The 10-Å clay components of sedimentary rocks (“illites”) are commonly mixtures of 100% nonexpandable illite and an ordered illite/smectite mixed-layer mineral. If the proportion of the illite/ smectite in a mixture is sufficient to produce a measurable reflection between 33–35°2θ (CuKα radiation) that is noncoincident with an illite reflection, the ratio of component layers and type of interstratification for the mixed-layer mineral can be determined. The identification technique developed in this study rests upon the following experimental findings for ordered illite/smectites of diagenetic origin: (1) the thickness of the illite layer in illite/smectites is 9.97 Å; (2) the thickness of smectite-ethylene glycol complex ranges from 16.7 to 16.9 Å; (3) illite/smectites form a continuous sequence of interstratification types—random, random/IS, IS, IS/ISII, ISII—and each type is related to a specific range of expandability.

The new technique broadens the computer simulation method developed by R. C. Reynolds and J. Hower to include those sedimentary materials which are dominated by the presence of discrete illite, are low in illite/smectite, and, as such, have been described previously only by an “illite crystallinity index.”

The effect of Fe oxidation state on the surface charge (CEC) and solubility of smectites were studied using the <2-μm, Na+-saturated fraction of an Upton, Wyoming; a Czechoslovakian; and a New Zealand montmorillonite; and a Garfield, Washington, nontronite. The reduction of structural Fe3+ in the octahedral sheet of each clay produced a net increase in the negative surface charge of the clay. The observed cation-exchange capacities deviated from the linear relationship predicted by charge-deficit calculations, assuming changes only in the Fe2+/Fe3+ ratio, and reversibly followed Fe reduction according to a 2nd-degree polynomial function. The deviations suggest reversible changes in mineral structure and composition during Fe reduction.

These clays were susceptible to partial dissolution in citrate bicarbonate (CB) and citrate-bicarbonate-dithionite (CBD) solutions. Small amounts of Fe and Si dissolved as a result of Fe reduction in CBD, but affected <1% of the total clay mass except for the Czechoslovakian clay in which 2% of the clay dissolved. Although slightly more Fe dissolved than Si, no change in surface charge was noted. Almost no dissolution of these elements was detected in CB solution. In contrast, significant Al was detected in the CB solution, suggesting a heterogeneous dissolution mechanism. The CEC, however, was unchanged by the CB treatment. These results may be explained by the adsorption of hydrogen ions into the vacated Al3+ sites in the mineral structure. Dissolution seems to have been independent of the effects of Fe oxidation state on surface charge.

Three montmorillonites and a nontronite were reduced by sodium dithionite to obtain different amounts of Fe2+ in their octahedral sites. The mass ratio of water to clay, mw/mc was determined as a function of Fe2+ at several values of the swelling pressure, π. The value mwmc decreased markedly with increasing Fe2+ at each value of π for each clay. Moreover, curves of π vs. mwmc for the different clays were displaced downwards as Fe2+ increased. A straight line was obtained when In(π + 1) was plotted against 1/(mw/mc) however, at some oxidation states of three of the samples this line exhibited a sharp break at a specific value of 1/(w/mc. The slope of the line decreased for each clay as Fe2+ increased, and an increase in Fe2+ was accompanied by an increase in the cation exchange capacity. These observations are thought to be due to a collapse or partial collapse of the superimposed clay layers resulting from the increase in cation-exchange capacity.

In a lateritic pallid zone ilmenite crystals alter via pseudorutile to porous leucoxene grains composed of randomly oriented aggregates of ~0.06 μm anatase crystals. This style of alteration differs from that in beach sands where parallel oriented rutile crystals develop from pseudorutile. Increased Si and Al in the altered grains is due to the crystallization from soil solution of halloysite, kaolinite and gibbsite within pores rather than to the incorporation of these elements into anatase crystals. Manganese was a significant constituent (3.2% Mn2O3) of the original ilmenite but was not retained by the leucoxene grains. The minor constituents Ni, Zn, Cu, Mg, Co and Ca were also lost, but Cr and V were retained.

Smectite close to the pure Fe end member of the nontronite-beidellite series was found in the fine clay separated from a 354-cm deep sediment core in the southwestern Pacific Basin. The mineral has a b-axis of 9.09 Å and an unusually low dehydroxylation temperature of 454°C and is composed of sheaves of fibers less than 50 Å wide. Its charge density is 5.09 × 10~4 esu/cm2. The charge originates mainly from the presence of 18% of the total Fe in tetrahedral positions, as determined by Mössbauer analysis. Slight deviations of the infrared spectra from those reported for nontronites are probably due to the presence of more octahedral Mg. The presence of authigenic quartz in the same sample permits some speculation on the concentration of dissolved silicon during nontronite genesis. A δ18O value of 26 ± 0.3‰ indicates a temperature of formation of about 22°C. The Sr isotope ratio suggests that the nontronite formed at least 12 million years ago.

The pH of Na-saturated, carbonate-containing and carbonate-free Leda clay, at salinities of 2 and 10 g/liter, was decreased from pH 8 to 4 by the addition of HCl. The Bingham yield stress, as determined with a coaxial viscometer, increased in all materials as the pH decreased. Above about pH 7 the 2-g/liter materials had a lower yield stress at any water content than the 10-g/liter materials, whereas, below about pH 6.8 the yield stress of the carbonate-containing soil at a salinity of 10 g/liter was lower. For the carbonate-free material, the change occurred at about pH 6.2. The influence of salinity on the remolded shear strength of these materials was pH-dependent. A yield stress increase with decreasing pH was likely due to a change in ion saturation. The carbonate-free material exhibited a maximum yield stress at about pH 5.5–6.2, depending on salinity. The isoelectric points for oxides and clay mineral edges most probably account for the existence of the maximum.

Statistical analyses of chemical data from the literature of corrensite minerals suggest a large compositional variability, more evident in octahedral than in tetrahedral coordination. Mg occupies 40–80% of the octahedral sites, with Al and Fe2+ making up the remainder. Approximately 15–30% of the tetrahedral sites are filled by Al. Despite this compositional variability, distinct fields for the several types of mixed-layer trioctahedral chlorite/trioctahedral swelling layer are not apparent. Statistical analyses of the composition of corrensite compared with saponite, vermiculite, and chlorite suggest that corrensite is an intermediate between trioctahedral chlorite and trioctahedral smectite. If Fe/(Fe + Mg) > 50%, chlorite alone is favored, but with increasing Mg, chlorite appears to transform into corrensite and then, by iron oxidation, into trioctahedral smectite. Despite the chemical variability between corrensite, chlorite, and saponite, corrensite appears chemically to be a well-defined species. On the other hand, corrensite cannot be characterized chemically on the basis of its swelling component. Thus, the current definition of corrensite as a regular 1:1 interstratification of trioctahedral chlorite and either trioctahedral smectite or vermiculite is appropriate.

Photon correlation spectroscopy (PCS), a dynamic light-scattering technique for particle size measurement, was used to determine the coagulation rates of aqueous dispersions of relatively monodisperse South Carolina Peerless kaolinite, Silver Hill, Montana, illite, Wyoming montmorillonite, and Florida palygorskite. This technique allows quantitative measurement of the rate of coagulation for clay particles where the traditional turbidity method gives only a qualitative measure. The critical coagulation concentrations for KCl at pH = 10.0 were: 0.199 M for kaolinite, 0.202 M for illite, 0.290 M for montmorillonite, and 0.034 M for palygorskite. The effective Hamaker constants, calculated using Derjaguin-Landau-Verwey-Overbeek theory, were: 3.1 × 10−20 J for kaolinite, 2.5 × 10−20 J for illite, 2.2 × 10−20 J for montmorillonite, and 1.63 × 10−19 J for palygorskite. Stern potentials at the critical coagulation concentration at pH 10.0 were: −42.7 mV for kaolinite, −40.7 mV for illite,‒21.2 mV for montmorillonite, and −66.9 mV for palygorskite.

Copper adsorption on a hydroxy-aluminum-hectorite complex (OH-Al-hectorite) at pH 4.5, 5.7, 7.4, and 7.8 was examined by means of electron spin resonance. The spectra of these samples were compared to those of Cu2+-hectorite and various aluminum hydrous oxides. Copper on the OH-Al-hectorite in aqueous gels occurred as mobile Cu(H20)62+ and chemisorbed to discrete sites of the OH-Al interlayer. As pH was increased, the ratio of chemisorbed to mobile Cu2+ increased. At pHs above 7 the solubility product of Cu(OH)2 was exceeded, but chemisorbed Cu2+ remained as the dominant species. These results contrast with the precipitation of Cu observed on microcry stalline gibbsite above pH 5 and indicate that the interlayer OH-A1 retained more Cu2+ on discrete sites. The greater adsorption capacity probably resulted in part from a higher specific surface area. Electron spin resonance spectra of Cu2+ in air-dried films of the OH-Al-hectorite at pH 4.5 and 7.4 showed Cu2+ in square planar symmetry, oriented with the z-axis perpendicular to the OH-Al-hectorite a-b plane. At the higher pH, the spectrum resembled that of Cu(OH)42- on alumina, suggesting a ligand exchange mechanism for Cu2+ adsorption on the complex.

Sulfate adsorption on kaolinite was followed at 0.7 μeq/ml to 99 μeq/ml solution concentrations at 30°C and at pH 6.0, and the amount of OH~ ions released and the change in surface charge were determined. Sulfate was adsorbed at positive and neutral sites by displacing OH2 and OH− groups, respectively. Adsorption of sulfate occurred predominantly at positive sites at low (0.7 μeq/ml to 0.9 /μeq/ml) solution concentrations, whereas at higher solution concentrations, the proportion of the sulfate adsorbed at the neutral sites increased, varying from 51% at 4.9 μeq/ml to 68% at 99 μeq/ml. The form of sulfate bonding was apparently governed by the level of the positive charge on the clay surface. Higher positive charge at low and intermediate levels of sulfate saturation resulted in the adsorption of sulfate as a divalent anion by forming a 6-member ring with surface Al. With a decrease in positive charge at higher levels of adsorption, the sulfate ion formed both monodentate and bidentate complexes.

Four hydrates with d(001) = 8.4, 8.6, and 10 Å (two types) were synthesized by intercalating kaolinite with dimethylsulfoxide and treating the intercalated clay with fluoride ions. X-ray powder diffraction, infrared spectroscopy, differential scanning calorimetry, thermal gravimetric analysis, and kinetics of dehydration experiments have led to the identification of two types of interlayer water. One type of water (hole water) is situated in the ditrigonal holes of the silica tetrahedral surface; the second type (associated water) forms a discontinuous layer of mobile water. The 8.4-Å and 8.6-Å hydrates have only hole water, whereas the two synthetic 10-Å hydrates and halloysite(10Å) contain both hole and associated water. The hole water is probably hydrogen bonded to the basal oxygens of the silica tetrahedra or, in the 8-Å hydrates when fluorine exchanges for inner-surface hydroxyls, the water molecules may reorient and form stronger hydrogen bonds to the fluorine. Associated water forms water-water hydrogen bonds approximately equal in strength to liquid water but is less strongly bonded to the clay surfaces than hole water. At room temperature the hole and associated water in the 10-Å hydrates do not form an ice-like structure.