Copper oxynitride thin films with a minor oxygen content were prepared on silicon wafers at 100 °C by reactive magnetron sputtering using a gas mixture of nitrogen and oxygen. Addition of oxygen immediately improves the compactness of the deposits, which otherwise comprise ragged Cu3N nanocrystallites. With an oxygen content <10.0 at.%, the deposits reveal some sporadic Cu2O nanocrystals under transmission electron microscopy, but their x-ray diffraction (XRD) patterns exhibit reflections only from the Cu3N phase. The decomposition temperature, at which the sample after prolonged annealing shows Cu reflections on its XRD pattern, can be raised from 300 °C for stoichiometric Cu3N to 360 °C. The decomposition product after annealing at 450 °C is pure copper having an electrical resistivity of 8.94 × 10−8 Ω·m at room temperature, which can be taken as a good conductor and stands in strong contrast with the oxynitride matrix with an electrical resistivity of 6.87 × 10−2 Ω·m. These results constitute progress in the search of directly writable copper nitride-based materials.

Poly(methyl methacrylate) was contacted by a Berkovich indenter at a range of constant loading strain rates. This particular loading scheme was used to maintain the strain-rate-dependent elastic modulus and indentation hardness of the creeping solid constant throughout loading. A loading curve analysis method identical to that of Malzbender and de With but based on the elastic-perfectly plastic contact model of Hochstetter et al. [Tribol. Int.36, 973–985, 2003] was used to process the load-displacement curves. Using the analysis method together with the strain-rate-dependent elastic modulus of the creeping solid known a priori, the strain-rate-dependent hardness could then be predicted. The predicted hardness versus strain-rate relationship was compared with that evaluated from the observed topographic images of the residual impressions due to heavier indentations at three constant loading strain rates. Based on this comparison, the elastic-perfectly plastic contact model was shown to be applicable to the creeping solid only when deformation takes place at a quasi-static strain rate.

In this paper, we report the first successful fabrication of dense and optically transparent cadmium tungstate (CWO) films by sol-gel processing and the study of their optical and x-ray scintillation properties. A new sol-gel processing method was developed using tungstic acid and cadmium nitrate as precursors and hydrogen peroxide as solvent; homogeneous and stable CWO sols were aged at room temperature and used for the preparation of CWO films. A rapid sintering process was investigated and found to be necessary to make dense and optically transparent nanocrystalline CWO films. CWO films were uniform, fully dense, and crack-free, with CWO as the only detectable crystalline phase, as determined by x-ray diffraction. The thickness, density, grain size, and crystallinity of CWO films are all found to be strongly dependent on the sintering conditions and in turn impact the optical and x-ray scintillation properties. Sol-gel-derived dense CWO films demonstrated intense photoluminescence and x-ray excited optical luminescence intensity. The relationships between sol-gel processing, nanostructures, and optical and x-ray scintillation properties are discussed in detail.

Calcium phosphate coatings prepared using the technique of electron beam deposition were immersed in a simulated body fluid for different periods of time to determine their response in vitro. The amorphous as-deposited coatings dissolved completely after a few days of immersion. After annealing in air at 700 °C, the dissolution of a small amount of amorphous phase in the crystalline coatings promotes the precipitation of bonelike apatite on the recessed regions by increasing the local supersaturation of calcium and phosphate ions. Formation of apatite was confirmed by the x-ray diffraction peaks at (200), (211), and (203) planes which grew after immersion in simulated body fluid. Fourier transform infrared results conformed to this with the increase in intensity of the absorption band at 1450 cm−1, signifying the increase in carbonate content. Scanning electron microscopy results showed spherical-shaped apatite nucleated on dissolved surface after 8 days of immersion. Sixteen days after immersion, almost 80% of the surface area was covered with apatite formation and grew to coalesce between neighboring particles forming an integrated platelike layer after 28 days. No obvious detachment between the grown layer and the underlying coating was observed.

Based on the synthesis of a sufficient amount of AlN nanowires (AlN-NWs), AlN-NWs/Al composites with homogenously distributed AlN-NWs were fabricated. Microstructural observations reveal that the interface between AlN-NWs and Al matrix is clean and bonded well, and no interfacial reaction product was formed at the nanowire-matrix boundary. Mechanical properties including yield and tensile strength of the composites were improved with AlN-NWs volume fraction changing from 5 to 15 vol%, and the maximum yield and tensile strengths of the composite were about 6 and 5 times, respectively, as high as those of Al matrix. Meanwhile, AlN-NWs effectively decreased the coefficient of thermal expansion (CTE) of the composites, and the CTE of 15 vol% composite was about one half that of Al matrix. The results obtained suggest that AlN nanowire is a promising reinforcement for optimizing the mechanical and thermal properties of metal matrix composites.

We report atomic force microscope observations of small pits formed on thin poly(methyl methacrylate) films after exposure to formic acid vapor, which condenses to form small drops on the surface and then evaporates. This procedure produces large numbers of small pits, 50–5000 nm in diameter, with aspect ratios (depth-to-diameter) as high as 0.5. About 25% of the volume removed from high-aspect-ratio pits has been transported to form a raised ring around the rim of the pit. We attribute the remaining 75% of the volume loss to densification of the surrounding polymer. Nanoindentation measurements show that material inside the pits is harder and stiffer than material outside the pits, consistent with densification. The effects of solvent concentration, exposure time, and exposure to ammonia vapor are described. Similar treatments with volatile solvents have potential applications in large-scale surface patterning, submicron hole formation, and controlled alteration of surface properties.

Iron-based bulk metallic glasses (BMGs) are characterized by high fracture strengths and elastic moduli, with some exhibiting fracture strengths near 4 GPa, 2–3 times those of conventional high-strength steels. Among the Fe-based BMGs, the non-ferromagnetic ones, designated “non-ferromagnetic amorphous steel alloys” by two of the present authors [S.J. Poon et al.: Appl. Phys. Lett.83, 1131 (2003)], have glass-forming ability high enough to form single-phase glassy rods with diameters reaching 16 mm. Fe-based BMGs designed for structural applications must exhibit some plasticity under compression. However, the role of alloy composition on plastic and brittle failures in metallic glasses is largely unknown. In view of a recently observed correlation that exists between plasticity and Poisson’s ratio for BMGs, compositional effects on plasticity and elastic properties in amorphous steels were investigated. For the new amorphous steels, fracture strengths as high as 4.4 GPa and plastic strains reaching ∼0.8% were measured. Plastic failure instead of brittle failure was observed as the Poisson’s ratio approached 0.32 from below. Investigation of the relationship between the elastic moduli of the alloys and those of the alloying elements revealed that interatomic interactions in addition to the elastic moduli of the alloying elements must be considered in designing ductile Fe-based BMGs. The prospects for attaining high fracture toughness in Fe-based BMGs are discussed in this article.

We report on linear and nonlinear dielectric property measurements of BaTiO3–CoFe2O4 (BTO–CFO) ferroelectromagnetic nanocomposites and pure BaTiO3 and CoFe2O4 samples with scanning near-field microwave microscopy. The permitivity scanning image with spatial resolution on the micrometer scale shows that the nanocomposites have a very uniform quality with an effective dielectric constant ɛr = 140 ± 6.4 at 3.8 GHz and room temperature. The temperature dependence of dielectric permittivity shows that the Curie temperature of pure BTO was shifted by the clamping effect of the MgO substrate, whereas the Curie temperature shift of the BTO ferroelectric phase in BTO–CFO composites is less pronounced, and if it exists at all, would be mainly caused by the CFO. Nonlinear dielectric measurements of BTO–CFO show good ferroelectric properties from the BTO.

Replication of metallic high-aspect-ratio microscale structures (HARMS) by compression molding has been demonstrated recently. Molding replication of metallic HARMS can potentially lead to low-cost fabrication of a wide variety of metal-based microdevices. Understanding the mechanics of metal micromolding is critical for assessing the capabilities and limitations of this replication technique. This paper presents results of instrumented micromolding of Al. Measured molding response was rationalized with companion high-temperature tensile testing of Al using a simple mechanics model of the micromolding process. The present results suggest that resisting pressure on the mold insert during micromolding is governed primarily by the yield stress of the molded metal at the molding temperature and a frictional traction on the sides of the insert. The influence of strain rate is also considered.

The SrFeO3/SiO2/Si thin film system has been studied using transmission electron microscopy (TEM). The thin films of SrFeO3 were grown by pulsed laser deposition onto silicon substrates with a SiO2 buffer layer at room temperature (RT) and 700 °C and subjected to annealing for various periods of time at temperature T = 700 °C. Transmission electron microscopy characterization showed that the microstructure of the film deposited at room temperature contained crystalline and amorphous layers. Silicon diffusion into SrFeO3 films occurred at the SiO2 interface for the samples deposited at 700 °C and for those films annealed at 700 °C. The silicon diffusion-induced interfacial reactions resulted in the phase transformations and the growth of complex crystalline and amorphous phases. The principal compositions of these phases were Sr(Fe,Si)12O19, SrOx and amorphous [Sr-Fe-O-Si].

Single crystals of the perovskite solid solution (1 − x)Pb(Fe2/3W1/3)O3–xPbTiO3, with x = 0, 0.07, 0.27, and 0.75, have been synthesized by the high-temperature solution growth using PbO as flux and characterized by x-ray diffraction and dielectric and magnetic measurements. The crystal structure at room temperature changes from a pseudocubic to a tetragonal phase with the PbTiO3 (PT) content increasing to x ⩾ 0.27. As the amount of PT increases, the relaxor ferroelectric behavior of Pb(Fe2/3W1/3)O3 (PFW) is transformed toward a normal ferroelectric state with sharp and nondispersive peaks of dielectric permittivity at TC. Two types of magnetic orderings are observed on the temperature dependence of the magnetization in the crystals with x ⩽ 0.27. This behavior is explained based on the relationships among the magnetic ordering, perovskite structure, composition, and relaxor ferroelectric properties. Furthermore, the macroscopic magnetization of the system was measured under the application of a magnetic field, which demonstrates different magnetic behavior associated with the weakly ferromagnetic, antiferromagnetic, and paramagnetic ordering in the temperature range of 2 to 390 K. Interestingly, the low-temperature ferromagnetism is enhanced by the addition of ferroelectric PT up to x = 0.27.

The effects of Sr and B addition on the microstructure and mechanical properties of AZ91 alloy were studied. The results of this work show that a small amount of Sr addition to AZ91 refined the grain size. The highest tensile strength was obtained from the alloy with the optimal composition of 0.5% Sr and 0.09% B added, in which the average grain size was 42 μm. The tensile strength and elongation of the AZ91–0.5%Sr–0.09%B alloy were 151 MPa and 1.62%, respectively. Some needle-shaped Al4Sr particles distributed mainly at grain boundaries have been observed in the alloys with Sr and B additions. The fluidity is improved significantly, and the solidification range decreased by adding Sr and B. The liquidus of AZ91 alloy decreased markedly with the addition of Sr and B, but the solidus hardly changed. Therefore, the solidification range can be decreased, which will improve the die-casting properties.

Anthracene based nano/microstructures of different sizes and shapes like tubes/fibers are synthesized using a simple open air chemical vapor deposition technique. Thermal solid phase reaction between anthracene 9-carboxylic acid and calcium oxide reported recently [H. Liu et al., J. Am. Chem. Soc.125, 10794 (2003)] is used to obtain organic molecular nanostructures. The products of temperature (320 °C) induced reaction get deposited on the substrates placed inside the reaction chamber as well as on the inner walls in different nano/micrometer forms, tubes/rods/fibers and having different sizes. Structural characterization of the reaction products is performed using optical microscopy, field emission electron microscopy (FE-SEM) and transmission electron microscopy (TEM). Chemical composition studies are conducted using infrared (IR), nuclear magnetic resonance (NMR), and gas chromatography (GC)-Mass spectroscopy, as well as elemental analysis. IR studies of the nanostructures obtained on the substrate using IR spectroscopy reveal the presence of C=O groups, the confirmatory evidence of which is obtained using energy dispersive x-ray spectroscopic (EDS) analysis. Interaction study of the C=O groups with ammonia vapor is conducted and resulting changes are monitored using Fourier transform infrared (FTIR). A strong covalent modification of anthracene based structures by exposure to ammonia molecules is indicated.

The influence of annealing on the structural changes and the mechanical properties of Zr41.2Ti13.8Cu12.5Ni10Be22.5 (Vit-1) bulk metallic glass was systematically studied by varying the annealing times at 703 K. The evolution of the structural state at a relatively high temperature within the supercooled liquid region was studied by thermal analysis, x-ray diffraction, high-resolution transmission electron microscopy, extended x-ray absorption fine structure, and dilatometric measurements. The deformation behavior and the mechanical properties were also examined by carrying out hardness and compression tests for the specimens annealed for various times.

Raw and partially infiltrated carbon–carbon composite preforms have been scanned by high-resolution synchrotron radiation x-ray computerized microtomography. Three-dimensional high-quality images of the pore space have been produced at two distinct resolutions and have been used for the computation of transport properties: heat conductivity, binary gas diffusivities, Knudsen diffusivities, and viscous flow permeabilities. The computation procedures are based on a double change-of-scale strategy suited to the bimodal nature of pore space and on the local determination of transport anisotropy. Good agreement has been found between all calculated quantities and experimental data.

The present investigation reports for the first time a dramatic decrease in the sintering temperature of elemental W from the conventional temperature of ≥2500 °C to the modest temperature range of 1700–1790 °C by making the W powder nanostructured through high-energy mechanical milling (MM) prior to sintering. The crystallite size of the initial W powder charge with a particle size of 3–4 μm could be brought down to 8 nm by MM for 5 h in WC grinding media. Further milling resulted in a high level of WC contamination, which apparently was due to work hardening and the grain refinement of W. A sintered density as high as 97.4% was achieved by sintering cold, isostatically pressed nanocrystalline (8 nm) W powder at 1790 °C for 900 min. The microstructure of the sintered rods showed the presence of deformation bands, but no cracks, within a large number of W grains. The mechanical properties, when compared with the hardness and elastic modulus, of the sintered nano-W specimen were somewhat superior to those reported for the conventional sintered W.

Cu, Pt, Ag, and Au were deposited on (100)-oriented ceramic substrates (SrTiO3, LaAlO3, and MgO). Over a wide range of temperatures (room temperature to 600 °C), Cu films were (100)-oriented and exhibited cube-on-cube epitaxy. Epitaxial Pt(100) films were obtained only at high temperature; oriented Pt(111) films were obtained at lower temperatures. Ag and Au were never obtained as purely (100)-oriented samples, although the amount of (100)-film increased with increasing temperature. Three-dimensional islands formed for all metals at higher temperatures, while flatter film surfaces developed at lower temperatures. At any given temperature, the surface roughness of films on SrTiO3(100) increased in the order Pt < Cu < Au < Ag. The variations in film structural characteristics are described well by considering the metals’ (i) surface/interfacial energies, (ii) surface energy anisotropies, and (iii) surface diffusion coefficients. Flat, epitaxial growth is promoted by low-energy interfaces, low surface energy anisotropies, and slow surface diffusion.

To explore the mechanism of grain growth, gas phase synthesized nanopowders of Al2O3 were heated in ambient conditions at elevated temperatures. Transmission electron microscopy and x-ray line broadening studies were performed to determine the microstructural parameters like crystallite size and root-mean-square (rms) strain. Increase in crystallite size with a decrease in dislocation density was observed for annealing the powder at higher temperatures. From a detailed analysis of the dislocation interactions, it was shown that polygonization like interaction of dislocations is the primary cause for such growth. A model for such growth is proposed. From the measured values of the rms strain and crystallite size at different temperatures, the ratio of the bulk to the shear modulus was determined. The measured ratio was found, within experimental uncertainties, to be close to the bulk value.

A novel multiferroic thin-film heterostructure exhibiting both ferromagnetic (FM) and ferroelectric (FE) properties, as well as magneto-optic (MO) and electro-optic (EO) properties, was fabricated via a wet chemical route. Oxide buffer layers were used to allow the growth of ferroelectric lanthanum modified lead magnesium niobate titanate (La:PMNT) layer on top of ferromagnetic bismuth and aluminum substituted yttrium iron garnet (BiAl:YIG). X-ray diffractometer (XRD) analysis confirmed the formation of both crystalline structures. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to examine the surface and cross-section morphologies of the resulted heterostructure. Multiferroic properties of the film were investigated.

Cylindrical Cu42.5Ti41.5Ni7.5Zr2.5Hf5Si1 bulk metallic glass with a diameter of 2 mm was fabricated by copper-mold casting. X-ray diffraction and differential scanning calorimetry analysis of the material showed that the alloy has a homogenous amorphous structure and high glass-forming ability. However, detailed observation by transmission electron microscopy revealed that a kind of nanocrystal with size of about 20 nm is sparsely distributed in the glass matrix. Nanobeam electron diffraction experiments indicated that the nanocrystal has a face-centered cubic crystalline structure. Room-temperature compression tests revealed that the alloy has a high fracture strength of 2250 MPa and obvious plastic strain of about 5.3%. Nanoindentation tests revealed that the as-cast alloy exhibits obviously serrated flow over a wide range of loading rate from 0.5 to 10 mN/min.