In this work, the synthesis of new hybrid material based on a poly (buthyl acrylate –co- vinyl formamide) copolymer using the emulsion polymerization and doped with Pd, is discussed. The copolymer structure was confirmed by FT-IR. Afterwards, Pd nanocrystals previously synthesized, resulting on a spherical shape of ~ 5 nm, as measured by High-resolution transmission electron microscopy (HR-TEM), were deposited on the structure of the organic material. The films were analyzed using AFM and Scanning electron microscopy (SEM), giving rise to a hybrid material that could be applied in areas such as nanolithography, catalysis, and sensors.

The effect of mesogenic organic salts as reinforcing fillers for natural rubber has been investigated. The influence of cation size (thallium and sodium) and organic chain length (thallium (I) pentanoate and dodecanoate) on the vulcanization parameters, physical and mechanical characteristics and rheological behavior has also been analyzed. In general, the maximum torque of the vulcanizates increases in the presence of the salts and is clearly manifested in a sensible increase in tensile modulus and strength of the composites. The reinforcing effect of these salts is noticeable in the natural rubber matrix. The thallium (I) salts are more effective reinforcements than the sodium salt, and the length of the organic chain hardly has any influence on the mechanical properties. The composites based on the thallium (I) dodecanoate salt show a very peculiar rheological behavior with a “plateau” in the G’ and G” vs temperature graphics which is related with solid phase I, existing between 83.5 ºC and 127 ºC, characterized as a plastic condis phase. This issue is especially interesting for the fabrication of devices such as sensors to control, for instance, the security (resistance of a material) as a function of temperature.

This work covers the design of stimuli-responsive membranes and their ever-expanding range of use. Stimuli-responsive membranes that change their physicochemical properties in response to changes in their environment were synthesized for biomedical application. Responsive cotton-g-[2-(dimethylamino) ethyl methacrylate] membranes were obtained using γ-rays by mutual irradiation (direct method). The effect of absorbed dose, dose rate, and monomer concentration on the grafting yield was determined. The grafted samples were verified by the FTIR-ATR, 1H and 13C HRMAS NMR and 13C CPMAS NMR spectroscopies; thermal properties were analyzed by TGA and DSC and the stimuli-responsive behavior was studied by DSC.

The main objective of this work was to control and manipulate tuneable equilibrium structures in elastomeric spherical particles. The cross-linked urethane/urea polymeric spheres with two soft segments, polypropylene oxide and polybutadiene, were prepared by reacting a poly(propyleneoxide)-based triisocyanate-terminated prepolymer (PU) with poly(butadienediol) (PBDO), with different weight ratio. Wrinkling on elastomeric Janus spheres is induced by UV irradiation (λ=254 nm) and permanently imprinted by swelling the particles in an appropriate solvent, followed by drying. The surface tailoring of the Janus elastomeric spheres, found by SEM, is dependent on the PU/PBDO ratio and on the elastic properties of the particles.

A brief summary about the research lines of our group is presented. The common factor in all the propositions is the fullerene in a chemical reactive role. The chemistry proposed is novel and can yield interesting results.

Theoretical calculations were performed on 2, 5-aromatic substituted pyrroles which have a nitro-benzene or a cyano-benzene link to the nitrogen atom of the pyrrol fragment. The molecules manifested interesting semiconductor behavior that was confirmed when thin films were prepared and their corresponding electrical characterization undertaken. The reason for this behavior is discussed, with reference to the electron withdrawing feature of the substituents in the benzene chain.