01)Σ2O14. The strongest reflections in its calculated X-ray diffraction pattern are [d, Å, (I, %), hkl]: 3.12, (100), 111; 2.85, (61), 201; 2.85, (48), 021; 2.32, (45), 211; 6.93, (31), 100; and 1.81, (30), 212. Qeltite is trigonal and crystallises in the noncentrosymmetric P321 space group, with a = 8.0077(5) Å, c = 4.9956(4) Å, V = 277.42(4) Å3 and Z = 1. Its microhardness VHN25 is 708(17) kg/mm2 and its hardness on the Mohs scale is ~6. Its calculated density is 3.48 g/cm3. It was found in fine-grained mineral aggregates within coarse-grained main minerals of rankinite–gehlenite paralava with subordinate wollastonite, Ti-bearing andradite and kalsilite. In these aggregates, the mineral is associated with khesinite, paqueite and pseudowollastonite, indicating a high-temperature genesis (~1200°C). Its crystallisation can be compared with the crystallisation of minerals containing refractory inclusions in meteorites.

Fluor-rossmanite, ideally □(Al2Li)Al6(Si6O18)(BO3)3(OH)3F, is a new mineral of the tourmaline supergroup, found at the Krutaya pegmatite, Malkhan pegmatite field, Zabaykalskiy Krai, Western Siberia, Russia. It forms an intermediate zone up to 3 mm thick in a chemically heterogeneous, concentrically zoned, polychrome tourmaline crystal 3 × 2 cm in size. The new mineral is light pink, transparent with a white streak and a vitreous lustre. It is brittle, with conchoidal fracture. The Mohs hardness is 7. The Dmeas = 3.07(2) g cm–3 and Dcalc = 3.071 g cm–3. Optically, fluor-rossmanite is non-pleochroic, uniaxial (–), ω = 1.647(2) and ɛ = 1.628(2) (589 nm). The empirical formula calculated on the basis of 31 anions (O+OH+F) is: X(□0.46Na0.32Ca0.20Pb0.02)Σ1.00 Y(Al1.84Li1.05Mn0.05Fe2+0.02Ti0.02Cr0.01)Σ2.99 ZAl6.00 T(Si5.79Al0.21)Σ6.00B2.99O27 V(OH)3 W[F0.44(OH)0.20O0.36]Σ1.00. Fluor-rossmanite is trigonal, R3m; the unit-cell parameters are: a = 15.7951(3), c = 7.08646(17) Å, V = 1531.11(7) Å3 and Z = 3. The crystal structure is refined from single-crystal X-ray diffraction data [R = 0.0211 for 1178 unique reflections with I > 2σ(I)]. The new mineral is a ‘fluor-’ species belonging to the X-vacant group of the tourmaline supergroup. The closest end-member compositions of valid tourmaline species are those of rossmanite and fluor-elbaite, to which fluor-rossmanite is related by the substitutions WF– ↔ WOH– and X2□ + YAl3+ ↔ X2Na+ + YLi+, respectively.

Kvačekite is a new mineral species discovered in a sample collected from the now abandoned Bukov uranium mine, western Moravia, Czech Republic. It occurs as rare anhedral grains, up to 15 μm in size, associated with nickeltyrrellite, tyrrellite, berzelianite, hakite-(Zn), hakite-(Cd), eucairite, clausthalite, and gold in calcite gangue. In reflected light, kvačekite is white with a faint yellowish shade; bireflectance, pleochroism and anisotropy are absent. Internal reflections were not observed. Reflectance values for the four COM wavelengths for kvačekite in air [R (%) (λ in nm)] are: 54.9 (470); 53.5 (546); 52.6 (589); and 52.2 (650). The empirical formula, based on electron-microprobe analyses (EPMA), is (Ni0.95Cu0.04Co0.03)Σ1.02Sb1.00(Se0.97S0.01)Σ0.98. The ideal formula is NiSbSe, which requires (in wt.%) Ni 22.63, Sb 46.93, Se 30.44, total 100.00. Kvačekite is cubic, P213, with unit-cell parameters a = 6.09013(13) Å, V = 225.881(15) Å3 and Z = 4. The strongest reflections in the X-ray powder diffraction pattern of synthetic kvačekite [d, Å (I) hkl] are: 3.0458 (11) 200; 2.7242 (100) 201, 210; 2.4867 (71) 211; 1.8632(39) 311; 1.6277(29) 321, 312; and 1.3290 (13) 421. Given the similarity with ullmannite, NiSbS, the crystal structure was refined from the powder X-ray diffraction data starting from those atomic coordinates using the synthetic analogue of kvačekite. Its crystal structure is formed by corner-sharing [NiSb3Se3] octahedra which form a three-dimensional network. The identity of the natural kvačekite and synthetic cubic NiSbSe were confirmed by a study of their chemical composition, reflectance measurements, Raman spectroscopy and electron back-scattered diffraction (EBSD) measurements on the mineral. Kvačekite is named after Milan Kvaček (1930–1993), a prominent Czech mineralogist. The mineral and its name have been approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2023-095).

Ermeloite is a new aluminium phosphate mineral from Galicia, Spain, in the northwest of the Iberian Peninsula. It is the third formally recognised mineral discovered in Galicia since morenosite and cervantite in the 19th Century. The name and symbol (Erm) were approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2021–017a) in recognition of the geographical location where it was found. The mineral occurs as a light blue to white fine aggregate over quartz and microcline associated with wardite. Crystals of ~0.04 mm are transparent and have a waxy lustre. The simplified empirical formula determined using electron microprobe analysis is Al1.02P0.95F0.06O3.88⋅1.06 H2O, which is near to the ideal formula Al(PO4)⋅H2O. The mineral is an alteration product within a phosphate pegmatite. Ermeloite is the second phosphate isostructural with the sulfates of the kieserite group. Single-crystal X-ray diffraction showed that ermeloite crystallises in the monoclinic C2/c space group with cell parameters a = 6.5371(4) Å, b = 7.5670(5) Å, c = 7.1146(5) Å, β = 115.335(2)°, V = 318.08(4) Å3 and Z = 4 at room temperature. Comparative analysis of the crystallographic data, with isostructural phosphates, revealed an interesting behaviour for these compounds.

The lithium sodium borosilicate jadarite, LiNaSiB3O7(OH), was first identified in 2007 in the Jadar basin, Serbia, where it forms the principal ore mineral of one of Europe's largest Li deposits. We report the successful application of the dry-gel conversion technique (DGC) to synthesise a jadarite analogue, via a dry-gel precursor made using sol-gel synthesis and the inclusion of the structure directing agent tetraethylammonium hydroxide (TEAOH). Pawley refinement of powder X-ray diffraction (PXRD) data collected on the synthetic sample was carried out using a monoclinic unit cell in space group P21/c (Whitfield et al., 2007), and gave refined unit cell parameters of a = 6.824(3) Å, b = 13.882(5) Å, c = 7.735(3) Å and β = 124.37(1)° (Rwp = 9.22). Inductively-coupled plasma optical emission spectroscopy (ICP–OES) on the synthetic sample confirmed an empirical formula of Li1.07Na1.40Si0.79B3O7.32(OH), based on three B atoms per formula unit (apfu). The synthetic product was found to be deficient in Si compared to natural jadarite from analysis of PXRD and ICP–OES data. Fourier-transform infrared spectroscopy (FTIR) showed that synthetic jadarite has peaks at 1415 and 1342 cm–1 and between 1180 and 900 cm–1, which are attributed to the presence of trigonal (BO3) and tetrahedral (BO4) borate groups characteristic of the natural jadarite structure, as well as a broad peak at 3441 cm–1 due to the presence of residual TEAOH. Scanning electron microscopy showed similarities in the morphologies between synthetic and natural jadarite particles.

Tetrahedrite-(Cu), Cu12Sb4S13, has been approved as a new mineral species (IMA2022–078) from the Bankov magnesite deposit near Košice, Slovak Republic where it occurs as anhedral grains, up to 0.4 mm across, associated with skinnerite, chalcostibite, famatinite, tetrahedrite-(Fe) and zoned aggregates of tennantite-(Cu) to tennantite-(Fe). Tetrahedrite-(Cu) is steel-grey, with a metallic lustre. Mohs hardness is ca. 3½–4 and calculated density is 5.029 g.cm–3. In reflected light, tetrahedrite-(Cu) is isotropic and grey with a bluish shade. Reflectance data for the four COM wavelengths in air are [λ (nm): R (%)]: 470: 31.1; 546: 30.1; 589: 29.9; and 650: 28.1. The empirical formula, based on electron-microprobe data (mean of 17 spot analyses), is Cu11.42Zn0.26Fe0.19(Sb4.06As0.08)Σ4.14S12.99. The ideal formula is Cu6(Cu4Cu2)Sb4S13, which requires (in wt.%) Cu 45.76, Sb 29.23 and S 25.01, total 100.00. Tetrahedrite-(Cu) is cubic, I$\bar{4}$3m, with unit-cell parameters a = 10.3296(15) Å, V = 1102.2(5) Å3 and Z = 2. Its crystal structure was refined by single-crystal X-ray diffraction data to a final R1 = 0.0347 on the basis of 261 unique reflections with Fo > 4σ(Fo) and 22 refined parameters. Tetrahedrite-(Cu) is isotypic with other tetrahedrite-group minerals. Previous findings of tetrahedrite-(Cu) are reported and some nomenclature issues, related to the Fe and Cu oxidation states, are discussed. At the Bankov deposit, tetrahedrite-(Cu) is related to hydrothermal, most probably Alpine, solutions strongly enriched in Cu, Sb and S.

An attempt to compare and describe the differences in the electron density distribution between two phase structures of AlOOH has been made. High-resolution, high-pressure experiments with α-AlOOH diaspore were conducted using single-crystal synchrotron X-ray diffraction data. A multipole model of experimental electron density in the α-AlOOH single crystal was refined. Simultaneously, similar multipole refinement was conducted for another phase of diaspore (δ-AlOOH), this time based on a previously published data set. Both results were compared and supported by density functional theory (DFT) calculations. Although the results are affected by the limited quality of the data, it is clear that the phase transition caused significant changes in the shape and arrangement of the atomic basins.

Atomic basins are a much better tool to present subtle electron density distribution changes than traditional polyhedra. Straightforward comparison of datasets available in older scientific papers and current datasets is challenging because of differences in data quality and collection parameters. However, augmenting experimental data with computational results can help reveal important information in even incomplete datasets.

Daqingshanite in the Kamthai REE deposit (India) occurs as two paragenetic types: primary granular coarse grained crystals coexisting with primary carbocernaite, baryte and bastnäsite; and as aligned micro-ovoid globules within clasts of Sr-bearing calcite. Carbocernaite forming trellis-type lamellae in some of these calcite clasts do not represent exsolution and are considered as replacement textures as they formed subsequent to daqingshanite. The origins of the textural relations of the microglobules of daqingshanite to their host Sr-calcite cannot be unambiguously determined, although an exsolution origin is not considered feasible. The textures are similar to those of ‘chalcopyrite disease’ and as such could be interpreted as replacement features formed in a low temperature carbothermal environment which should facilitate replacement. Given that daqingshanite is an early crystallising phase it is also possible that cotectic crystallisation with Sr-calcite occurred, followed by subsolidus re-equilibration with recrystallisation along specific crystallographic planes in the calcite. The Kamthai REE deposit is best described as a low temperature carbothermalite microbreccia consisting of a wide variety of clasts resulting from the autobrecciation of rocks formed during, and after, the magmatic to carbothermal transition of an undetermined parental calcite carbonatite-forming magma. Many clasts have been replaced by late stage La-enriched carbothermal fluids mixed with exogenous water during the final low-temperature stage of evolution of the deposit.

Škáchaite (IMA2022–143) is a new mineral species discovered in samples from the hydrothermal vein B117, shaft No. 6 at the Brod deposit of the uranium and base-metal Příbram ore district, central Bohemia, Czech Republic. Škáchaite is a Co-dominant member of the dolomite group and forms anhedral grains up to 50 μm in size and as 20–100 μm thick growth zones in škáchaite–dolomite crystals as a part of carbonate (dolomite, calcite, siderite, spherocobaltite, ankerite, kutnohorite and minrecordite) gangue, associated with native silver, sulfides and arsenides. Škáchaite is pale to bright pink with vitreous lustre. The Mohs hardness is ca. 3½–4, similar to other members of the dolomite group. The calculated density is 3.140 g.cm–3. Škáchaite is optically uniaxial (–); the indices of refraction are ω = 1.741(3) and ɛ = 1.535(3). On the basis of electron-microprobe analyses, its empirical formula is Ca1.00(Co0.45Mg0.38Ca0.08Fe0.05Mn0.03Zn0.01)Σ1.00(CO3)2. The ideal formula is CaCo(CO3)2, which requires (in wt.%) CaO 25.60, CoO 34.21, CO2 40.19, a total of 100.00. Škáchaite is trigonal, R$\bar{3}$, with unit-cell parameters a = 4.8177(18), c = 16.093(7) Å, V = 323.5(2) Å3 and Z = 3. The strongest reflections of the calculated powder X-ray diffraction pattern [d, Å, (Irel, %) hkl] are: 3.704 (13) 10$\bar{2}$; 2.896 (100) 104; 2.409 (15) 110; 2.019 (17) 202; 1.812 (19) 10$\bar{8}$; and 1.792 (16) 11$\bar{6}$. According to the single-crystal X-ray diffraction data (R1 = 0.0304 for 94 reflections with [I > 3σ(I)]), the crystal structure of škáchaite is isotypic with its Mg-analogue, dolomite. The Raman spectrum of škáchaite, as well as the tentative assignment of observed bands, are given in this paper. The mineral is named in honour of Pavel Škácha, a Czech mineralogist and curator of the mineralogical collection of the Mining Museum Příbram, Czech Republic.

Mineral species are known to be heterogeneously distributed throughout the Earth such that a relatively small number of minerals make up a large proportion of the lithosphere while the majority of all known minerals are rare and have been identified at only a small number of locations that frequently exhibit high levels of species richness. Intuitive understandings of mineral scarcity and abundance are reconsidered through the characterisation of the quantitative aspects of spatio-temporal trends in new mineral discovery. Using data drawn from online mineralogical databases, it is found that the Earth's mineral hotspots exhibit an exponential distribution of species abundance, while those same mineral hotspots exhibit a power-law distribution in the number of minerals first recognised at those locations. That is, locations rich in first occurrences are extremely rare, even when considering only the Earth's most species-rich mineral locations. Global distributions of mineral scarcity and abundance can be estimated from the number of mineral-location pairs for each species reported in a database. Two-thirds of all known species have been reported from ten or fewer locations and the frequency distribution of these mineral-location pairs exhibit a power-law distribution that extends with increasing dispersion over several orders of magnitude of mineral abundance. Initially, nearly all minerals are first reported from only their type locality. Over time, additional occurrences of newly discovered minerals are reported at an average rate of one new location per mineral every 5.5 years. As a result, the percentage of minerals that were discovered in a given year that continue to be known only from their type locality is found to decline exponentially over time. However, a few minerals remain known from only their type locality for long periods, including some that were first identified in the 19th Century. Conversely, other recently identified minerals have been subsequently recognised at locations spanning a wide geographic range such that the number of minerals with cosmopolitan distributions is found to increase exponentially over time. Taken together, these several quantitative representations of mineral distributions lend structure and refinement to qualitative and intuitive notions of the scarcity and abundance of Earth's many minerals.