The method of known additions for estimating clay-mineral content was reversed in that increasing proportions of soil clay were added to a standard composed of equal weights of kaolinite, illite, and montmorillonite. After glycolation, peak-area ratios were calculated from 7.2 (kaolinite), 10 (illite), 14 and 17 Å (vermiculite and montmorillonite) diffraction peaks of standard, mixes, and soil clay. Ratios were plotted against % soil clay from the standard (0%) through the mixes (14 to 77%). Curves of fit were calculated and projected to 100% soil clay giving theoretical values which agree with measured values. As weight proportions are known in the standard, the projections permit estimates of clay-mineral weight proportions in the soil clay.

The effects of NaOAc removal of carbonates, H2O2 removal of organic materials, and sodium citrate-bicarbonate-dithionite (SCBD) removal of iron oxides upon the X-ray powder diffraction (XRD) characteristics of clay minerals present within weathered volcanic ash deposits were examined. All pretreatments of samples derived from the Ae and Bhf horizons containing volcanic ash resulted in dramatic increases in XRD peak intensities, while the treatment of IIC-horizon samples resulted in subdued XRD peak intensities. Also, the chemical treatments produced an apparent increase in the amount of expandable clay minerals within the Ae horizon, due probably to the hydrolysis and removal of interlayer Al3+ when H2O2 and SCBD were used. Hence, poorly ordered and pedogenically modified vermiculite or vermiculite/montmorillonite interstratifications became “weathered” by H+ attack and Al3+ removal in a manner similar to the natural processes which take place in the acid and eluvial A horizon. In addition, possible XRD peak modification due to the dilution of crystalline clay concentrations by amorphous clay-size material appeared to be subordinate to the laboratory-induced chemical alteration of the weathered clay minerals.

To evaluate the importance of oxides to the surface chemistry of acid mineral soils, clay fractions were separated from a surface and subsurface horizon of an Inceptisol representative of many of the acid soils of the Southern Tier of New York state. Portions of the clays were treated to remove selectively noncrystalline and microcrystalline Fe and A1 oxides (acid ammonium oxalate extraction), total free iron oxides (dithionite reduction in buffered citrate solution), and organic matter (hypochlorite oxidation). Charge and ion-adsorption characteristics of the treated and untreated clays were investigated by means of Ca2+- and Cl−-exchange capacities, potentiometric titrations, and electrophoretic mobility (zeta potential) measurements of the CaCl2-treated clays.

Based upon surface area and anion- and cation-exchange measurements, the Fe and A1 oxides or oxideorganic matter complexes were found to contribute a large part of the surface area and pH-dependent charge of these clays. Oxide removal increased the cation-exchange capacity (CEC) and virtually eliminated the anion-exchange capacity (AEC) at pH 3 and 5.5 while shifting the positive zeta potential (ZPC) of the B-horizon clay toward negative values. Organic matter oxidation increased the AEC at pH 3 and the CEC at pH 5.5 and markedly shifted the ZPCs of both A- and B-horizon clays toward more positive values, probably by the removal of adsorbed organics from oxide surfaces. Estimates of the ZPCs of the clays varied among the three methods used, Ca2+- and Cl−-exchange capacities giving the lowest, and electrophoresis giving the highest values.

In a study of “rana” soils of central Spain, hydroxy-interlayered 2:1 clay minerals were identified in the upper horizons and high-charge smectite in the lower horizons, with kaolinite the most abundant phyllosilicate. The high-charge smectite showed a basal spacing of 18 Å on Mg-saturation and glycerol solvation and 10 Å on K-saturation and air-drying. It is concentrated in the coarse fractions and appears to be basically a beidellite in the fine-silt fractions and a montmorillonite in the clay fractions. Pre-existing illite was probably transformed into hydroxy-interlayered 2:1 clays in the surface horizons, whereas high-charge smectite formed in the deeper horizons. These minerals, which were apparently not stable in the existing soil conditions, were the first stage in the degradation process of illite. The stable mineral in these soil profiles was kaolinite.

Low-angle X-ray powder diffraction (XRD) measurements of soil samples, made at controlled relative humidities, showed the presence of major reflections at 20–33, 10–27, and 7–8 Å. The first reflection, which increased in intensity but did not shift in spacing with decreasing relative humidity, represents curved smectite layers. This spacing was also observed by high-resolution transmission electron microscopy. The value of 10–27 Å for the second reflection, the 001 reflection of smetite, is unusually high, probably due to poorly stacked, irregularly curved layers. The 7–8-Å reflection originates from kaolinite or dehydrated halloysite, which also contain curved layers. The more curved the layer structure of the smectite, the more difficult it is to detect this phase; therefore the XRD relative peak heights are not directly proportional to the percentages of the smectite.

The expandabilities of kaolin-group minerals in different horizons in 10 soils from New Zealand and Fiji were measured immediately after the application of formamide and after the sequential application of hydrazine, water, and glycerol (HWG treatment). The expandabilities of these minerals in some of the soil samples with dimethylsulphoxide (DMSO) and after long-term (4-day) formamide treatments were also measured. The abundance of characteristic halloysite shapes was determined from electron micrographs of selected samples. The expandabilities of several non-soil kaolinite samples with the DMSO and HWG treatments were also measured.

The expansion of kaolin-group minerals showed the same trends within almost all profiles, whether determined using formamide (by the immediate-formamide treatment) or glycerol (by the HWG treatment). Except where both treatments led to complete intercalation, the HWG treatment always caused more expansion of kaolin-group minerals than obtained immediately after formamide application. The HWG treatment expanded some non-soil kaolinite samples, but well-crystallized kaolinite was not affected by this treatment. The DMSO treatment expanded kaolin-group minerals in the soils to a similar extent as the HWG treatment and also expanded well-crystallized kaolinite. The degree of expansion resulting from the immediate-formamide treatment matched abundance of typical halloysite particle shapes more closely than the degree of expansion given by the other intercalation treatments. The degree of expansion immediately following formamide application could be diminished, if the samples were heated at 40 ± 5°C.

A method using Li saturation and heating to 250°C to differentiate montmorillonite from beidellite and nontronite has been developed. The test utilizes three washings with 3 M LiCl and two washings with 0.01 M LiCl in 90% methanol to prevent dispersion. An 'infinitely thick’ sample (6–8 mg/cm2) on a glass slide is used to avoid the effects of the reaction of a thin clay film with sodium of the slide when it is heated at 250°C. Solvation with glycerol rather than ethylene glycol is used, because all of the Li smectites studied expanded to some extent in ethylene glycol after the heating. The smectites included several montmorillonites, a nontronite, and saponites. The presence of interstratified montmorillonite and beidellite layers was clearly shown by the test for several smectite samples, including the so-called beidellites from Beidell, Colorado, and Chen-yuan, Taiwan, and several soil clays. The test thereby provides more mineralogical information than the often-used arbitrary dividing point between montmorillonite and beidellite at 50% tetrahedral charge. Heating the Li-saturated clays at 250°C caused substitution of 35 to 125 meq/100 g of nonexchangeable Li. These amounts exceeded the changes in cation-exchange capacity plus Li by 4 to 21 meq/100 g, except for the end-member beidellite from the Black Jack mine, Idaho. Fusion with LiNO3 at 300°C could not be used to differentiate between smectites instead of washing with LiCl solution and heating to 250°C, because fused montmorillonite subsequently expanded to 18 Å with glycerol. Large increases in nonexchangeable Li were caused by the fusion of smectites, a vermiculite, and two partially expanded micas.

K-Ar measurements were used in this study of upland Savannah River Site soils to distinguish between sorbed K and the K remaining in remnants of primary minerals. Study of sorbed K contributes to understanding further the interaction of alkali metals (Cs in particular) with the soils. Primary mineral K and the associated radiogenic Ar were studied to characterize soil mica with respect to its provenance and its relationship to hydroxy-interlayered vermiculite. K-Ar age values of Na-saturated clay fractions from five samples of these soils range in age from 270 to 370 Ma. After a moderate acid treatment (6% HNO3 v/v, ~1 mol dm-3, 3 h, 80°C) of the clay fractions, K-Ar age values (270-325 Ma) were little changed on the whole, but they were more closely grouped near 300 Ma. Earlier work had shown that most of the K in these soils is found in material resistant to moderate acid extraction. The K-Ar age values show that this acid-resistant material is much older than any pedogenic minerals could be, even much older than the sedimentary parent rocks from which the soils were derived. These observations support earlier inferences by others that the K in these well leached soils is largely in remnants of primary muscovite from the parent sediments. Age values near 300 Ma suggest that the muscovite is largely from proximal Piedmont terranes of the Appalachian orogen, where the K-Ar relationship in most micas was set by Alleghanian tectonic processes late in the Paleozoic Era. The structural location of the K within mica, shown by the retention of the associated radiogenic Ar, is in contrast to the sorption-dominated behavior of the Cs and most of the Rb in these soils during pedogenesis. Stronger acid treatment (~6 mol dm-3 HNO3, 3 h, 100°C) extracted substantial fractions of both the K and the radiogenic Ar from bulk-soil portions, indicating destruction of some of the primary mica. K-Ar age values for the sand-rich bulk soils were not useful for this study because the sand contains excess radiogenic Ar, probably in sand-sized vein quartz.