The strong interactions between Mg and Ni/NiH4 are attributed to harsh operating conditions and difficulties for H2 release, restricting the practical applications of the Mg-based hydrides. In this study, a new method of interstitial nonmetals co-doping was proposed to reduce the strong interactions. The calculation results showed that the method of interstitial nonmetals co-doping causes a more significant reduction in the thermal stability of Mg-based hydrides, as compared with the methods of either single transition metal or nonmetal doping. To determine the influence mechanism, a theoretical study was conducted based on the first-principles calculations. The computations demonstrated that the criss-cross action between B–Ni and N–Mg bonds weakens the bonding effects between Mg and Ni/NiH4. Besides, the mutual interactions between nonmetals and H atoms could weaken Ni–H bonding effects and stimulate the breaking of stable NiH4 clusters, thereby facilitating the release of H2 from the hydride.

Highly ordered wrinkling morphologies of liquid crystalline polymer films are demonstrated based on simple multi-rubbing. The spontaneous pattern formation of periodic wrinkling morphology is achieved through utilizing plasma treatment on a predefined alignment layer. The multi-directional ordering on the alignment layer obtained through selectively covering the alignment layer with a protective layer, which is chemically inert and keeps alignment properties during another rubbing process. The ordering of the wrinkle pattern can be tailored through a molecular orientation of liquid crystal (LC) and a process condition, including film thickness, plasma treatment, and rubbing. The proposed methods enable the spontaneous pattern formation of well-aligned one- or two-dimensionally periodic microstructures over a large area, without an additional template or patterning steps. Since the LC polymer incorporated the optical anisotropic mesogenic groups into polymer chains, it has an optical birefringence in the film and it can be utilized for optical devices requiring a microstructure on a surface.

Biodegradable poly(lactide acid) (PLA) has been well-studied as a shape memory polymer in recent years, but the brittleness and relatively high Tg limit its applications. In this study, a series of PLA/poly(ethylene glycol) (PEG) blends were manufactured by using the solvent evaporation method. The thermal behaviors, morphology, hydrophilicity, and mechanical properties of the samples with different contents of PEG have been experimentally studied by differential scanning calorimetry, scanning electronic microscopy, water contact angle, dynamic mechanical analysis, and tensile test. Furthermore, the influence of PEG on the shape memory properties under different loading conditions including the stretch strain, recovery temperature, deformation temperature, and tensile rate were explored systematically. Experimental results reveal that introduction of appropriate contents of the plasticizer PEG into the PLA/PEG systems results in the significant improvement of morphology, hydrophilicity, and mechanical properties while the high shape memory properties are still retained.

Among various methods used for the reduction of graphene oxide (GO) into a purer form of graphene, the thermal reduction method provides a simpler, safer, and economic alternative, compared to other techniques. Thermal reduction of GO causes significant weight loss and volume expansion of the material. Current work investigates the onset temperature where reduction in terms of exfoliation takes place, which is determined to be 325 °C at standard atmospheric pressure. Reduction temperature plays the most crucial role as it controls the quality of reduced graphene oxide in terms of weight percentage of carbon and lattice defect. The study leads to achieving highest content with a minimum defect in the graphene lattice at the optimum temperature, which is found to be 350 °C at standard atmospheric pressure. The thermal reduction process has been analyzed with the help of Fourier transform infrared spectroscopy, thermogravimetric analysis, and thermal degradation kinetics. From thermal degradation kinetics of GO, the rate of reaction has been found to be independent of concentration and is a sole function of temperature.

Magnesium is a biodegradable material that has potential application in cardiovascular stent development: its excellent mechanical properties and blood compatibility make it highly useful in interventional therapy. Nevertheless, the following shortcomings restrict its further application: antihyperplasia function and promoting surface endothelialization. In this study, we immobilized a specific link peptide of endothelial cells, Arg-Glu-Asp-Val (REDV), onto polydopamine (PDA)-deposited Mg–Zn–Y–Nd alloy surface via covalent reaction to improve the growth of the endothelial cells. The PDA/REDV coating with optimized parameters maintained the good blood compatibility of the Mg–Zn–Y–Nd alloy at the biomimetic speed of the blood flow and significantly inhibited the growth of the vascular smooth muscle cells and macrophage attachment/activation, which indicated its better functions in antihyperplasia and anti-inflammation. In particular, the PDA/REDV coating not only showed consistent results in promoting the attachment of endothelial cells as reported elsewhere, but also displayed the ability of enhancing the viability of endothelial cells (or inhibiting apoptosis), suggesting its pro-endothelialized function through different pathways. In summary, this PDA/REDV coating addressed the above-mentioned shortcomings of the magnesium alloy, which may promise its wider application.