Riet veld X-ray powder diffraction (XRD) analysis has been evaluated as a procedure for characterizing Al-substituted goethite according to the Rietveld scale factor, unit-cell parameters, and atom positional parameters. The study was conducted with three synthetic goethite samples for which the degree of Al substitution for Fe determined by chemical analysis was 8.0 ± 0.4, 12.0 ± 0.4, and 20.1 ± 0.4 mole %. The weight fractions of crystalline material (WFCM) in the specimens, determined from the Rietveld scale factors after correcting for adsorbed water and impurities, were 0.878 (esd = 0.014), 0.919 (0.014), and 0.965 (0.015), respectively. The Al mole % substitutions, inferred from the Rietveld cell parameters according to the method of Schulze (1984), were 10.4 ± 2.5, 16.5 ± 2.6, and 17.1 ± 2.6, respectively. The cause of the significant difference between the second value and the chemical analysis result is not known. The atom positional parameters did not differ significantly within the sample suite and agreed satisfactorily with literature values. The results have demonstrated the value of using Rietveld XRD analysis to determine simultaneously the WFCM and Al mole % substitutions, as well as to confirm the non-hydrogen atom positions.

The Upper Cretaceous (Maastrichtian) Whitemud Formation is a potentially commercial kaolin deposit located in southern Saskatchewan and southeastern Alberta. The Whitemud Formation contains a lower kaolinitic sandstone, a middle lignite and carbonaceous shale, and an upper interbedded siltstone and claystone. The sediments that comprise the rocks of the Whitemud Formation were deposited on alluvial or upper deltaic plains located along the northwest flank of the Williston Basin.

Mineralogy and textures were determined by X-ray powder diffraction, scanning electron microscopy, and optical microscopy. Kaolinite abundance increases upward from the underlying rocks of the Eastend Formation through the Whitemud Formation, and the abundance of smectite, micas, and feldspars decreases from the Eastend Formation into the Whitemud Formation. Vermiform kaolinite crystals are in close spatial association with feldspar and mica grains. Near the top of the Whitemud Formation, etched quartz and feldspar grains, and gibbsite suggest the presence of a strong chemical leaching environment.

Mineral distributions, presence of root remains, pedologic mottles, grain coatings composed of clay, and soil horizons indicate the Whitemud Formation sediments were modified by intense weathering in a paleosol environment.

Kaolin concentrated from selected kaolinitic sandstone deposits, and beneficiated by oxidation, leaching, and high-intensity wet-magnetic separation has a product brightness up to filler quality. Recovery of lowabrasion kaolin is low and viscosity of a fine-particle kaolin fraction is high. Economics of producing a wet-processed filler-grade kaolin is marginal.

The rate of Fe(II) oxidation at a constant rate of oxygen supply in the presence of citrate was measured at pH 6.0 at various citrate/Fe(II) molar ratios at 23.5°C in 0.01 M ferrous Perchlorate system. The kinetics followed a first-order reaction with respect to Fe(II) concentration at constant pH (6.0) and aeration (5 ml/min). The rate constant decreased exponentially from 41.3 × 10-4 to 7.6 × 10-4/min with an increase in the citrate/Fe(II) molar ratio from 0 to 0.1.

The nature of the hydrolytic products formed after 120 min of oxidation was arrived at by X-ray powder diffraction (XRD), infrared spectrometry (IR), and transmission electron microscopic (TEM) analyses. In the absence of citrate, goethite (α-FeOOH) and poorly crystalline lepidocrocite (γ-FeOOH) were the oxidation products formed at pH 6.0. The formation of lepidocrocite was promoted at the expense of goethite at citrate/Fe(II) molar ratios of 0.0005 to 0.005. The formation of lepidocrocite was especially pronounced at a citrate/Fe(II) molar ratio of 0.001, as observed from the width at half height (WHH) and the area of the 020 XRD peak of lepidocrocite. At a citrate/Fe(II) molar ratio of 0.01, however, the crystallization was perturbed resulting in the formation of noncrystalline Fe oxides, and no precipitate was observed at a citrate/Fe molar ratio of 0.1. The strong complexation of Fe(II) with citrate retarded the kinetics of Fe(II) oxidation and the formation and hydrolysis of Fe(III). The complexation, electrostatic, and steric effects of the coexisting citrate anions in solution apparently influenced the oxygen coordination and the way by which the double rows of edge-sharing Fe(O,OH)6 octahedra linked during crystallization, resulting in the formation of lepidocrocite.

The chemical composition and the thermal behavior of sodium and hydrogen octosilicate was studied by chemical and thermal analysis, infrared (IR), magic-angle-spinning nuclear magnetic resonance (MAS-NMR) spectroscopy, and X-ray diffractometry. Both compounds are layer silicates with basal spacings of 11.10 and 7.38 Å, respectively. In both forms the ratio of Q4 silicon (connected via oxygen bridges with four silicon atoms) to Q3 silicon (connected with only three other Si atoms) is 1. At least a small part of the Q4 silicon can be substituted by aluminum. Elimination of water coordinated to the cations in sodium octosilicate results in a concomitant structural collapse. Replacement of the sodium ions by protons affects the atomic arrangement in the sheets only to a minor degree, but results in a decrease of the periodicity along the crystallographic c axis. Upon heat treatment an endothermal structural rearrangement occurs at about 360 K as revealed by significant changes of the IR and 29Si MAS-NMR spectra. Reexchange with Na ions largely, but not completely, restores the structure of the parent octosilicate.

The X-ray diffraction pattern of sodium octosilicate was indexed in the monoclinic system with a = 7.345 Å, b = 12.74 Å, c = 11.25 Å and β = 99.3°. Based on conclusions drawn from the results of the present study, the X-ray pattern of hydrogen octosilicate was tentatively indexed in the monoclinic system with a = 7.345 Å, b = 12.74 Å, c = 8.51 Å and β = 119.8°.

Unheated natural mixtures of manganite and secondary pyrolusite, from the same lateritic manganiferous sequence, were studied in different orientations by high-resolution transmission electron microscopy (HRTEM), electron diffraction, and energy-dispersive X-ray analysis (EDX) to determine the fine structure of these phases, their possible crystallographic relations, and the genetic processes that led to the formation of the pyrolusite. Typical palisadic texture was observed for both minerals. Characteristic cracks parallel t. (010) of the pyrolusite structure and in particular <210> microfissures in manganite were noted as signs of structural accommodation accompanying the transformation phenomenon between these two minerals. A previously unreported manganese oxide of the spinel-type (γ-Mn2O3 or Mn3O4) was also identified in the original mixture. This oxide gave pure microdomains as intergrowths with pyrolusite adjacent to manganite. This is the first report of a natural occurrence of γ-Mn2O3. The manganite-pyrolusite transformation process and an unsuspected γ-Mn2O3 (Mn3O4)-pyrolusite transition were directly illustrated in detail for the first time. Interfaces between the concerned phases were not sharp or smooth, but exhibited strong strain contrasts and interferential periodicities. Lattice images and microdiffraction patterns proved that both transformations were oriented, suggestive of topotactic relations. In addition, the principal minerals in the matrix (illite, kaolinite, and goethite) were examined for a better understanding of their role in Mn-oxyhydroxides transformations.

The interaction of Mn and akaganéite in neutral to alkaline media has been investigated using X-ray powder diffraction and transmission electron microscopy. Akaganéite transformed into goethite and/or hematite, whereas Mn precipitated as hausmannite and birnessite at pH > 12 and as manganite at pH 7.5–8.5. Mn influenced the kinetics of the transformation of akaganéite: the rate-determining step, i.e., the dissolution of akaganéite, was retarded by adsorbed Mn species. Hematite formation was not suppressed. By catalyzing the air oxidation of adsorbed Mn(II), akaganéite promoted the formation of birnessite. Akaganéite did not retard recrystallization of the Mn phases. The incorporation of Mn in the structure of goethite formed in this system was negligible, and jacobsite (MnFe2O4) did not form. The formation of mixed Mn-Fe phases appeared to require a ratio of Mn2+: Fetotal > 0.02; this ratio was not achieved due to the oxidation of Mn2+ at the akaganéite surface.

Two distinct zonal sequences of clay minerals (H- and L-type) were found around silicified rocks in the Makurazaki volcanic area, Kagoshima Prefecture, Japan. The clay mineral sequences from the inner to the outer parts of the alteration aureoles are: 1. H-type, pyrophyllite → dickite → 2M2 mica → sudoite → tosudite; and 2. L-type, kaolinite → rectorite → smectite. The structural formula for the sudoite is: (Al1.04Mg1.28Fe3+0.20Ti0.03Li0.01K0.02Na0.01(OH)6Al2.00(Si3.54Al0.46)O10(OH)2. It is characterized by relatively large amounts of Mg and very small amounts of Li. The polytype is identified as IIb. The chemical analysis of tosudite shows that the sample is composed of an interstratification of sudoite-like and beidellite-like layers. The structural formula for rectorite is: (K0.45Na0.19Ca0.01Mg0.01)(Al1.81Fe3+0.04Mg0.13Ti0.03)(Si3.41Al0.59)O10(OH)2, suggesting that the nonexpandable and expandable layers have K-mica-like and beidellite-like compositions, respectively. These clay minerals in the H- and L-type alteration aureoles were formed under relatively high- and low-temperature conditions, respectively, with pH value and K- and Mg-activities increasing as the fluids ascended through the wall rocks.

Direct water-activity measurements were made for calcium-smectite-CaCl2 mixtures. The samples used were prepared by high-pressure filtration and had water contents <0.60% by weight of clay. For deionized water, the water activity (aw) ranged between 1 and 0.4 and was independent of the pressure history of the clay cake. Good agreement was found with the results of an adsorption isotherm. Samples were also prepared in 1,3, and 5 M CaCl2 solutions. The final concentration of chloride present in the cakes was measured: substantial anion exclusion was observed. The water activity of the clay-salt mixtures depended on both the water content and the concentration of CaCl2. The data can be well represented by the expression aw = min(aw0, aw*c × aw*s), where aw0 is the water activity of the brine used to prepare the cake, and aw*c and aw*s are water activities calculated for clay (in absence of salt) and salt (in absence of clay), respectively. The compaction and swelling behavior of a core of the same Ca-smectite was also investigated for pressures (P) between 0.5 and 800 bar. In two compaction-swelling cycles total recovery of the void ratio (e) was observed with, however, large hysteresis in the relationship between e and P. The osmotic pressure developed in the core at equilibrium, evaluated using the water-activity data, was intermediate between the compaction and swelling pressures. Apparently, another force, Pm, linked to irreversible changes in the structure of the matrix was contributing to the resistance to compaction. Pm values agreed with literature results for Ca-smectite suspensions.

The adsorption of citrate, at 10 4−10−3 M initial concentration, by pseudoboehmite suspended in 0.02 M NaC1O4 was investigated at varying pH. Citrate shows a strong affinity for the pseudoboehmite surface, as seen in the adsorption isotherm at pH 6. Adsorption envelopes of adsorbed citrate vs. pH for a given initial citrate concentration are characteristic for the adsorption of a polyprotic acid by a variable-charge mineral. The envelope data were fit well by the Constant Capacitance Model assuming a ligand-exchange adsorption mechanism, three monodentate surface species of citrate, and a reactive surface OH density of 0.4 mol kg−1. Aqueous speciation calculations suggest that solubility equilibrium with pseudoboehmite was attained at pH > 9 and that particulate or polymeric Al may have existed at 6 < pH < 9. Dissolved Al appeared to reduce the adsorption of citrate at pH < 5.5 via solution complexation reactions.

The hydrothermal synthesis of kaolinite was examined in the Al2O3-SiO2-H2O system to study inhibitory effects of additional ions on the formation of kaolinite. Syntheses were carried out with amorphous starting materials and salt solutions of various concentrations in Teflon pressure vessels at 220°C for 5 days. The reaction products were characterized by XRD, IR, DTA-TG, NMR and TEM. In all of the runs using solutions with cation concentrations less than 0.001 M, no significant effect on the formation of kaolinite was observed. The inhibitory effect of the univalent cations Li+, Na+ or K+ was less than that of divalent cations such as Mg2+ or Ca2+. The addition of trivalent Fe3+ or excess Al3+ ions interfered with the formation of kaolinite significantly. Sulfate and acetate solutions interfered with the formation of kaolinite more than chlorides and nitrates. No crystalline product was obtained using a 1.0 M basic solution of carbonate or hydroxide. The addition of the lithium ion to the system affected the crystallization of kaolinite only slightly. The use of 0.1 M LiCl and LiNO3 solutions for the syntheses improved crystallization of kaolinite along the [001] direction.

A new iron oxide dissolution method designed to measure the abundance of “free” Fe oxide phases and associated elements in soils and sediments has been tested. The method employs a ternary complex of Ti(III), citrate, and ethylenediaminetetraacetate (EDTA) as a reductant and bicarbonate as a proton acceptor. The Ti(III)-citrate-EDTA-HCO3 method dissolved more synthetic amorphous ferric oxide and goethite, but less synthetic hematite, than the dithionite-citrate-HCO3 method of Mehra and Jackson. The production of acidity by the dissolution indicated that Ti(IV) is hydrolyzed to TiO2 during the extractions. The heated dithionite method dissolved 3–6 times more Al from kaolinite and nontronite standard clays than room temperature dithionite, and 4–6 times more Al than the Ti(III)-citrate-EDTA-HCO3 method. Furthermore, the release of Fe from the clay mineral samples consistently and rapidly reached a plateau during multiple extractions by the Ti(III)-citrate-EDTA-HCO3 method, indicating that a well-defined Fe oxide fraction was removed. Fe released by the dithionite method continued to increase with each extraction, suggesting that some release of structural Fe occurred. Tests on two natural sediments and one heavy mineral fraction from the Miocene Cohansey Sand in the New Jersey Coastal Plain suggested that the Ti(III)-citrate-EDTA-HCO3 method removed Fe oxides more effectively and more selectively than the dithionite method. The selectivity of the Ti(III)-citrate-EDTA-HCO3 method is enhanced by rapid extractions at room temperature and low free ligand concentrations.

To determine the parameters that control the attack of Mn minerals by acid ammonium oxalate in darkness (AAOD), rhodochrosite, pyrolusite, manganosite, hausmannite, and bixbyite were shaken with AAOD for 2 hr. These treatments were followed systematically by X-ray powder diffraction (XRD) and AAOD-extractable Mn analyses. About 5% of original hausmannite (surface area = 6 m2/g) remained in the solid residue of the AAOD treatment; however, if the hausmannite surface area was increased to 8 m2/g, by grinding, it completely dissolved in oxalate. Synthetic hausmannite of high surface area (37 m2/g) and rhodochrosite were completely dissolved by oxalate. Manganosite (1.5 m2/g) and especially pyrolusite (~ 1 m2/g) were more resistant to AAOD attack. Ground manganosite (4.2 m2/g) dissolved completely, but ground pyrolusite (7.2 m2/g) was only partially attacked by AAOD, inasmuch as about 25% of pyrolusite was found in the residue. An increase of the extraction time to 4 hr did not completely dissolve the ground pyrolusite.

As a result of the AAOD treatment, MnC2O4 · 3H2O and MnC2O4 · 2H2O precipitated from the oxalate solutions with all starting minerals, except pyrolusite (~ 1 m2/g), which only slightly dissolved. The seldom reported MnC2O4 · 3H2O phase was identified in residues of freshly extracted samples by its strong characteristic peak at 6.5.-6.6 Å, the intensity of which gradually decreased and disappeared over several days when the sample was exposed to ambient conditions (22°C and 70% relative humidity). The trihydrate phase also collapsed after heating AAOD-treated rhodochrosite at 50°C; α-MnC2O4 · 2H2O was identified as the main crystalline product. Heating the α-MnC2O4 · 2H2O product at 115°C overnight transformed most of it to MnC2O4. The color of the oxalate-treated samples ranged from pinkish-gray to black (7.5 YR); their surface area ranged from about 20 to 30 m2/g. The degree of transformation of Mn minerals by oxalate depended on the surface area and structural characteristics of the starting materials.

The effect of electrolyte concentration, exchangeable sodium percentage (ESP), sodium adsorption ratio (SAR), and pH on the flocculation-dispersion behavior of 50/50 mixtures of reference illite with reference kaolinite or reference montmorillonite was investigated. The clays were Na- or Ca-saturated and freeze-dried before use. Critical coagulation concentrations (CCCs) were investigated in the range of pH 5.9 to 9.6, percent Na-clay 0, 10, 20, 40, 60, 80, and 100 and SAR 0, 10, 20, 40, 60, 80, and ∞. CCC values increased with increasing ESP, increasing SAR, and increasing pH. The pH dependence of illite/kaolinite was greater than that of illite/montmorillonite especially at high ESP and SAR. The presence of illite did not play a dominant role in determining flocculation-dispersion behavior of the 50/50 clay mixtures. The CCCs of illite/kaolinite resembled reference illite more than reference kaolinite for SAR 0 to SAR 60. Illite/montmorillonite exhibited CCCs more similar to reference illite than reference montmorillonite at SAR 40 and SAR 60. At the agriculturally desirable ESP and SAR values of 0 to 15, all the 2:1 clays and 2:1 clay mixtures demonstrated similar CCC values.

The surface free energy components of clay-organic complexes were determined to assess to what extent an organic adsorbate modified the surface properties of the mineral, insofar as the stability of soil aggregates is concerned. Adsorption isotherms for two synthetic, humic acid-like polymers were determined on a Ca-montmorillonite. From contact-angle measurements performed on dry surfaces, the surface free energy properties of the clay-organic complexes were determined using the two-liquid-phases method (water and hydrocarbons). This method allows both the dispersive and nondispersive components of the solid surface free energy, γDS and γPS, to be determined. The results show that a very small amount of polymer (1% by weight) adsorbed on the external surfaces of the montmorillonite decreased markedly the surface free energy components of the clay: γDS decreased from 75 to 28 mJ/m2 for polycondensate catechol (PC) and from 75 to 30 mJ/m2 for polycondensate catechol triglycine (PCT), whereas γPS ranged from 35 to 16 mJ/m2 (PC) and from 35 to 17 mJ/m2 (PCT). Although their chemical compositions were different, both polymers similarly modified γDS and γPS. Increasing the amount of polymer adsorbed (from 1% to 3.5% by weight) affected mostly γPS, which became as low as 5 mJ/m2; meanwhile, γDS decreased from 30 to 23 mJ/m2. Possibly, the molecular orientation of the adsorbate changed in the process of dehydration. Following adsorption of synthetic humic acid-like polymers, dry Ca-montmorillonite complexes displayed γS values < 50 mJ/m2, which were consistent with the solid-water contact angles measured in air.

The effect of layer charge and of the interlayer cations of smectites on the hydrolysis of azinphosmethyl (0,0-dimethyl S-((4-oxo-l,2,3-benzotriazine-3(4H)-yl)methyl) phosphorodithioate) in an aqueous medium was investigated. Ultraviolet spectroscopy was used for monitoring the hydrolysis process. Hydrolysis of the pesticide is catalyzed by Ca-hectorite (layer charge 0.216) but is not catalyzed by Ca-nontronite nor by Ca-montmorillonites with a layer charge above 0.216. The Mg- and Cu-hectorites and Cu-montmorillonite with a layer charge of 0.264 also show catalytic activity. The catalytic activities of the Ca2+ and Cu2+ cations as exchange cations of the smectite and as salts are compared. In agreement with previously reported work, the results show that the hydrolysis of azinphosmethyl may involve the adsorption of the pesticide into the interlayer space of the smectites, forming a bidentate complex with the interlayer cations. This interaction must enhance the electrophilic nature of the phosphorus atom, thereby facilitating its nucleophilic attack by the OH-ion and producing rupture of the P-S bond.

The reaction of gibbsite in various organic solvents at 250°–300°C under spontaneous vapor pressure of the solvents was examined. Glycols and aminoalcohols afforded the organic derivatives of boehmite in which one of the oxygen atoms of the glycol molecule or the alcoholic oxygen atom of aminoalcohol was incorporated into the boehmite layers. By increasing the molecular size of the solvent, the yield of the boehmite derivative decreased, and, at the same time, the basal spacing of the boehmite derivative increased. The product had a honeycomb texture on the surface of the particle, which suggests a dissolution-recrystallization mechanism for the formation of the boehmite derivatives. A hydroxyl group and a functional group, such as hydroxyl, methoxyl, or amino group having the ability to donate its lone pair electrons, were apparently necessary for the organic solvent molecules to form the boehmite derivative by this mechanism.

Dealumination of vermiculite was carried out using (NH4)2SiF6 solutions. The dealuminated products were studied by high-resolution solid state 29Si and 27Al nuclear magnetic resonance. A decrease in the cation-exchange capacity (CEC) resulted from the partial removal of Al from the tetrahedral layer, which decreased the framework negative charge, and from the partial replacement of Mg by Al in the octahedral layer, which increased its positive charge contribution. The lowest CEC was obtained by swelling the structure with butyl-ammonium prior to the reaction with (NH4)2SiF6. Thus, CECs in the range observed for beidellite were measured; however, the lowest (Al/Si)IV ratio was still more than twice as high as in beidellite. In addition, the dealumination reaction yielded noncrystalline silica as a by-product.

In contact with a solution of Al hydroxypolymer (Al13), the dealuminated vermiculite showed no 18-Å reflection characteristic of Al13-intercalated smectite; instead it showed an ill-defined interstratification. For some samples, however, a significant increase in the specific surface area (as much as 230 m2/g) was observed, suggesting that an intercalation of Al moieties did occur. The 27Al resonance spectra of the intercalated structure showed at least two components in octahedral coordination. On thermal activation, a resonance line attributable to pentacoordinated Al was observed.

Hydroxy-Al-montmorillonite was prepared by mixing Na-Wyoming montmorillonite with Al(OH)2.5 polycations and aging the mixture for 10 days. The reactions of this complex with citric acid at millimolar concentrations were investigated at different pHs for a 4-hr reaction time. The citrate sorption data, X-ray powder diffraction patterns of the montmorillonite adsorbent, and solubility products for Al(OH)3, estimated after computer speciation of the aqueous solution phase, suggested two reaction mechanisms, depending on pH. At 4 < pH < 5.5, the complex was stable, and only external hydroxy-Al polycations could react with citrate, yielding a sorption envelope characteristic of an acid having a low pKa. At higher pH, and particularly at pH > 7, the interlayer Al-polymers became accessible to the ligand and desorbed quickly from the montmorillonite basal planes to form a new, external, X-ray-amorphous solid phase with citrate. This reaction produced a large second peak in the sorption envelopes near pH 8, which was controlled by the increasingly negative surface charge at high pH and by the initial concentration of citric acid. This ligand accelerated, i.e., favored kinetically, the dissociation of adsorbed hydroxy-Al polymers from montmorillonite at pH > 7.

X-ray diffraction and chemical analyses were performed on clay fractions separated from an acid brown soil (Dystrochrept) by means of size fractionations using high-gradient magnetic separation techniques. Breakdown of large phyllosilicates preexisting in the saprolite involved physical fragmentation and mineralogical transformations strongly related to chemical weathering.

Compared to the C horizon, the proportion of chlorite and vermiculite decreased strongly in the silt and coarse-clay fractions of the Al horizon, but was maintained in the finer clay fraction (< 1 μm). The distribution of mica in the different fractions was quite the opposite. Micas are the major component of the Al, 1–2 μm fractions, and their proportion progressively decreased with decreasing fraction size. Thus, it is concluded that during fragmentation and/or simple transformation of the larger phyllosilicates, clusters of chlorite, mica/vermiculite, and vermiculite layers were preferentially affected. A concentration of mica layers took place in the coarse clay fractions as chlorite and vermiculite residues were accumulated in the fine clays.

The process involved the loss of Fe and Mg, leaving, or forming, more aluminous dioctahedral minerals. As the transformation processes occurred, dissolution of preexisting minerals led to the precipitation of amorphous and/or crystalline Fe- and Al-oxides, and possibly of phyllosilicates. The new phyllosilicates appear to be montmorillonitic.

The most abundant end products of the weathering processes in either the Al or the Bw horizons appeared to be quite different. In the Al horizon they were identified mainly a hydroxyl-Al (Fe) intergrade smectite (montmorillonite), whereas in the Bw horizon the major component was an intergrade vermiculite originating, at least in part, from chlorite.

Iron phyllosilicates with 1:1 and 2:1 layer structures were prepared from silicic acid, ferrous sulfate and sodium hydroxide. Hydrothermal treatment at 100–200°C of a reaction mixture with an initial Fe/Si ratio of 1.5 gave the 2:1 iron phyllosilicate, whereas a Fe/Si ratio of 2.25 gave the 1:1 phyllosilicate. The 57Fe Mössbauer spectroscopy showed that 60% of the iron in the 1:1 phyllosilicate is ferrous, versus only 3% in the 2:1 phyllosilicate. The values of quadrupole coupling showed that the iron-oxygen tetrahedra and octahedra in the 2:1 phyllosilicate were more deformed than those in the 1:1 phyllosilicate.