Domerockite, Cu4(AsO4)2(AsO3OH)(OH)3·H2O, is a new mineral from the Dome Rock Mine, South Australia. It occurs as aggregates of bluish green, equant to short prismatic and tabular crystals up to 0.3 mm long and 0.2 mm across. Domerockite is translucent, with a vitreous lustre and pale green streak. It displays no fluorescence under UV irradiation. The mineral is brittle with an uneven fracture, a Mohs hardness of ∼3 and a calculated density of 4.44 g/cm3 (based on the structure refinement). Optically, it is biaxial negative, with α = 1.798(4), β = 1.814(4), γ = 1.817(4), 2Vcalc. = 46°; pleochroism is very weak; X pale greenish yellow, Y greenish blue, Z greenish blue; absorption X < Y = Z; orientation is uncertain. Chemical analysis by electron microprobe gave CuO 52.04, ZnO 0.78, BaO 0.11, As2O537.67, P2O50.32, SiO20.24, H2O 8.84, total 100.00 wt.%, with H2O calculated by difference. The empirical chemical formula is (Cu3.94, Zn0.06)Σ4.00H0.91(As1.97, P0.03, Si0.02)Σ2.02O8(OH)3.00˙H2O based on 12 oxygen atoms.

Domerockite is triclinic, space group P, with a = 5.378(11), b = 8.962(18) c = 9.841(2) Å, α = 75.25(3), β = 83.56(3), γ = 79.97(3)°, V = 450.5(16) Å3 and Z = 2. The eight strongest lines in the X-ray powder diffraction pattern are [d (Å), (I)(hkl)]: 4.716 (30)(101, 002, 111), 3.697 (25)(121), 3.605 (30)(120, 12), 3.119 (60)(12), 3.073 (100)(1), 2.856 (40)(02, 030), 2.464 (50)(212, 13), 2.443 (40)(014). The crystal structure of domerockite has been solved by direct methods and refined to an R index of 7.44% using 2635 observed reflections. The structure comprises [Cuφ4] (φ = O, OH) chains of edge-sharing sharing, distorted octahedra that extend along [10] and are decorated by AsO4 tetrahedra to form sheets in the (010) plane. Dimers of edge-sharing [CuO4(OH)(H2O)] octahedra share corners with dimers of edge-sharing [CuO4(OH)] square pyramids to form zigzag chains which extend along [101]. The chains lie between and link to the sheets by sharings corners of octahedra, square pyramids and tetrahedra to form a heteropolyhedral framework.

Three new minerals in the dumortierite supergroup were discovered in the Szklary pegmatite, Lower Silesia, Poland. Nioboholtite, endmember (Nb0.6☐0.4)Al6B3Si3O18, and titanoholtite, endmember (Ti0.75☐0.25)Al6B3Si3O18, are new members of the holtite group, whereas szklaryite, endmember ☐Al6BAs3+3O15, is the first representative of a potential new group. Nioboholtite occurs mostly as overgrowths not exceeding 10 μm in thickness on cores of holtite. Titanoholtite forms patches up to 10 μm across in the holtite cores and streaks up to 5 μm wide along boundaries between holtite cores and the nioboholtite rims. Szklaryite is found as a patch ∼2 μm in size in As- and Sb- bearing dumortierite enclosed in quartz. Titanoholtite crystallized almost simultaneously with holtite and other Ta-dominant minerals such as tantalite-(Mn) and stibiotantalite and before nioboholtite, which crystallized simultaneously with stibiocolumbite during decreasing Ta activity in the pegmatite melt. Szklaryite crystallized after nioboholtite during the final stage of the Szklary pegmatite formation. Optical properties could be obtained only from nioboholtite, which is creamy-white to brownish yellow or grey-yellow in hand specimen, translucent, with a white streak, biaxial (–), nα = 1.740 – 1.747, nβ ∼ 1.76, nγ ∼ 1.76, and Δ < 0.020. Electron microprobe analyses of nioboholtite, titanoholtite and szklaryite give, respectively, in wt.%: P2O5 0.26, 0.01, 0.68; Nb2O5 5.21, 0.67, 0.17; Ta2O5 0.66, 1.18, 0.00; SiO2 18.68, 21.92, 12.78; TiO2 0.11, 4.00, 0.30; B2O3 4.91, 4.64, 5.44; Al2O3 49.74, 50.02, 50.74; As2O3 5.92, 2.26, 16.02; Sb2O3 10.81, 11.48, 10.31; FeO 0.51, 0.13, 0.19; H2O (calc.) 0.05, –, –, Sum 96.86, 96.34, 97.07, corresponding on the basis of O = 18–As–Sb to {(Nb0.26Ta0.02☐0.18)(Al0.27Fe0.05Ti0.01)☐0.21}Σ1.00Al6B0.92{Si2.03P0.02(Sb0.48As0.39Al0.07}Σ3.00(O17.09OH0.04☐0.87)Σ18.00, {(Ti0.32 Nb0.03 Ta0.03☐0.10)(Al0.35 Ti0.01 Fe0.01)☐0.15 }Σ1.00 Al6 B0.86 {Si2 . 3 6 (Sb0.5 1 As0.14 )}Σ3.01(O17.35☐0.65)Σ18.00 and {☐0.53 (Al0.41 Ti0.02 Fe0.02 )(Nb0.01☐0.01 )}Σ1.00Al6 B1.01 {(As1.07 Sb0.47 Al0.03 ) Si1.37 P0.06 }Σ3.00(O16.46☐1.54 )Σ18.00. Electron backscattered diffraction indicates that the three minerals are presumably isostructural with dumortierite, that is, orthorhombic symmetry, space group Pnma (no. 62), and unit-cell parameters close to a = 4.7001, b = 11.828, c = 20.243 Å, with V = 1125.36 Å3 and Z = 4; micro-Raman spectroscopy provided further confirmation of the structural relationship for nioboholtite and titanoholtite. The calculated density is 3.72 g/cm3 for nioboholtite, 3.66 g/cm3 for titanoholtite and 3.71 g/cm3 for szklaryite. The strongest lines in X-ray powder diffraction patterns calculated from the cell parameters of dumortierite of Moore and Araki (1978) and the empirical formulae of nioboholtite, titanoholtite and szklaryite are [d, Å, I (hkl)]: 10.2125, 67, 46, 19 (011); 5.9140, 40, 47, 57 (020); 5.8610, 66, 78, 100 (013); 3.4582, 63, 63, 60 (122); 3.4439, 36, 36, 34 (104); 3.2305, 100, 100, 95 (123); 3.0675, 53, 53, 50 (105); 2.9305, 65, 59, 51 (026); 2.8945, 64, 65, 59 (132), respectively. The three minerals have been approved by the IMA CNMNC (IMA 2012-068, 069, 070) and were named for their relationship to holtite and occurrence in the Szklary pegmatite, respectively.

Two new minerals – manganoblödite (IMA2012–029), ideally Na2Mn(SO4)2·4H2O, and cobaltoblödite (IMA2012–059), ideally Na2Co(SO4)2·4H2O, the Mn-dominant and Co-dominant analogues of blödite, respectively, were found at the Blue Lizard mine, San Juan County, Utah, USA. They are closely associated with blödite (Mn-Co-Ni-bearing), chalcanthite, gypsum, sideronatrite, johannite, quartz and feldspar. Both new minerals occur as aggregates of anhedral grains up to 60 μm (manganoblödite) and 200 μm (cobaltoblödite) forming thin crusts covering areas up to 2 × 2 cm on the surface of other sulfates. Both new species often occur as intimate intergrowths with each other and also with Mn-Co-Ni-bearing blödite. Manganoblödite and cobaltoblödite are transparent, colourless in single grains and reddish-pink in aggregates and crusts, with a white streak and vitreous lustre. Their Mohs' hardness is ∼2½. They are brittle, have uneven fracture and no obvious parting or cleavage. The measured and calculated densities are Dmeas = 2.25(2) g cm−3 and Dcalc = 2.338 g cm−3 for manganoblödite and Dmeas = 2.29(2) g cm−3 and Dcalc = 2.347 g cm−3 for cobaltoblödite. Optically both species are biaxial negative. The mean refractive indices are α = 1.493(2), β = 1.498(2) and γ = 1.501(2) for manganoblödite and α = 1.498(2), β = 1.503(2) and γ = 1.505(2) for cobaltoblödite. The chemical composition of manganoblödite (wt.%, electron-microprobe data) is: Na2O 16.94, MgO 3.29, MnO 8.80, CoO 2.96, NiO 1.34, SO3 45.39, H2O (calc.) 20.14, total 98.86. The empirical formula, calculated on the basis of 12 O a.p.f.u., is: Na1.96(Mn0.44Mg0.29Co0.14Ni0.06)Σ0.93S2.03O8·4H2O. The chemical composition of cobaltoblödite (wt.%, electron-microprobe data) is: Na2O 17.00, MgO 3.42, MnO 3.38, CoO 7.52, NiO 2.53, SO3 45.41, H2O (calc.) 20.20, total 99.46. The empirical formula, calculated on the basis of 12 O a.p.f.u., is: Na1.96(Co0.36Mg0.30Mn0.17Ni0.12)Σ 0.95S2.02O8·4H2O. Both minerals are monoclinic, space group P21/a, with a = 11.137(2), b = 8.279(1), c = 5.5381(9) Å, β = 100.42(1)°, V = 502.20(14) Å3 and Z = 2 (manganoblödite); and a = 11.147(1), b = 8.268(1), C = 5.5396(7) Å, β = 100.517(11)°, V = 501.97(10) Å3 and Z = 2 (cobaltoblödite). The strongest diffractions from X-ray powder pattern [listed as (d,Å(I)(hkl)] are for manganoblödite: 4.556(70)(210, 011); 4.266(45)(01); 3.791(26)(11); 3.338(21)(310); 3.291(100)(220, 021), 3.256(67)(211, 21), 2.968(22)(21), 2.647(24)(01); for cobaltoblödite: 4.551(80)(210, 011); 4.269(50)(01); 3.795(18)(11); 3.339(43)(310); 3.29(100)(220, 021), 3.258(58)(11, 21), 2.644(21)(01), 2.296(22)(122). The crystal structures of both minerals were refined by single-crystal X-ray diffraction to R1 = 0.0459 (manganoblödite) and R1 = 0.0339 (cobaltoblödite).

A new mineral, yaroshevskite, ideally Cu9O2(VO4)4Cl2, occurs in sublimates collected from the Yadovitaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with euchlorine, fedotovite, hematite, tenorite, lyonsite, melanothallite, atlasovite, kamchatkite and secondary avdoninite, belloite and chalcanthite. Yaroshevskite forms isolated prismatic crystals, up to 0.1 × 0.15 × 0.3 mm in size, on the surface of euchlorine crusts. The mineral is opaque and black, with a reddish black streak and lustre between metallic and adamantine. Yaroshevskite is brittle, no cleavage was observed and the fracture is uneven. The Mohs hardness is ~3½ (corresponding to a mean VHN micro-indentation hardness of 172 kg mm -2) and the calculated density is 4.26 g cm-3. In reflected light, yaroshevskite is grey with a weak bluish hue. Pleochroism, internal reflections and bireflectance were not observed. Anisotropy is very weak. The composition (wt.%) determined by electron microprobe is: CuO 61.82, ZnO 0.53, Fe2O3 0.04, V2O531.07, As2O50.32, MoO3 1.56, Cl 6.23, O=Cl2 1.41; total 100.16. The empirical formula, calculated on the basis of 20 (O + Cl) anions is (Cu8.80 Zn0.07 Fe0.01)Σ 8.88(V3.87Mo0.12As0.03)σ 4.02O18.01Cl1.99. Yaroshevskite is triclinic, space group P, a = 6.4344(11), b = 8.3232(13), c = 9.1726(16) Å , α = 105.338(14), β = 96.113(14), γ = 107.642(1)°, V = 442.05(13) Å3 and Z = 1. The nine strongest reflections in the X-ray powder pattern [dobs in Å (I)(hkl)] are as follows: 8.65(100)(001); 6.84(83)(01); 6.01(75)(100); 5.52(60)(01); 4.965(55)(011); 4.198(67)(1); 4.055(65)(110); 3.120(55)(021); 2.896(60)(21,003,20). The crystal structure was solved by direct methods from single-crystal X-ray diffraction data and refined to R = 0.0737. The yaroshevskite structure is unique. It is based on corrugated layers made up of chains of edge-sharing flat squares with central Cu2+ cations [Cu(1), Cu(4) and Cu(5)]; neighbouring chains are connected via groups consisting of three Cu2+ -centred squares [two Cu(3) and Cu(6)]. Neighbouring layers are connected via pairs of Cu(2)O4Cl five-coordinate polyhedra and isolated VO4 tetrahedra. The structure of yaroshevskite can also be considered in terms of oxygen-centred tetrahedra: O(7)Cu4 tetrahedra are connected via common Cu(4) and Cu(5) vertices to form pyroxene-like chains [O2Cu6]∞. In this context, the structural formula can be written Cu3[O2Cu6][VO4]4Cl2. The mineral name honours the Russian geochemist Alexei A. Yaroshevsky (b. 1934) of Moscow State University.

The Kûngnât Complex (1275±1.8 Ma) in the Gardar Alkaline Province, South Greenland, cuts Archaean gneisses and comprises two intersecting syenitic stocks and a gabbroic ring-dyke. The magmas, with increasingly more primitive compositions, were emplaced successively by ring-faulting and roof stoping. The syenites are orthocumulates (cumulus alkali feldspar, olivine, pyroxene, titanomagnetite and apatite; intercumulus phases include alkali amphibole, biotite, quartz and calcite). In the well dissected earlier stock, a 2.2 km-thick layered sequence displays graded modal layering, feldspar lamination and cryptic layering. Modal layering in both stocks is directed mainly inwards at 35° – 50°. Heterogeneous nucleation of the cumulus assemblage, close to steep thermal boundary layers, is inferred. The modal layering is ascribed primarily to gravitational sorting aided by the large density differential between a) feldspar and b) Fe-rich silicates and oxides. Episodic collapse of cumulus + melt slurries contributed to inward-dipping crystal pediments on the chamber floors. The Ring-Dyke (up to 100 m wide) is nearly continuous through 360°. Kûngnât exhibits a compositional nearcontinuum from olivine gabbro through syenite intermediaries to alkali granite, ascribed to protracted assimilation/fractional crystallization processes. The most radiogenic Nd isotope data from Kûngnât (εNdi values between –3.3 and –1.0) point to a lithospheric mantle source, whereas the most unradiogenic values imply enrichment in LREE by crustal contamination of the magmas.

Ferritchromite is rarely reported in forearc mantle peridotites. This contribution describes ferritchromite alteration and zoned Cr-spinel in serpentinites from the Rio San Juan Complex in the Dominican Republic. These rocks originated from the forearc mantle and protruded along lithosphere-scale faults in the mid Eocene. The cores of the Cr-spinel grains have Cr# ratios [i.e.atomic Cr/(Cr + Al)] between 0.48 and 0.66; such values are relatively high and are considered to represent primary compositions. Relatively high Zn contents in the grain cores (0.46 c 0.95 wt.% ZnO) are also thought to be primary; they reflect exceptionally cool conditions in the northern Caribbean forearc mantle. A progressive change in the zoning of Cr-spinel is recorded in the samples. Weakly zoned grains of Cr-spinel have rims with lower Mg# ratios [i.e.atomic Mg/(Mg + Fe2+)] and slightly higher Cr# ratios than the cores. More strongly zoned grains of Cr-spinel, in addition to low Mg# and high Cr# in their rims, have a marked increase in Fe3+# [i.e.Fe3+/(Fe3+ + Al + Cr)] of up to 0.35 in their rims and are partially coated by Mg-rich chlorite. All grains show core-to-rim decreases in their Zn content and increases in Ti, Mn and V. The association with Mg-rich chlorite and the compositional zoning are reminiscent of those reported for ferritchromite. Ferritchromite (with Fe3+# >0.5) is common in ultramafic rocks in amphibolite-grade terranes; however, the serpentinite samples described herein show little evidence of high-grade metamorphism. The lowtemperature serpentine-group mineral lizardite is dominant and high-temperature antigorite is either very rare or absent; other high-temperature minerals, such as talc, tremolite and cummingtonite, are trace constituents. The observed zoning in the Cr-spinel is thought to represent 'immature' ferritchromite, probably formed in response to a short-lived thermal event. This event appears to have been on too short a timescale to produce either proper ferritchromite or significant quantities of high-temperature minerals. It may be related to the emplacement of the nearby Rio Boba Intrusion, or the upward protrusion of the serpentinites along the lithosphere-scale Septentrional fault zone from the base of the mantle wedge through its hotter interior. We suggest that such alteration is rare in forearc serpentinites because they are not commonly heated during exhumation along the plane of subduction. This work demonstrates that Cr-spinel compositions can be modified by relatively low-grade metamorphism.

Deveroite-(Ce), ideally Ce2(C2O4)3·10H2O, is a new mineral (IMA 2013-003) found in the alpine fissures of Mount Cervandone, overlooking the Devero Valley, Piedmont, Italy. It occurs as sprays of colourless elongated tabular, acicular prisms only on cervandonite-(Ce). It has a white streak, a vitreous lustre, is not fluorescent and has a hardness of 2–2.5 (Mohs' scale). The tenacity is brittle and the crystals have a perfect cleavage along {010}. The calculated density is 2.352 g/cm3. Deveroite-(Ce) is biaxial (–) with 2V of ∼77°, is not pleochroic and the extinction angle (β ∧ c) is ∼27°. No twinning was observed. Electron microprobe analyses gave the following chemical formula: (Ce1.01Nd0.33La0.32Pr0.11Y0.11Sm0.01Pb0.04U0.03Th0.01Ca0.04)2.01(C2O4)2.99·9.99H2O. Although synchrotron radiation was not used to solve the structure of deveroite-(Ce) the extremely small size of the sample (13 μm × 3 μm × 1 μm) did not allow us to obtain reliable structural data. However, it was possible to determine the space group (monoclinic, P21/c) and the unit-cell parameters, which are: a = 11.240(8) Å, b = 9.635(11) Å, c = 10.339(12) Å, β = 114.41(10)°, V = 1019.6 Å3. The strongest lines in the powder diffraction pattern [d in Å (I)(hkl)] are: 10.266(100)(100); 4.816(35.26)(21); 3.415(27.83)(300); 5.125(24.70)(200); and 4.988(22.98)(111). Deveroite-(Ce) is named in recognition of Devero valley and Devero Natural Park.

Hylbrownite, ideally Na3MgP3O10·12H2O, the second known triphosphate mineral, is a new mineral species from the Dome Rock mine, Boolcoomatta Reserve, Olary Province, South Australia, Australia. The mineral forms aggregates and sprays of crystals up to 0.5 mm across with individual crystals up to 0.12 mm in length and 0.02 mm in width. Crystals are thin prismatic to acicular in habit and are elongate along [001]. Forms observed are {010}, {100}, {001}, {210} and {201}. Crystals are colourless to white, possess a white streak, are transparent, brittle, have a vitreous lustre and are nonfluorescent. The measured density is 1.81(4) g cm−3; Mohs' hardness was not determined. Cleavage is good parallel to {001} and to {100} and the fracture is uneven. Hylbrownite crystals are nonpleochroic, biaxial (−), with α = 1.390(4), β = 1.421(4), γ = 1.446(4) and 2Vcalc. = 82.2°. Hylbrownite is monoclinic, space group P21/n, with a = 14.722(3), b = 9.240(2), c = 15.052(3) Å, β = 90.01(3)°, V = 2047.5(7) Å3, (single-crystal data) and Z = 4. The strongest lines in the powder X-ray diffraction pattern are [d (Å)(I)(hkl)]: 10.530(60)(10,101), 7.357(80)(200), 6.951(100)(11, 111), 4.754(35)(10, 103), 3.934(40)(022), 3.510(45)(30, 303), 3.336(35)(41, 411). Chemical analysis by electron microprobe gave Na2O 16.08, MgO 7.08, CaO 0.43, P2O5 37.60, H2Ocalc 38.45, total 99.64 wt.%. The empirical formula, calculated on the basis of 22 oxygen atoms is Na2.93Mg0.99Ca0.04P2.99O9.97·12.03H2O. The crystal structure was solved from single-crystal X-ray diffraction data using synchrotron radiation (T = 123 K) and refined to R1 = 4.50% on the basis of 2417 observed reflections with F0 > 4 σ(F0). [Mg(H2O)3P3O10] clusters link in the b direction to Naφ6 octahedra, by face and corner sharing. Edge sharing Naφ6 Octahedra and Naφ7 polyhedra form Na2O9 groups which link via corners to form chains along the b direction. Chains link to [Mg(H2O)3P3O10] clusters via corner-sharing in the c direction and form a thick sheet parallel to (100). Sheets are linked in the a direction via hydrogen bonds.

Irinarassite, Ca3Sn2SiAl2O12, a new mineral species of the garnet supergroup was discovered in metasomatically altered carbonate-silicate xenoliths in ignimbrites of the Upper Chegem Caldera, Northern Caucasus, Kabardino-Balkaria, Russia. It occurs as small zones and irregular spots in kimzeyite-kerimasite or rarely as single crystals not exceeding 10 μm in size, within complex pseudomorphs after zircon. Lakargiite, tazheranite, baddeleyite, kerimasite, kimzeyite, baghdadite and rarely magnesioferrite are associated with irinarassite in the pseudomorphs which are confined to larnite-cuspidine zones immediately adjoining the ignimbrite. Larnite, cuspidine, rondorfite, fluor- and hydroxylellestadite, fluorite and secondary minerals such as ettringite, hillebrandite and bultfonteinite are associated with irinarassite. Irinarassite is pale brown to yellow colour. The mineral is characterized by the absence of cleavage and by an irregular fracture. The calculated density is 4.3 g cm–1. The mineral is isotropic with a calculated refractive index of 1.9. The empirical crystal chemical formula of irinarassite from the holotype specimen is as follows (Ca2.965Fe2+0.035)Σ3(Sn1.016Zr0.410Ti0.262Sb5+0.237Fe2+0.035U6+0.017Sc0.014Hf0.006Nb0.004)Σ2.001(Al1.386Fe3+0.804Si0.446Ti4+0.364)Σ3O12. Electron backscatter diffraction patterns of irinarassite are fitted to the garnet model with a = 12.50(3) Å with excellent MAD (mean angular deviation) = 0.16°. The Raman spectrum of irinarassite is analogous to those of kerimasite and other Zr-Sn-garnets of the schorlomite and bitikleite groups.

A detailed mineralogical examination of representative material from the P2-West 'kimberlite' located in the Wajrakarur Kimberlite Field (India) demonstrates that significant differences exist between these rocks and archetypal hypabyssal kimberlite. The intrusion consists of an olivine-phyric facies which has been transected by, and includes clasts of, a consanguineous phlogopite-rich pegmatitic facies. The olivine-rich parts of P2-West are relatively fresh and consist of euhedral-to-subhedral microphenocrystal olivine set in a groundmass of fine-grained anhedral monticellite, amoeboid apatite, and subhedral-to-euhedral perovskite within a partially chloritized-to-fresh phlogopite-rich mesostasis. The rock lacks the abundant olivine macrocrysts characteristic of kimberlite. Monticellite crystals are commonly partially or completely replaced by pectolite and hydrogarnet. Similar material occurs as irregular aggregates randomly scattered throughout the groundmass. The groundmass, in contrast to that of hypabyssal kimberlites, is relatively poor in spinels. Atoll spinels are absent, with the majority of spinels occurring principally as mantles upon microphenocrystal olivine. Disaggregated cumulate-like assemblages of intergrown anhedral perovskite and spinel are common. Spinel compositions are unlike those of kimberlites and their evolutionary trend is similar to that of lamproite and lamprophyre spinels. The pegmatitic facies of the intrusion are highly and pervasively altered, and characterized by the presence of large clasts, veins, and irregular aggregates consisting of large (1–5 mm) crystals of pinkish-bronze Al-poor phlogopite intergrown with and/or including: apatite; pectolite-hydrogarnet pseudomorphs after an unidentified euhedral phase; chlorite laths; barytolamprophyllite; perovskite; tausonite; diverse Sr-Ba-carbonates; and baryte. The presence of barytolamprophyllite and tausonite are typical of potassic undersaturated alkaline rocks and have never been reported from kimberlite; however, neither feldspar nor feldspathoids are present in P2-West. Micas in fresh and altered rocks are Al2O3- and BaO-poor, and exhibit compositional evolutionary trends towards tetraferriphlogopite rather than kinoshitalite. On the basis of these mineralogical data it is suggested that P2-West represents an unusual lamproite-like intrusion which has undergone extensive hydrothermal deuteric alteration and should not be considered a bona fide kimberlite.

The new mineral species oxycalcioroméite, Ca2Sb5+2O6O, has been discovered at the Buca della Vena mine, Stazzema, Apuan Alps, Tuscany, Italy. It occurs as euhedral octahedra, up to 0.1 mm in size, embedded in dolostone lenses in the baryte + pyrite + iron oxides ore. Associated minerals are calcite, cinnabar, derbylite, dolomite, hematite, 'mica', pyrite, sphalerite and 'tourmaline'. Oxycalcioroméite is reddish-brown in colour and transparent. It is isotropic, with ncalc = 1.950.

Electron microprobe analysis gave (wt.%; n = 6) Sb2O5 63.73, TiO2 3.53, SnO2 0.28, Sb2O3 10.93, V2O3 0.68, Al2O3 0.28, PbO 0.68, FeO 5.52, MnO 0.13, CaO 13.68, Na2O 0.83, F 1.20, O = F – 0.51, total 100.96. No H2O, above the detection limit, was indicated by either infrared or micro-Raman spectroscopies. The empirical formula, based on 2 cations at the B site, is (Ca1.073Fe2+0.338Sb3+0.330Na0.118Pb0.013Mn0.008)Σ=1.880(Sb5+1.734Ti0.194V0.040Al0.024Sn0.008)Σ=2.000(O6.682F0.278)Σ6.960. The crystal structure study gives a cubic unit cell, space group Fdm, with a 10.3042(7) Å, V 1094.06(13) Å3, Z = 8. The five strongest X-ray powder diffraction lines are [d(Å)I(visually estimated)(hkl)]: 3.105(m)(311); 2.977(s)(222); 2.576(m)(400); 1.824(ms)(440); and 1.556(ms)(622). The crystal structure of oxycalcioroméite has been solved by X-ray single-crystal study on the basis of 114 observed reflections, with a final R1 = 0.0114. It agrees with the general features of the members of the pyrochlore supergroup.

Combined microfocus XAS and XRD analysis of α-particle radiation damage haloes around thorium-containing monazite in Fe-rich biotite reveals changes in both short- and long-range order. The total α-particles flux derived from the Th and U in the monazite over 1.8 Ga was 0.022 α particles per atomic component of the monazite and this caused increasing amounts of structural damage as the monazite emitter is approached. Short-range order disruption revealed by Fe K-edge EXAFS is manifest by a high variability in Fe–Fe bond lengths and a marked decrease in coordination number. XANES examination of the Fe K-edge shows a decrease in energy of the main absorption by up to 1 eV, revealing reduction of the Fe3+ components of the biotite by interaction with the 24He2+, the result of low and thermal energy electrons produced by the cascade of electron collisions. Changes in d spacings in the XRD patterns reveal the development of polycrystallinity and new domains of damaged biotite structure with evidence of displaced atoms due to ionization interactions and nuclear collisions. The damage in biotite is considered to have been facilitated by destruction of OH groups by radiolysis and the development of Frenkel pairs causing an increase in the trioctahedral layer distances and contraction within the trioctahedral layers. The large amount of radiation damage close to the monazite can be explained by examining the electronic stopping flux.

Štěpite, tetragonal U(AsO3 OH)2(H2O)4 (IMA 2012-006), is the first natural arsenate of tetravalent uranium. It occurs in the Geschieber vein, Jáchymov ore district, Western Bohemia, Czech Republic, as emerald-green crystalline crusts on altered arsenic. Associated minerals include arsenolite, běhounekite, claudetite, gypsum, kaatialaite, the new mineral vysokýite (IMA 2012-067) and a partially characterized phase with the formula (H3O)+2(UO2)2(AsO4)2˙6H2O. Štěpite typically forms tabular crystals with prominent {001} and {010} faces, up to 0.6 mm in size. The crystals have a vitreous lustre and a grey to greenish grey streak. They are brittle with an uneven fracture and a very good cleavage on (001). Their Mohs hardness is about 2. Štěpite is not fluorescent in either short-wave or long-wave ultraviolet light. It is biaxial (–) with refractive indices (at 590 nm) of α = 1.636(2), β = 1.667(3), γ = 1.672(2) and 2Vobs < ~5°, anomalous greyish to pale yellow interference colours, and no pleochroism. The composition is as follows: 0.12Na2O, 50.19 UO2, 0.04SiO4, 0.09 P2O5, 0.93 As2O5, 1.95 SO3, 16.41 H2O; total 107.90 wt.%, yielding an empirical formula (based on 12 O a. p. f. u.) of (U1.01Na0.02)Σ1.03[(AsO3OH)1.82 (PO3OH)0.04(SO4)0.13(SiO4)0.01]Σ 2.00˙4H2O. Štěpite is tetragonal, crystallizing in space group I41/acd, with a = 10.9894(1), c = 32.9109(6) Å, V = 3974.5(1) Å3, Z = 16 and Dcalc = 3.90 g cm-3. The six strongest peaks in the X-ray powder-diffraction pattern [dobs in Å (I) (hkl)] are as follows: 8.190(100)(004), 7.008(43)(112), 5.475(18)(200), 4.111(16)(008), 3.395(20)(312,217), 2.1543(25)(419). The crystal structure of šteěpite has been solved from singlecrystal X-ray diffraction data by the charge-flipping method and refined to R1 = 0.0353 based on 1434 unique observed reflections, and to wR2 = 0.1488 for all 1523 unique reflections. The crystal structure of štšpite consists of sheets perpendicular to [001], made up of eight-coordinate uranium atoms and hydroxyarsenate 'tetrahedra'. The ligands surrounding the uranium atom consist of six oxygen atoms which belong to the hydroxyarsenate groups and two oxygen atoms which belong to interlayer H2 O molecules. Each UO8 polyhedron is connected to five other U polyhedra via six AsO3OH groups. Adjacent electroneutral sheets, of composition [U4+(AsO3OH)22-]0, are linked by hydrogen bonds involving H2 O molecules in the interlayers and OH groups in the sheets. The new mineral is named in honour of Josef Štěp (1863–1926), a Czech mining engineer and 'father' of the world's first radioactive spa at Jáchymov.

Fine-grained garnet (grains <50 μm across) is an accessory component of compact hematite, a rock consisting essentially of hematite; compact hematite is a variety of high-grade Fe ore. The garnet is characterized compositionally as spessartine (81–86 mol.%) with subordinate, but significant, amounts of calderite (5–11 mol.%) and “blythite” (up to ∼5 mol.%), as well as andradite (4–7 mol.%); pyrope and almandine endmembers are ≤∼2 and 1 mol.%, respectively. The recognition of spessartine in compact hematite indicates that oxidation state, rather than whole-rock chemical composition, controlled the garnet composition. The spessartine has a positive Eu anomaly, and a low Th/U ratio (0.13–0.65) compared to the average upper continental crust, Th/U = 3.9, as well as a positive linear correlation of U vs. Li. The spessartine-hosting compact-hematite rock is a high-grade hematite ore that similarly shows a low Th/U ratio, but a convex, tetrad-like segment between Gd and Dy. Decoupling of Eu from other rare-earth elements and of U from Th in the spessartine, together with the anomalous geochemical behaviour of Gd, Tb and Dy in the compact hematite, and its low Th/U ratio, could have been achieved under oxidizing conditions at greenschist-facies metamorphic temperatures. The U and Li present in the spessartine could have been sourced from metamorphic fluids of continental, possibly evaporitic, origin. These interpretations are underpinned by the regional hematitization and tourmalinization observed in the southern Serra do Espinhaço.

Barikaite, ideally Pb10Ag3(Sb8As11)Σ19S40, is a new mineral species from the Barika Au-Ag deposit, Azarbaijan Province, western Iran. It was formed in fractures developed in silica bands situated in massive banded pyrite and baryte ores. These fractures house veinlets that contain a number of Ag-As-Sb-Pb-rich sulfosalts, tetrahedrite-tennantite, realgar, pyrite and electrum. Barikaite appears as inclusions in guettardite. The mineral is opaque, greyish black with a metallic lustre; it is brittle without any discernible cleavage. In reflected light barikaite is greyish white, pleochroism is distinct, white to dark grey. Internal reflections are absent. In crossed polars, anisotropism is distinct with rotation tints in shades of grey. The reflectance data (%, in air) are: 37.0, 39.3 at 470 nm, 34.1, 36.9 at 546 nm, 33.1, 36.2 at 589 nm and 31.3, 34.1 at 650 nm. The Mohs hardness is 3–3½, microhardness VHN50 exhibits the range 192 – 212, with a mean value of 200 kg mm–2. The average results of five electron-microprobe analyses in a grain are (in wt.%): Pb 35.77(33), Ag 5.8(1), Tl 0.15(08), Sb 18.33(09), As 15.64(16), S 24.00(15), total 99.69(10) wt.%, corresponding to Pb9.31Ag2.90Tl0.04(Sb8.12As11.26)Σ19.36S40.37 (on the basis of 32Me + 40S = 72 a.p.f.u.). The simplified formula, Pb10Ag3(Sb8As11)Σ19S40, is in accordance with the results of a crystal-structure analysis, and requires Pb 37.89, Ag 5.91, Sb 17.79, As 15.05 and S 23.42 (wt.%). The variation of chemical composition is minor, the empirical formula ranging from Pb10.39Ag2.32Tl0.02Sb7.52As11.27S40.49 to Pb9.24Ag2.93Tl0.04Sb8.13As11.35S40.31. Barikaite has monoclinic symmetry, space group P21/n and unit-cell parameters a 8.5325(7) Å, b 8.0749(7) Å, c 24.828(2) Å, and b 99.077(6)o, Z = 1. Calculated density for the empirical formula is 5.34 (g cm–3). The strongest eight lines in the (calculated) powder-diffraction pattern [d in Å(I)(hkl)] are: 3.835(63)(022), 3.646(100)(016), 3.441(60)(212), 3.408(62)(14), 2.972(66)(16), 2.769(91)(222), 2.752(78)(24) and 2.133(54)(402). Barikaite is the N = 4 member of the sartorite homologous series with a near-equal role of As and Sb, which have an ordered distribution pattern in the structure. It is a close homeotype of rathite and more distantly related to dufrénoysite (both distinct, pure arsenian N = 4 members) and it completes the spectrum of Sb-rich members of the sartorite homologous series. The new mineral and its name have been approved by the IMA-CNMNC (IMA 2012-055).

The crystal structure of comancheite, Hg2+55N3–24(OH, NH2)4(Cl,Br)34, orthorhombic, space group Pnnm, a = 18.414(5), b = 21.328(6), c = 6.6976(19) Å, V = 2630(2) Å3, Z = 1, was solved by direct methods and refined to an R1 index of 4.3% based on 4160 unique observed reflections. In the structure of comancheite, there are nine crystallographically distinct Hg2+ cations, each of which is coordinated by two N3– anions to form near-linear N3––Hg2+–N3– groups. Four other crystallographically distinct Hg2+ cations are coordinated by a mixture of N3–, O2–, (OH)– and (NH2)– anions, and there is a small amount of [Hg–Hg]2+ dimer. In addition, there are eight crystallographically distinct halogen sites, three of which are completely occupied by Cl–, and five of which are occupied by both Cl– and Br–. The principal anion, N3–, shows a strong preference for tetrahedral coordination by Hg2+, which results in a strongly bonded three-dimensional {–Hg2+–N3––} framework. This framework is both interrupted and contains large interstices that incorporate additional Hg2+ cations, a very small amount of [Hg+–Hg+]2+ dimer and additional anion species, O2–, (OH)– and (NH2)–, that coordinate Hg2+.

Comancheite was described originally as an Hg-oxide mineral. The major change in chemical composition indicated by the present work was approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (Voting Proposal 13-B). The presence of N provides some analytical challenges, particularly in the presence of Hg. New bond-valence parameters were derived for Hg2+–N3– bonds [Ro(N3–) = 1.95] using well refined Hg2+ structures, and this allows discrimination between Hg2+–O2– and Hg2+–N3– bonds based on the valence-sum rule. Comparison of the Raman spectra of several Hg-bearing minerals shows that peaks in the range 500–700 cm–1 are characteristic of Hg2+–N3– stretching vibrations whereas peaks in the range 350–500 cm–1 are characteristic of Hg2+–O2– stretching vibrations; Hg2+–O2– and Hg2+ – N3– bonds may be discriminated on this basis.