We report the structure and physical properties of two quasi-two-dimensional triangular antiferromagnetic materials, Co0.66Al2Se3.53 and Ni0.61Al2Se3.55, which show highly magnetically frustrated characters. Powder X-ray diffractions demonstrate that Co0.66Al2Se3.53 and Ni0.61Al2Se3.55 possess identical space group of P-3m1 with lattice parameters a = 3.8089(1) Å, c = 12.676(1) Å and a = 3.7880(1) Å, c = 12.650(1) Å, respectively. Analyzing the susceptibility data of Co0.66Al2Se3.53 reveal a Curie Weiss temperature of −216 K, and a spin-freezing transition temperature of 4.5 K, giving a frustration index f = −θcw/Tf ≈ 48. Ni0.61Al2Se3.55 possesses an effective moment of 2.38 µB, a Curie–Weiss temperature of −62 K with no sign of spin-freezing transition down to 2 K. The AC susceptibility data of Co0.66Al2Se3.53 suggest a spin glass-like transition, but no intersite mixing between Co2+ and Al3+ was observed from the X-ray photoelectron spectroscopy measurements.

Ga2−xFexO3 (GFO) bulks with x from 0.7 to 1.3 have been fabricated using the classic solid-state route. The structural, optical, and magnetic properties have been investigated systematically. X-ray diffraction spectra and FULLPROF profile fitting indicate that GFO bulks belong to the orthorhombic structure with the space group Pc21n. Phase separation appears at the Fe content of x = 1.3. The optical bandgap decreases almost linearly with the increase of iron content, which means that the bandgap of GFO bulks can be controlled by adjusting the Fe content in the samples. The magnetic property measurements suggest that GFO is ferromagnetic, and the magnetic properties are enhanced compared with other reported works, exhibiting the application in ferromagnetic semiconductors devices.

The National Institute of Standards and Technology (NIST) certifies a suite of Standard Reference Materials (SRMs) to address specific aspects of the performance of X-ray powder diffraction instruments. This report describes SRM 1879b, the third generation of this powder diffraction SRM. SRM 1879b is intended for use in the preparation of calibration standards for the quantitative analyses of cristobalite by X-ray powder diffraction in accordance with National Institute for Occupational Safety and Health (NIOSH) Analytical Method 7500, or equivalent. A unit of SRM 1879b consists of approximately 5 g of cristobalite powder bottled in an argon atmosphere. It is certified with respect to crystalline phase purity, or amorphous phase content, and lattice parameter. Neutron powder diffraction, both time-of-flight and constant wavelength, was used to certify the phase purity using SRM 676a as an internal standard. A NIST-built diffractometer, incorporating many advanced design features was used for certification measurements for lattice parameters.

Single-phase polycrystalline samples of RBa2Cu2.9Zn0.1Oy (R = Y, Nd, Gd, Er, and Tm) (ZnR123) were synthesized using the standard solid-state reaction method. They were characterized by X-ray powder diffraction (XRD) and scanning electron microscope. XRD shows that all samples consist essentially of a single phase and retain the orthorhombic structure. The structure of the samples was refined by the Rietveld method with the help of the bond valence sum method. The variation of the lattice parameters and some meaningful bond angles and lengths with the ionic radius are discussed. In these compounds, the variations of the buckling angles Cu2–O(2,3)–Cu2 and Cu2–Cu2–O(2,3) are unique: the bond angles Cu2–O3–Cu2 and Cu2–Cu2–O2 increase, whereas the bond angles Cu2–O2–Cu2 and Cu2–Cu2–O3 decrease. The variation of these bond angles brings about a strong curvature of the Cu2O plane. Furthermore, we have found tree fixed triangles formed by the Cu2, O2, and O3 atoms in addition to another fixed triangle O1–Ba–O1 observed for the first time. BVS of Cu2 atom shows a specific and unique variation compared with other compounds.

Polycrystalline samples of Ca2Zn2(V4O14) (I) and Pb2Cd2(V3O10)(VO4) (II) were synthesized using the nitrate–citrate method (I) and conventional solid state reaction (II). The structural refinement based on X-ray powder diffraction data showed that the crystal structure of (I) is characterized by monoclinic symmetry with unit-cell parameters a = 6.8044(1) Å, b = 14.4876(3) Å, c = 11.2367(2) Å, β = 99.647(1)° [space group P21/c (No. 14), Z = 4], and the crystal structure of (II) is triclinic with unit-cell parameters a = 7.03813(6) Å, b = 12.9085(1) Å, c = 6.99961(5) Å, α = 90.7265(5)°, β = 96.3789(5)°, γ = 94.9530(6)°, V = 629.470(8) Å3 [space group P$\bar 1$ (No. 2), Z = 2].

Thiazolidinones present a wide range of useful applications especially in the biological aspect. Based on these facts, the compound of interest 2-(α-naphthyl)-3-(α-pyridinyl)-1,3-thiazolidine-4-one (C18H14N2OS), was synthesized via multi-component reaction with the aim of obtaining a compound that would show activity against fungi and bacteria. The synthesis of 2-(α-naphthyl)-3-(α-pyridinyl)-1,3-thiazolidine-4-one, was carried out from the respective α-aminopyridine with α-naphthylaldehyde and α-mercaptoacetic acid, under reflux in dry toluene for 8 h, obtaining a solid compound. Molecular characterization of the compound was carried out by infrared spectrometry, mass spectrometry, and nuclear magnetic resonance. The study of the crystallization and the calculation of the unit-cell constants were determined by the technique of X-ray diffraction of polycrystalline samples. It was determined that the compound crystallizes in a monoclinic system with space group P21/c [No. 14] and the constants of the unit cell a = 11.958 (3), b = 9.675 (4), c = 12.661 (4) Å, β = 96.960° (2), V = 1454.01 (Å3).

The crystal structure of terazosin hydrochloride dihydrate has been solved and refined using synchrotron X-ray powder diffraction data, and optimized using density functional techniques. Terazosin hydrochloride dihydrate crystallizes in space group P-1 (#2) with a = 10.01402(4), b = 10.89995(4), c = 11.85357(4) Å, α = 89.5030(3), β = 71.8503(3), γ = 66.5632(2)°, V = 1118.143(8) Å3, and Z = 2. The terazosin cation occurs in an extended conformation. The crystal structure is dominated by hydrogen bonds. The most notable are the O–H···Cl from the water molecules to the chloride anion and N–H···Cl from the protonated ring nitrogen to the chloride. The amino group donates protons to each of the two water molecules. The powder pattern has been submitted to ICDD® for inclusion in the Powder Diffraction File™.

The crystal structure of the partially ordered vacancy compound Cu2In14/3□4/3Se8, belonging to the system I3-III7-□2-VI12, was analyzed using X-ray powder diffraction data. Several structural models were derived from the structure of the selenium-rich phase β-Cu0.39In1.2Se2 by permuting the cations in the available Wyckoff positions. The refinement of the best model by the Rietveld method in the tetragonal space group P$\overline 4 $ 2c (No 112), with unit-cell parameters a = 5.7487(3) Å, c = 11.5106(6) Å, V = 380.40(3) Å3, led to Rp = 9.0%, Rwp = 9.9%, Rexp = 7.2%, S = 1.4 for 134 independent reflections. This model has the following Wyckoff site atomic distribution: Cu in 2e (0,0,0); In in 2b (½,0,¼), 2d (0,½,¼), and 2f (½,½,0);□ in 2f (½,½,0); Se in 8n (x,y,z).

X-ray powder diffraction data, unit-cell parameters and space group for methoxmetamine (C14H20ClNO2) are reported [a = 6.5768(7) Å, b = 14.0830(10) Å, c = 15.0530(10) Å, β = 90.975(2)°, unit-cell volume V = 1394.0(2) Å3, and Z = 4, and space group P21/n]. All measured lines were indexed and are consistent with the P21/n space group. No detectable impurities were observed.

The crystal structures of Ca1.5Mn0.5V2O7 (I) and Ca1.5Cd0.5V2O7 (II) synthesized by the citrate method and by a conventional solid-state reaction, respectively, were determined using X-ray powder diffraction data. It was found that the compound I has a monoclinic crystal structure a = 4.88563(9) Å, b = 11.21279(22) Å, c = 5.69643(11 Å), β = 96.376(7)°, V = 310.132(10) Å3 (space group P21/c), Z = 2). Compound I has a narrow homogeneity region Ca1.5±0.1Mn0.5±0.1V2O7. The vanadate Ca1.5Cd0.5V2O7 crystallizes in the triclinic system with the parameters a = 6.66139(6) Å, b = 6.93019(7) Å, c = 7.02211(6) Å, α = 85.4404(9)°, β = 63.7505(7)°, γ = 82.5515(10)° и V = 288.201(5) Å3 (space group P$\bar 1$, Z = 2). It is one of the formulations of the primary solid solution, formed as a result of the substitution of part of the calcium cations for cadmium cations in Ca2V2O7.