In general, the N2-BET surface areas of sepiolite samples range from 95 to 400 m2/g depending on deposits.

The surface areas of five sepiolites, all varying in crystallite size, were measured on heating, and were compared with a model calculation. A sharp decrease in the surface area, due to crystal folding, was observed between 200° and 400°C. Both before and after the folding, each sepiolite sample had peculiar values. Our model sufficiently explains this difference in surface areas among the samples. In the model, which is based on the Brauner-Preisinger structural model, surface area is a function of the crystallite size and the ratios of the coverage for nitrogen adsorption on both the internal and external surfaces. These ratios of the coverage can be inversely estimated from the model. The ratios of the coverage on the internal surface are less than 0.19, and that on the external surface between 0.7 and 1.0.

Experimental alterations of K-feldspar in distilled-deionized water at 150°, 175°, 200°, and 225°C were performed. The alteration products and dissolution mechanism of K-feldspar were examined by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX), and X-ray photoelectron spectroscopy (XPS). SEM, TEM, and EDX clearly showed formation of fibrous boehmite less than 1.0 μm in length at the early alteration stages. The boehmite fibers decreased in abundance and rounded platy 1 M mica was produced as alteration proceeded. The mica exhibited initially angular shaped small flakes of 0.69 μm in average size, which developed to rounded platy particles of 1.97 μm. The main chemical reactions occurring in this experimental system can be expressed by: $$\begin{array}{l} \mathop {KAlS{i_3}{O_3}}\limits_{\left[ {K - feldspar} \right]} + 6{H_2}O + {H^ + } \to \mathop {AlO\left( {OH} \right)}\limits_{\left[ {boehmite} \right]} + 3{H_4}Si{O_4} + {K^ + }, \\ \mathop {3KAlS{i_3}{O_8}}\limits_{\left[ {K - feldspar} \right]} + 12{H_2}O \to \mathop {KA{l_3}S{i_3}{O_{10}}{{\left( {OH} \right)}_2}}\limits_{\left[ {mica} \right]} + 2{K^ + } + 6{H_4}Si{O_4} + 22{H^ + }. \\ \end{array}$$ XPS showed no significant changes in intensities of photoelectron lines excited from K, Si, and Al in the K-feldspar surface before and after alteration, however the K/Si molar ratios in the solutions were considerably smaller than that of the original K-feldspar. The results of XPS strongly indicate that no dealkalized layer was produced on the surface, and that dissolution of K-feldspar in aqueous solution proceeded congruently by a surface-reaction mechanism. The discrepancy of mass balance in the solutions may be mainly caused by adsorption of K on the surface of boehmite.

The association between clay silicates, and iron and aluminium oxides has a major influence on the chemical and physical properties of soils. In this work the interaction of a kaolin substrate with iron and aluminium oxides and/or hydroxides obtained by basification of solutions of the metal ions was compared to that of quartz. Both precipitates were obtained in the presence of the substrates.

The aluminium precipitates had higher crystallinity, and thus led to smaller increases in specific surface area than those of iron, and were more effective modifiers of the surface electrical properties of the kaolin-oxide mixtures. At concentrations as low as 0.43% Al (g/100 g of substrate) the point of zero charge (PZC) of the components with variable charge was measurable, while Fe required 2.23% and gave lower PZCs than those of corresponding concentrations of Al. In both cases the PZCs shifted to higher pH as metal concentration was increased, as did the flocculation interval of colloidal suspensions of kaolin, which were close to the PZCs (where these were evaluated).

The Al and Fe oxides precipitated on quartz had higher crystallinities. Both metals increased the specific surface area to a similar extent, with an almost linear relationship to metal concentration. Samples containing ca. 6.5% Fe or Al had similar or slightly higher PZCs than corresponding kaolin samples.

The results were interpreted by assuming, in the case of kaolin, the union of the metal precipitate with the basal faces of the substrate, so decreasing the negative charge at this surface; and in the case of quartz, the formation of a hydroxide coating that neutralizes the negative charge on the silica surface. The difference between the results obtained for each metal was attributed to the different morphologies of their oxide precipitates.

Novel promising modified clays adsorbents were synthesized by intercalating hydroxy-Al polymer associated with poly(ethyleneoxide) in the interlayer of montmorillonite. Two different PEOs of low molecular weight (600) and high molecular weight (100,000) were used. In both cases, the resulting materials are hydrolytically stable and display a slightly better crystallinity than the materials prepared in the absence of PEO. Thermal analysis and infrared spectroscopy indicate changes in the PEO molecular conformation after intercalation revealing interactions between the polycations and the organic molecules. The chain length of the polymer has a strong influence on the surface area of the pillared materials obtained after calcination at 500°C. The use of the high molecular weight polymer leads to products with a higher specific surface area (about 400 m2/g) whereas the lower molecular weight compound does not modify significantly the surface areas. This behavior can be explained by the different nature of the species intercalated in the interlayer. PEO(600) leads to isolated organometallic species whereas PEO(100,000) seems to lead to a network of complexed polycations linked by ethylene oxide units. In the case of the PEO(100,000), high amounts of polymer in the pillaring solution provoke a partial dissolution of the octahedral layer of the clay.

Historically, the decarbonation of Mg-Al-CO3 hydrotalcite-like compounds (HTlc) has been thought to occur between 400° and 500°C. The present work demonstrates that when HTlcs having the maximum Al content, Al/(Al + Mg) = 0.33, are heated to 500°C, 20–30% of the carbonates remain. The evolution of the remaining carbonates was observed as two maxima, at 600 and 900°C At these temperatures, Al ions go into MgO, and spinel (MgAl2O4) forms. Therefore, the carbonates are released as the Al ions migrate.

At a lower Al content, Al/(Al + Mg) = 0.25, CO2 evolution is almost complete at 500°C. This HTlc has no maximum of CO2 evolution above 500°C. Lower charge densities, due to lower Al contents, lead to lower amounts of remaining carbonate anions.

A laboratory study of the hydraulic conductivity (HC) of a marine clay with monovalent, divalent and trivalent cations revealed large differences in HC. The exchangeable cations employed in this study are Na, K, NH4, Mg, Ca and Al in order of increasing valency. An interpretation of the results derived from consolidation tests suggests that HC is significantly affected by the valency and size of the adsorbed cations. An increase in the valency of the adsorbed cations leads to quicker rates of consolidation and higher HC, while, for a constant valency an increase in the hydrated radius of the adsorbed cations results in a lower rate of consolidation and HC. The reduction in HC was related to the dispersion and deflocculation of clay. Lower valency and higher hydrated radii of the exchangeable cations enable the double layer repulsive forces to predominate, thereby increase dispersion and deflocculation.

A new model for the description of the structural disorder in natural kaolinite materials is proposed, based on the stacking of two 1:1 layers and their enantiomorphs, and encompassing previously proposed models. The layers, where randomly stacked along the c axis (using probabilistic functions nested in recursive algorithms), correctly describe the observed powder diffraction patterns of natural kaolinites with any density of structural faults. The proposed model was evaluated using electrostatic energy calculations against earlier models of disorder based on layer shift, layer rotation, statistical occupancy of the Al octahedra, or enantiomorphic layers. The present 4-layer model has a minimum of potential energy with respect to the previous models. As expected, the fully ordered triclinic structure of kaolinite possesses the absolute minimum of potential energy.

Young marine green grains, from Fe-rich sediments, were studied by using HRTEM systematically combined with punctual microchemical EDX analyses. Experimental results demonstrated these grains were made of a mixture of very small phases (mainly 1:1 and 2:1 silicates layer phases) with a dominant 7-Å Fe specie. All the main crystallochemically characterized phases appeared intimately related in the same evolutionary process. Each of them experienced different and well described conversion mechanisms. So first, a starting original Fe-rich kaolinite recrystallized via solution into another particular 7-Å Fe-rich phase, the composition of which varies from a di-tri to a pure trioctahedral (Mg + Fe) end member.

This Fe-rich 1:1 mineral is effectively not a classical one. Then crystallization of a 10Å, rather dioctahedral K-rich phase occurs at the expense of it, through 1:½:1 interstratified structures. Such an evolution takes place through a solid state mechanism in which one 10-Å layer replaces one 7-Å layer. Another part of mica-like structures may also directly develop after dissolution of original kaolinites. The development of 10-Å K-rich phases could be significative of the beginning of the glauconitization process in these grains.

The Sinya Beds of the Amboseli Basin in Tanzania and Kenya consist largely of carbonate rocks and Mg-rich clays that are intensely deformed where exposed in and near former meerschaum mines. The carbonate rocks consist of limestone and dolomite in Tanzania, but only dolomite has been identified in Kenya. Sepiolite and mixed-layered kerolite/stevensite (Ke/St) are subordinate constituents of the carbonate rocks. The carbonate rocks and overlying bedded sepiolite were deposited in a semiarid lake basin at the foot of the large volcano Kilimanjaro. Calcite and dolomite of the carbonate rocks have δ18O values 4–6‰ lower than calcite and dolomite of the late Pleistocene Amboseli Clays, suggesting that the Sinya Beds were deposited in the middle or early Pleistocene under a different climatic regime when meteoric water had lower δ18O values than at present.

Mg-rich clay minerals form veins and fill cavities in the Sinya Beds. The principal clay minerals are sepiolite and Ke/St, some of which contains substantial Al and Fe (Al-Ke/St). NEWMOD® modeling and other X-ray diffraction (XRD) data suggest that most of the Ke/St contains 25–50 percent kerolite layers, but minor amounts of kerolite-rich Ke/St are present in some samples. Illite with an inferred high content of Fe or Mg is a minor constituent of the samples with Al-Ke/St. The cavity-filling clays were chemically precipitated, as shown by field relationships and SEM study. The early-deposited clays of veins and cavities are principally Ke/St with minor sepiolite, and the latest clay is sepiolite (meerschaum), generally with minor Ke/St.

The δ18O values of cavity-filling Ke/St range from 22.5–25.6‰ and correlate with mineral composition, with the highest values associated with the highest content of stevensite and the lowest values with the highest content of kerolite. This relation suggests that high salinities favored stevensite and low salinities favored kerolite. δ18O values of sepiolite (meerschaum) fall in the middle of the range for Ke/St, suggesting that salinity was not the main control on sepiolite precipitation. High values of $a_{Si{O}_2}/a_{M{g}^{2+}}$ may have been a major factor in sepiolite precipitation.

Different mixtures of dilute ground water and saline, alkaline lake water in pore fluids may largely account for the differences in clay mineralogy of cavity-filling clays. Sepiolite is the dominant clay mineral in lacustrine sediments of the Amboseli Basin, and the cavity-filling sepiolite may reflect a high proportion of lake water. The low-Al Ke/St may have formed from fluids with a higher proportion of ground water. Detrital clay was very likely a factor in forming the Al-Ke/St, for which δ18O values suggest a saline environment.

The fraction <20 μm of a bentonitic material was selected to study the transformation of smectite into illite under hydrothermal conditions. Powder XRD showed that the studied material was composed of 97% dioctahedral smectite and 3% of quartz, cristobalite and plagioclase. The XRD analysis of the oriented, glycolated sample showed that the smectitic phase was actually a randomly interstratified illite/smectite with 11% illite. The chemical analysis of the sample yielded the structural formula: K0.25Na0.25Ca0.12Mg0.13(Al2.76Fe0.33Mg1.03)(Si7.66Al0.34)O20(OH)4. The reaction conditions of the hydrothermal experiments were: KCl concentrations 0.025, 0.05, 0.1, 0.3, 0.5, 1 M; temperature 60, 120, 175, 200°C; run time 1, 5, 15, 30, 90, 180 days; solid: solution ratio 1:5. XRD of run products showed an important transformation of smectite into illite, in contrast with all other techniques (DTA, IR, NMR), which did not detect any transformation of the original material. This suggests that illite quantification in I/S by means of XRD patterns after hydrothermal experiences can be much affected by other variables. The original material and the run products were analysed by means of DTA. The starting material displayed two dehydroxylation peaks, one at 560°C corresponding to illite, and the other at 650°C corresponding to smectite. Quantification of the two dehydroxylation peaks also yielded a content of 11% illite. The run products displayed DTA diagrams in which the smectitic peak remained unaltered, but the illitic one was reduced or eliminated by the presence of exchangeable K in the interlayer. When exchangeable K was removed the illitic dehydroxylation peak appeared again. The coherence of XRD and DTA in quantifying the proportion of illite layers and the effect of exchangeable K on dehydroxylation of illite layers in mixed-layer illite/smectite seem to be positive proofs of the existence of polar layers.

The terms “hydrophobic” and “hydrophilic” are typically used in a non-specific sense and, as such, they have a limited utility. Surface thermodynamic theory, as described here, allows a natural and potentially powerful definition of these terms. The boundary between hydrophobicity and hydrophilicity occurs when the difference between the apolar attraction and the polar repulsion between molecules or particles of material (1) immersed in water (w) is equal to the cohesive polar attraction between the water molecules. Under these conditions, the interfacial free energy of interaction between particles of 1, immersed in water (ignoring electrostatic interactions), exactly zero. When is positive, the interaction of the material with water dominates and the surface of the material is hydrophilic; when is negative, the polar cohesive attraction between the water molecules dominates and the material is hydrophobic. Thus, the sign of defines the nature of the surface and the magnitude of may be used as the natural quantitative measure of the surface hydrophobicity or hydrophilicity.

SiO2 sols were made unstable by addition of Ca2+ ions. The resulting states of instability were classified as gelation, flocculation, and precipitation by means of observation, by checking the Tyndall effects on the supernatant or suspending solution, as appropriate, and by measuring the apparent densities of flocculated mass. The concentrations of free Ca2+ ions left in solution were measured by means of a Ca2+ ion selective electrode. The amounts sorbed onto SiO2 particles were then calculated by material balance. It was found that while the amount sorbed dictates the limit of stability, the SiO2 concentration in the mixture is an important factor deciding the state of instability. Depending on the SiO2 concentration, there were two distinct flocs with the apparent floc density of 6 ± 1 and 12 ± 1 mg SiO2/ml.

To obtain Cu-kaolinites with a controlled range of chemical compositions, syntheses were performed by hydrothermally ageing gels with kaolinite stoichiometric compositions. Gels were prepared with sodium metasilicate and nitrates of octahedral cations. Temperature of synthesis was 250°C with a corresponding equilibrium water pressure of 38 bars.

Three samples with copper contents ranging from 0.1 to 7% and another one with the chemical composition of the Cu end-member were synthesized. While this fourth sample led to tenorite after the hydrothermal treatment, the three others crystallized well into kaolinite.

Up to almost 1% CuO was measured by TEM in some isolated ‘clean’ and hexagonal kaolinite particles. EPR and XPS spectroscopies were consistent with an octahedral position of Cu2+. In IR spectra, vAl-OH-Cu absorption bands were not observed, but vAl2OH bands appeared more and more blurred when Cu content of samples increased. Weak bands situated at 868 cm−1 and 840 cm−1 are tentatively attributed to δAlCuOH. By differential thermal analysis, a downward shift of 20°C in temperature of the endothermic peak from the less Cu-rich sample to the most Cu-rich one, argued for the existence of some Al-OH-Cu bonds, whose binding energies are presumed to be less than the Al-OH-Al ones.

In view of these results, Cu2+ appears incorporated in the octahedral sheet of kaolinite. Moreover, this incorporation is made without major perturbation of the kaolinite structure.

The fine silt (2–5 μm) coarse clay (0.1–2 μm) and fine clay (<0.1 μm) fractions of a Vertisol from South Italy were studied with X-ray diffraction. The most reactive fine clay (<0.1 μm) fraction was investigated in detail using a curve decomposition method analysis of X-ray diffraction diagrams, FTIR spectroscopy and chemical analysis. In the soil parent material, the fine clay fraction was dominated by low-charge smectites (beidellite and montmorillonite) whereas, high-charge beidellite was the dominant clay mineral in the fine clay from the upper soil horizons. This suggested that high-charge beidellite was produced through alteration of the preexisting low-charge smectites and was the stable clay phase in this soil environment, characterized by high pH (>8.0). After K-saturation and 25 wetting and drying cycles, the high-charge beidellite from the soil horizons lost expandability far more than the original low-charge smectites.

Layered double hydroxides (LDH's) interlayered with silicate anions were prepared by reaction of tetraethylorthosilicate (TEOS) with synthetic meixnerite-like precursors of the type [Mg1−xAlx(OH)2][OH−]x·zH2O, where (1 − x)/x ≈ 2, 3, or 4. TEOS hydrolysis at ambient temperature occurred readily in the galleries of the hydroxide precursors with (1 − x)/x ≈ 3 or 4, but a temperature of ∼100°C was required to achieve silicate intercalation for the LDH composition with (1 − x)/x ≈ 2. On the basis of the observed gallery heights (∼7.0−∼7.2 Å) and 29Si MAS NMR spectra that indicated the presence of Q2, Q3, and Q4SiO4 sites, the intercalated silicate anions, which are formed by condensation reactions of silanol groups and partial neutralization of SiOH groups with gallery hydroxide ions, are assigned short chain structures. Also, some O3SiOH groups become grafted to the LDH layers by condensation with MOH groups on the gallery surfaces. The LDH-silicates exhibited comparable non-microporous N2 BET surface areas in the range 59–85 m2/g, but they differed substantially in acid/base reactivities, as judged by their relative activities for the catalytic dehydration/disproportionation of 2-methyl-3-butyn-2-ol (MBOH). Under reaction conditions where the LDH structure is retained (150°C), all the silicate intercalates showed mainly basic reactivities for the disproportionation of MBOH to acetone and acetylene. However, all the LDH silicates were less reactive than the corresponding LDH carbonates. Conversion of the LDH silicates to metal oxides at 450°C introduced acidic activity for MBOH dehydration, whereas the metal oxides formed by LDH carbonate decomposition were exclusivity basic under analogous conditions.