The adsorption of Cr(III) was studied at pH 1, 2, 3, 4, 6, 8, and 10 on chlorite and kaolinite and at pH 1, 2, 3, and 6 on illite. The amount of chromium adsorbed on chlorite varied from 3.1 × 10–5 mole/ g at pH 1 to 16.6 × 10–5 mole/g at pH 4, and on illite from 4.9 × 10–5 mole/g to 9.2 × 10–5 mole/g at pH 1 and 3, respectively. Kaolinite adsorbed 3.7 × 10–5 mole Cr/g at pH 1, 2, and 3 and 5.5 × 10–5 mole Cr/g at pH 4. Measurements of the Cr 2p core-level binding energies indicate that chromium is probably adsorbed as a Cr(III) aqua ion at pH values below 4. The binding energies for the Cr 2p level for samples prepared above pH 4 compare favorably with the value determined for chromium hydroxide and lead to the conclusion that the chromium species present at pH 6, 8, and 10 is chromium hydroxide.

In environments contaminated with Cr, the interlayers of expandable layer silicates may serve as sinks for this potentially toxic element. As a means of determining the potential for smectites to serve as sinks for Cr, the precipitation products of Al and Cr in the interlayers of a montmorillonite were examined. Five montmorillonite (SWy-1) clay suspensions were treated with preweighed amounts of AlCl3 and CrCl3 to give five Al/(Al + Cr) molar ratios (1.0, 0.67, 0.5, 0.33, 0) with a total trivalent cation (M3+) concentration of 600 cmol(+)/kg clay. The clay-cation suspensions were titrated with 0.1 N NaOH to give a NaOH/M3+ molar ratio of 2.5. Analysis of the solid-phase reaction products showed that the cation exchange capacity and specific surface of all clays were reduced. Chromium reduced the exchangeability of the interlayers while Al increased the thermal stability. X-ray diffraction analysis revealed that all Al-containing interlayer materials formed similar gibbsitelike polymers. Data from infrared spectroscopy indicated that both Al and Cr were present within the same polymer. Differential thermal analysis and thermogravimetric tracings showed that the rapid collapse of the interlayer in the Cr end-member upon heating was due to a low-temperature loss of hydroxyls. It was not possible to identify all interlayer structures in the Cr end-member. Data from X-ray photoelectron spectroscopy showed all Cr to be Cr(III). Displacement of the interlayer material became more difficult as Cr content increased. The least exchangeable interlayers, therefore, may be found in environments containing the most Cr.

X-ray photoelectron spectroscopy (XPS) has been used to characterize the bonding state of Cu2+, Si4+, Al3+, and O2− ions in structural (octahedral and interlamellar) or adsorbed position in phyllosilicates. Five smectites, 5 kaolinites, and 1 chrysocolla with Cu(II) in known positions (octahedral, interlamellar, or surface adsorbed) have been investigated. Their spectra were compared with those of pure Cu metal and of pure Cu(I) and Cu(II) oxides.

The line for Cu 2p3/2 (binding energy of 935.4 eV) and well-defined shake-up lines (binding energy of about 943 eV) observed after 1 hr of X-ray irradiation are characteristic of Cu(II) in phyllosilicate octahedral sites. But due to the photoreduction effect, they show Cu(I) oxidation states (Cu 2p3/2, binding energy of 933.2 eV and near absence of shake-up lines) for the phyllosilicates with adsorbed Cu or in interlamellar positions. The kinetics of photoreduction distinguishes octahedral from interlamellar positions, and the latter from a surface adsorbed position. The enlargement of the FWHM (full width at half maximum) of XPS lines has been used to describe crystallochemical parameters linked to local ordering around the probe cations. Crystallization produces decreasing O 1 s and Cu 2p (octahedral cation) line widths but has no effect on the Si 2p (tetrahedral cation) line width. The enlargement of FWHM for all ion lines of the lattice is linked to the nature (Cu > Mg > Al) and the number and amount of structural cations in the phyllosilicates.

Two clay minerals, a dioctahedral, Na-montmorillonite from Wyoming and a trioctahedral, synthetic Na-laponite, were exchanged by cupric (Cu(II)) ions and subsequently heated at 100 °C intervals up to 500 °C. The resulting materials were analyzed by chemical analysis, X-ray diffraction (XRD), cation exchange capacity (CEC) measurements, combined thermogravimetric and differential thermal analysis (TGA-DTA), infrared (IR) spectroscopy, electron paramagnetic resonance (EPR) and X-ray photoelectron spectroscopy (XPS). Montmorillonite exhibits a well-known Hoffmann-Klemen effect in that, when heated, cupric (Cu) ions migrate into the lacunae of the octahedral sheet, where they compensate the negative charge deficit of the clay layer. In the case of laponite, CEC measurements and spectroscopic measurements reveal that Cu ions migrate into the octahedral sheet where they replace Li and Mg ions. After heating at 200 °C, approximately half the interlayer Cu ions are exchanged. The exchange appears to be 1 Cu for 1 Li, resulting in a slight decrease of the negative charge of the layer. After heating at 300 °C, the remaining Cu ions are exchanged by either 1 Mg or 2 Li, which does not result in any further charge reduction. At 400 °C, some of the extracted Mg remigrates into the structure and exchanges some Li (1 Mg for 2 Li). The final product at 400 or 500 °C is then a Li-laponite with Cu(II) in the octahedral sheet.

The cleavage of two single-crystal chlorites (a clinochlore and a penninite) has been studied using angle-resolved X-ray photoelectron spectroscopy (XPS). Both minerals cleaved in regions not typical of the bulk; the composition of the clinochlore was found to be especially non-uniform. The brucitic interlayer divided evenly between the pair of new surfaces exposed for two cleaves in the clinochlore, but was partitioned unequally in two cleaves in the penninite. The differences in apparent composition between the complementary pairs of surfaces are interpreted to show a marked preference of octahedral Al for the brucitic layer, in agreement with X-ray bulk structure refinements. For both chlorites, the layer charge was reduced in regions of easy cleavage, which also had a higher proportion of Si and less tetrahedral Al than the bulk chlorite. The percentages of tetrahedral aluminium deduced from the XPS surface analyses agreed satisfactorily with the percentages independently determined by consideration of the magnitude of anisotropy in the X-ray photoelectron diffraction (XPD) patterns. The XPD patterns from the clinochlore for rotation about axes parallel and antiparallel to the crystallographic a-axis were identical, showing that tetrahedral ordering was absent.

The distribution and chemical state of Si in a synthetic 2-line ferrihydrite with a Si/(Si + Fe) molar ratio of 0.11 was studied. Heat treatment under oxidizing conditions shows that Si-rich ferrihydrite is stable to 400°C. The transformation to hematite and the formation of a polymerized amorphous-silica phase occur at 850°C. At this temperature, the specific surface area decreases greatly and the average pore diameter increases, which is indicative of sintering. Heating under severe reducing conditions causes a segregation of Si from Fe and results in a mixture of elemental Fe and SiO2. Surface and structural data suggest that Si is located near the particle surface where it limits the rearrangement of Fe octahedra to form hematite.

The influence of water vapor on bentonites or smectites is of interest in many different fields of applied mineralogy such as nuclear-waste sealing or casting in the foundry industry. The water vapor affects the smectite surface and perhaps its structure probably leading to mostly unfavorable changes in its properties. In this first part of the present study, the influence of hot water vapor (200°C) on the physicochemical and mineralogical properties of smectite-group minerals was studied. After the steam treatment, turbidity measurements, methylene-blue sorption, water adsorption, and cation exchange capacity (CEC) were measured on both untreated and treated samples. Mineralogical changes were monitored by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) was used to measure O, Al, and Si. Only a few parameters showed differences between the untreated and vapor-treated samples. Sedimentation volumes (SV) decreased following the treatment. As shown by XRD and XPS, the crystalline structure of smectite remained unaffected by the steam treatment. Equivalent sphere diameters (ESD) were not affected systematically by the steam treatment. Differences in CEC values between untreated and treated samples were observed, but only for smectites with monovalent interlayer cations. From the variety of different measurements the conclusion of the present study was that steam treatment changes the charge properties at or near the smectite particle surface.

The crystallochemical features of Co in Co-substituted goethite solid-solutions prepared by two different procedures have been studied using infrared, X-ray photoelectron and electron energy loss spectroscopies. It was found that the path followed for the synthesis of Co-substituted goethite determines the oxidation state of Co in the goethite structure. Thus, in the solid-solution prepared by precipitation with Na2CO3 of an Fe(II) aqueous solution containing Co(II) cations, followed by the aerial oxidation of the precipitate, the Co cations were found to be divalent, whereas trivalent Co was incorporated into the goethite obtained by ageing a solution containing Fe(III) and Co(II) cations precipitated by the addition of KOH. This different behavior is explained by the higher pH of goethite formation in the latter case, which favors the oxidation of the Co(II) cations.

Clay–organic interaction is an important natural process that underpins soil ecosystem services. This process can also be tailored to produce clay–organic nanocomposites for industrial and environmental applications. The organic moiety of the nanocomposites, typically represented by a toxic surfactant, could be replaced by hydrochar formed from biomolecules (e.g. glucose) via hydrothermal carbonization. The effect of montmorillonite (Mnt) and glucose dosage on hydrochar formation, however, has not been clarified. In addition, the mechanisms by which Mnt-hydrochar nanocomposites (CMnt) can detoxify and remove carcinogenic Cr(VI) from aqueous solution are not well understood. In the current study, research milestones in terms of clay–organic interactions are summarized, following which the synthesis and characterization of CMnt for Cr(VI) adsorption are outlined. Briefly, 1 g of Mnt was reacted with 75 mL of glucose solution (0.1, 0.2, 0.3, 0.4, 0.5, and 0.6 mol L−1) by hydrothermal carbonization at 200°C for 16 h. The resultant CMnt samples were analyzed for chemical composition, functional groups, morphological features, and Cr(VI) adsorptive properties. Mnt promoted the conversion of glucose to hydrochars, the particle size of which (~80 nm) was appreciably smaller than that formed in the absence of Mnt (control). Furthermore, the hydrochars in CMnt had an aromatic structure with low hydrogen substitution and high stability (C/H atomic ratio 0.34–0.99). The weakened OH (from hydrochar) and Si–O–Si stretching peaks in the Fourier-transform infrared (FTIR) spectra of CMnt are indicative of chemical bonding between Mnt and hydrochar. The CMnt samples were effective at removing toxic Cr(VI) from acidic aqueous solutions. Several processes were involved, including direct reduction of Cr(VI) to Cr(III), complexation of Cr(III) with carboxyl and phenolic groups of hydrochar, electrostatic attraction between Cr(VI) and positively charged CMnt at pH 2 followed by indirect reduction of Cr(VI) to Cr(III), and Cr(III) precipitation.

The characterization of freshly cleaved mica surfaces for surface structure and chemical composition was briefly reviewed and focused on surface crystal chemistry using X-ray photoelectron spectroscopy (XPS) and other surface-sensitive techniques. This paper considers micas, which are useful as a first approximation for the behavior of many clay surfaces. Emphasis was given to phyllosilicate XPS binding energies (“chemical shift”), which were described and used to obtain oxidation state, layer charge, and chemical bonding information from the chemical shifts of different peaks. The chemical shift of the Si2p binding-energy to lower values can result from a negative charge increase because of Si4+ replacement by Al3+ and/or Fe3+. The apparent interlayer coordination number reduction from twelve to eight at muscovite and tetraferri-phlogopite (001) surfaces was indicated by the XPS measured K2p binding-energy and is consistent with bond relaxation. Although chemical shifts are valuable to distinguish chemical bonding and oxidation state, chemical shifts usually cannot distinguish between different Al coordination environments where Al is in both tetrahedral and octahedral sites.

Among the several steps involved in molecular evolution, molecular preconcentration is the first and most important. If the molecules are not preconcentrated the other steps of molecular evolution cannot occur. There are several ways to preconcentrate molecules: sorption, wetting/drying cycles, freezing/sublimation and sorption/precipitation with minerals. In the present work, the effect of NH4SCN and artificial seawater 4.0 Gy on the synthesis of ferrihydrite was studied. It should be noted that thiocyanate could play the same role as that of CN− in the Strecker reaction. Unlike today's seawater that has high Na+ and Cl− concentrations, the seawater used in this work has high Mg2+, Ca2+ and SO42− concentrations. Two results stand out, first SCN− and NH4+ were preconcentrated by sorption/precipitation in some syntheses and second, in some experiments, a mixture of goethite, hematite and magnetite was obtained. The sorption/precipitation of SCN− is always associated with the synthesis of goethite. This could be an indication that SCN− interacts with Fe3+ through the sulphur group of SCN−. In addition, the synthesis of magnetite could be an indication that the SCN− ion oxidized, forming thiocyanogen-(SCN)2 or trithiocyanate ion-(SCN)−3 and that Fe3+ reduced to Fe2+. Besides the sorption/precipitation of SCN− and NH4+, Fourier-transform infrared spectroscopy also showed that sorption/precipitation of SO42− and CO32− occurred. Ferrihydrite synthesized with artificial seawater presented the highest surface area and pore size. The pHpzc values of the samples were in the range of pHpzc described in the literature. The X-ray photoelectron spectroscopy (XPS) measurements performed show proportions of iron present in different oxidation states, however, the electronic similarities observed in the mixtures of iron oxides and oxy-hydroxides make it difficult to quantify them. Direct comparison between XPS spectra of the Fe2p and O 1s core-levels reveal no significant differences from the effect of artificial seawater 4.0 Gy on the synthesis of ferrihydrite.

We have synthesized graphene oxide (GO) using Hummer's method which was subsequently reduced (rGO) by hydrazine hydrate. The synthesized GO was coated with poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT-PSS) conducting polymer (CP) to obtain CP-GO which was also further reduced using hydrazine hydrate to form CP-rGO. Scanning electron microscopy, Raman spectroscopy, X-ray diffraction, ultraviolet photoelectron spectroscopy, and X-ray photoelectron spectroscopy, X-ray absorption near-edge structure (XANES) techniques were used to study the electronic and structural properties of GO, rGO, CP-GO, and CP-rGO nanocomposites for biomedical applications. The superconducting quantum interference device method was used to investigate the magnetic properties of the nanocomposites. The electrical conductivity of the CP-GO nanocomposites was found to be ~104 times higher than that of GO due to an increase in sp2 content and subsequent decrease in oxygen functional groups. In rGO, we observed an improved paramagnetic saturation magnetization of approximately 5.6 × 0−3 emu/g at 2 K. The electronic and magnetic behavior of PEDOT-PSS-coated nanocomposites, as a result, were successfully tuned for potential biological and biomedical applications.

Nano-forms of copper oxides (CuO and Cu2O) are potential candidates in the field of energy conversion and storage. Low temperature and controlled growth of three-dimensional nanostructured hierarchical assembly of CuO over Cu2O is reported here with demonstrated advantage in energy conversion and storage applications. Electrodeposited Cu2O is partially oxidized in an alkali bath to two different forms of hierarchical nanostructures (HNS): CuO/Cu2O and CuO:Cu(OH)2/Cu2O. Randomly oriented nanorods and nanoflakes with high surface area tussock-like nanostructure are formed during oxidation at room and at elevated temperatures, respectively. The nanoflake morphology exhibits a high surface area of 85.82 m2/g and sufficient ion percolation pathways, leading to an efficient electrode–electrolyte interface for electrochemical energy devices. A favorable conduction and valence band alignment in the HNS with respect to water redox level along with fast electron diffusion time of 0.8 μs make it an ideal photocathode.

Desorption experiments performed on four Cu-adsorbed palygorskites suggest that the leached Cu2+ ion originates at the surface and/or net-like interstice of the palygorskite fibres. The leached fraction, calculated from the quantities of adsorbed Cu2+ before and after desorption, is <1%. This may indicate that the majority of Cu is in inaccessible structural sites. X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared (FTIR) spectroscopy and electron spin resonance (ESR) were used to determine the mineralogical character of the Cu-adsorbed palygorskite. Two photoelectron lines at 932.5 and/or 933.7 eV in the narrow scan Cu 2p3/2 spectra show that Cu adsorbed on the surface of palygorskite is in the Cu+ and Cu2+ state. The stretching vibrations of the octahedral cation shift ~3–5 cm–1 towards a greater wavenumber in the FTIR spectra of Cu-adsorbed palygorskite. It can be deduced that the Cu2+ is trapped in the channel of the palygorskite structure. The ESR spectra of the palygorskite give g values of 2.34, 2.12, 2.08 and 2.05, suggesting that some Cu ions cannot be reached by H+. These results confirm that Cu is adsorbed by palygorskite via three possible mechanisms: (1) the Cu is adsorbed onto the surface or in a net-like interstice, and its oxidation states are +1 and +2; (2) Cu forms a complex ion – [Cu(H2O)4]2+ or [Cu(H2O)6]2+, and is trapped in the channel; or (3) Cu enters into the hexagonal channel of the tetrahedral sites or the unoccupied octahedral sites of palygorskite.

Synthetic pentlandite surfaces were subjected to oxidation by a range of inorganic oxidants, and the resultant alteration of the surface studied by a range of surface-sensitive spectroscopic techniques. The oxidants used were air during heating to relatively low temperatures (150°C), steam, ammonium hydroxide, hydrogen peroxide, and sulphuric acid. Electrochemical oxidation was also undertaken. X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), conversion electron Mössbauer spectroscopy (CEMS), and spectral reflectance measurements were used to characterize the surface compositions. New data for the binding energies of core electrons in pentlandite and violarite, based on the fitted XPS spectra, are proposed. For pentlandite and violarite respectively, values of 707.3 eV and 708.4 eV for the Fe 2p3/2, 853.0 eV and 853.2 eV for the Ni 2p3/2, and 161.2 eV for the S 2p in both sulphides, were obtained. After oxidation the pentlandite surfaces indicated nickel enrichment in the subsurface, with the formation of violarite. The immediate oxidized surface, of approximately 10Å thickness, indicated a range of iron oxides and hydroxides (Fe3O4, Fe2O3 and FeOOH, with possible Fe1−xO and Fe(OH)3), nickel oxide (NiO), and iron sulphates (FeSO4, Fe2(SO4)3). The proportions of the phases present in the surface layer are inferred to be a consequence of both the strength of the oxidant employed, and the thermodynamic stability of the phases, as can be illustrated using partial pressure and Eh/pH diagrams. A sequence of oxidation is proposed, accounting for the sub-surface enrichment in violarite, and the development of the oxidized surface, which is inferred to have a major affect on the rates of oxidation.

Surfaces of a natural sample of arsenopyrite (FeAsS) were oxidized by a range of inorganic oxidants, and the resultant surface alteration products studied using various spectroscopic techniques. The oxidants used were air during heating to relatively low temperatures (150°C), steam, ammonium hydroxide, hydrogen peroxide, and sulphuric acid. Electrochemical oxidation in water was also undertaken. X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and spectral reflectance measurements, were used to characterize the surface compositions. New data are proposed for the binding energies of core electrons in arsenopyrite based on the fitted XPS spectra: 706.9 eV for the Fe 2p3/2 level, 161.2 eV for the S 2p level, and 40.7eV for the As 3d level. Spectroscopic analyses of the surfaces following oxidation indicated a range of iron oxides and hydroxides (Fe1−xO, Fe3O4, Fe2O3, FeOOH and Fe(OH)3), arsenic oxides (As2O3 and As2O5), sulphur and iron sulphates (FeSO4, Fe2(SO4)3). The relative proportions of the different phases present in the surface layer are related to the strength of the oxidant employed and, where relevant, the Eh/pH conditions prevalent during oxidation. The conclusions regarding the nature of the oxidation of arsenopyrite are discussed in relation to arsenopyrite extraction by flotation and leaching, and the breakdown of arsenopyrite in natural systems.

Extreme silver enrichment at the surface of the complex sulphide, tennantite (ideal formula: Cu12As4S13), occurs following exposure to alkaline solutions, and involves the development of an Ag-rich sulphide surface species. The tennantite has a low bulk Ag content of 0.3 at.%, and a percentage surface enrichment of Ag is thirty-six times that of the bulk. The techniques of X-ray photoelectron spectroscopy (XPS) and reflection extended X-ray absorption fine structure spectroscopy show the new phase to be a Ag sulphide species compositionally similar to cupriferous proustite ((Cu,Ag)3AsS3). Solution experiments and XPS depth profiling show that the surface is most depleted in Cu and Zn, and enriched in Ag compared to the bulk tennantite. Selective dissolution and reprecipitation at the tennantite surface cannot explain the enrichment of Ag relative to the bulk. Migration must have occurred and could have been driven by the leaching out of Cu which produces a metal-depleted surface, coupled to the relative incompatibility of Ag in the tennantite lattice. To account for the extreme enrichment at the surface, Ag must have diffused from depths of up to 9 nm, probably via structural weaknesses and vacancies in the tennantite lattice.

Organoclays are sorbent materials prepared from clays by exchanging inorganic with organic cations. Their properties depend on the loading and conformational structure of the organic cations, but little information is available about the surface structures of organoclays. In this work, X-ray photoelectron spectroscopy (XPS) and classical molecular dynamics (MD) simulations are combined to characterize the external interface of an organoclay prepared from hexadecylpyridinium (HDPy+) and bentonite. The XPS survey spectra show well the varying elemental composition of the surface with increasing amount of surfactant, showing a decreasing contribution of clay-derived elements with increasing organic coverage. The high-resolution C 1s XPS spectra depict sensitively the surface arrangement of the surfactant. In combination with MD simulations, the results implied a monolayer coating for low surfactant coverage and a disordered bilayer arrangement at high surfactant uptakes. Molecular dynamics simulations showed that for very high cation uptake a quasi-paraffin-like configuration is also possible. The combination of experimental and modelling methods yielded congruent information on the molecular-scale arrangement of organic cations at the organoclay surfaces and the controlling mechanisms.

Qualitative and quantitative analysis of surface species on size-segregated atmospheric particulate collected in Antarctica during the 2010–11 summer was performed by X-ray photoelectron spectroscopy (XPS). This represents the first example of surface characterization of Antarctic aerosols. The size class with particle cut-off diameter of 3 μm was richest in terms of chemical elements. Peculiar findings of the application included detection of Ca (possibly surface-segregated) and surface enrichment of Mg. The determination of nitrate, ammonium and sulphate species on collection filters provides evidence for a possible advantage of XPS over more laborious techniques (e.g. ion chromatography). The presence of these species is in reasonable agreement with other recent reports from Antarctica.

Carbon nanotubes (CNT) have proven to be materials with great potential for the construction of biosensors. Development of fast, simple, and low cost biosensors to follow reactions in bioprocesses, or to detect food contaminants such as toxins, chemical compounds, and microorganisms, is presently an important research topic. This report includes microscopy and spectroscopy to characterize raw and chemically modified multiwall carbon nanotubes (MWCNTs) synthesized by chemical vapor deposition with the intention of using them as the active transducer in bioprocessing sensors. MWCNT were simultaneously purified and functionalized by an acid mixture involving HNO3–H2SO4 and amyloglucosidase attached onto the chemically modified MWCNT surface. A 49.0% decrease in its enzymatic activity was observed. Raw, purified, and enzyme-modified MWCNTs were analyzed by scanning and transmission electron microscopy and Raman and X-ray photoelectron spectroscopy. These studies confirmed purification and functionalization of the CNTs. Finally, cyclic voltammetry electrochemistry was used for electrical characterization of CNTs, which showed promising results that can be useful for construction of electrochemical biosensors applied to biological areas.