Fe2+-catalyzed transformation of poorly crystalline ferrihydrite into highly crystalline forms is critical in the biogeochemical cycles of Fe, nutrients, and trace elements. The co-existence of ferrihydrite and kaolinite is widespread in soils of tropical and subtropical regions. In this investigation, three associations of ferrihydrite–kaolinite with ratios of 10, 30, and 50% (10% Fhy–Kln, 30% Fhy–Kln, and 50% Fhy–Kln) were examined to study the impact of the initial Fe2+ concentration and pH on Fe2+-catalyzed transformation under anoxic conditions. The findings reveal that the ferrihydrite in the 10% Fhy–Kln associations has the smallest particle size and the largest number of surface hydroxyl groups. At 0.5 mM Fe2+ and pH 7.5, ferrihydrite underwent transformation into lepidocrocite, with the presence of kaolinite promoting the formation of goethite. Moreover, the presence of kaolinite influenced the morphology of the resulting transformation products. A decrease in pH hindered the transformation of ferrihydrite, while an increase in Fe2+ concentration resulted in the formation of magnetite. The impact of kaolinite in the association system on the transformations of ferrihydrite occurs primarily through alteration of the properties of ferrihydrite during its formation process.

Aluminum-substituted hematites (Fe2−xAlxO3) were synthesized from Fe-Al coprecipitates at pH 5.5, 7.0, and in 10−1, 10−2, and 10−2 M KOH at 70°C. As little as 1 mole % Al suppressed goethite completely at pH 7 whereas in KOH higher Al concentrations were necessary. Al substitution as determined chemically and by XRD line shift was related to Al addition up to a maximum of 16–17 mole %. The relationship between the crystallographic a0 parameter and Al substitution deviated from the Vegard rule. At low substitution crystallinity of the hematites was improved whereas higher substitution impeded crystal growth in the crystallographic z-direction as indicated by differential XRD line broadening. At still higher Al addition crystal growth was strongly retarded. The initial Al-Fe coprecipitate behaved differently from a mechanical mixture of the respective “hydroxides” and was, therefore, considered an aluminous ferrihydrite.

Ferrihydrite was transformed to goethite and/or hematite at various temperatures, [OH], and [Al]. Increasing temperature and [Al] favored hematite, increasing [OH] favored goethite. A given [Al] induces hematite more effectively at lower [OH]. Al substitution in goethites increased linearly with log[Al], but was independent of temperature. At a given [Al], substitution increased with decreasing [OH]. In a plot of Al/Fe in the goethite against [Al]/[Fe(OH)4−] in solution a straight line was obtained for all preparations independent of [OH].

Hydroxy-carboxylic acids inhibit the crystallization of ferrihydrite in the pH range 9–11 in the order

citric > meso tartaric > L-tartaric ≫ lactic

and favor hematite formation relative to goethite in the order

L-tartaric > citric > meso tartaric > lactic.

The crystal shape of hematite can change from hexagonal plates to acicular in the presence of these acids. The influence of the acids on the crystallization rises with increasing concentration and with falling pH.

The effectiveness in suppressing crystallization depends on whether and how strongly the acid adsorbs on ferrihydrite and how strongly it complexes with Fe3+ in solution. Inhibition of crystallization of hematite is believed to be due to the di- and tricarboxylic acid linking ferrihydrite particles in an immobile network. Goethite formation is suppressed by the acid complexing with Fe in solution and hindering nucleation; strongly adsorbing acids also adsorb on the nuclei and hinder further growth. Certain acids can induce hematite formation because they contain a group which acts as a template for nucleation of hematite.

The influence of Al on the products formed by aerial oxidation at pH 5.5-7 and 20°C of Fe(II) chloride, sulfate and carbonate solutions, was examined. In all cases Al at levels Al/Al + Fe = 0.09−0.30 inhibited the formation of y phases (lepidocrocite and maghemite) in favor of goethite under conditions where, in the absence of Al, these y phases formed. The influence of Al in these laboratory studies was supported by field observations.

At higher levels of Al, ferrihydrite formation was favored. This effect of Al was seen to be the result of a slowing down in the hydrolysis/oxidation rate of the Fe(II) system.

The presence of Al not only changed the direction of mineral formation, but also caused the formation of Al substitued goethites which resembled in particle size and morphology the natural aluminiferous goethite extracted from a soil.

Adsorption of p-hydroxybenzoate anion on synthetic Fe oxides, hydroxides, and oxyhydroxides (hereafter referred to as oxides) was measured at pH 5.5, and the organic-oxide interaction was characterized using diffuse-reflectance Fourier-transform infrared (DRIFT) spectroscopy. Surface complexes with ferrihydrite, hematite, goethite, and noncrystalline Fe oxide were investigated. Infrared (IR) spectra of the oxides after separation from p-hydroxybenzoate solutions showed the organic to be coordinated by an inner-sphere mechanism to the oxide surface through the carboxylate group. Bidentate binding of the carboxylate was identified to be the dominant type of complexation on the oxides. Although the IR study suggested that goethite formed the strongest surface iron-carboxylate bond, the total amount of organic adsorbed was the least on this oxide. This result suggested that bond energy was less important than adsorption site density in determining the amount of organic anion adsorption. Increasing ionic strength had little effect on adsorption by the noncrystalline Fe oxide, but dramatically decreased adsorption on hematite and goethite. This difference might have been due to anion competition for binding sites. At pH 5.5, the amount of organic adsorbed per unit weight of oxides (in 0.05 M NaClO4) followed the order: ferrihydrite > noncrystalline Fe oxide > hematite ≫ goethite. Adsorption per unit of surface area however, followed the order: ferrihydrite > hematite > noncrystalline Fe oxide ≫ goethite. The hematite adsorption reaction appeared to be driven by entropy, inasmuch as the reaction was endothermic. The difference among the oxides in surface reactivity toward p-hydroxybenzoate is hypothesized to have been caused by differences in both quantity and structural arrangement of reactive sites on the oxide surface.

The transformation of ferrihydrite to goethite and/or hematite, as influenced by the presence of co-precipitated Si, was investigated by infrared spectroscopy (IR), X-ray powder diffraction (XRD), and transmission electron microscopy (TEM). Ferrihydrite samples having Si/Fe molar ratios ranging from 0 to 1 were synthesized by reacting Fe2(SO4)3 with NaOH to an equilibrium pH of 8.2 in the presence of Na2SiO3. The XRD pattern of the Si-free sample contained five distinct but weak peaks, whereas the patterns of ferrihydrite samples containing Si had only two broad bands. With an increase of the Si/Fe molar ratio from 0.10 to 1.0, the 2.54-Å XRD peak shifted to 2.97 Å, and broad IR bands were observed at 990 cm−1 (Si-O stretching region) and 450 cm−1 (silicate bending region). The intensities of both IR bands increased with increasing Si/Fe molar ratio.

Ferrihydrite samples were incubated at room temperature in sodium acetate/acetic acid buffer solutions at pH 3, 5, 7, and 10 and in CaCO3 suspension at pH 8.3 for 10 months. Additional samples were incubated at pH 12.5 at 24°, 40°, 60°, and 91°C for 36 hr. Room-temperature incubation of ferrihydrite samples having Si/Fe molar ratios ≥0.1 at pH 3 for one week resulted in the dissolution of Fe and the precipitation of silica gel. Ferrihydrite samples having Si/Fe molar ratios ≤0.05 transformed to poorly crystalline goethite during room-temperature incubation at pH 5. The rate of transformation and the degree of crystallinity of the product were inversely related to Si/Fe molar ratio, and, with heat treatment, were also dependent on incubation temperature. Siliceous ferrihydrite samples having Si/Fe molar ratios ≥0.10 did not transform to phases having greater crystallinity during incubation at either room temperature in buffered solutions at pH ≥7 for as long as 10 months or at pH 12.5 at 91°C for 36 hr. The XRD peak at 2.97 Å did not shift significantly during incubation procedures, providing evidence that the structure of the high-Si ferrihydrite was not significantly altered.

A series of synthetic goethites containing varying amounts of Si and P dopants were characterized by X-ray powder diffraction, electron diffraction, microbeam electron diffraction, and Mössbauer spectroscopy. Very low level incorporation produced materials having structural and spectral properties similar to those of poorly crystalline synthetic or natural goethite. At higher incorporation levels, mixtures of noncrystalline materials were obtained which exhibited Mössbauer spectra typical of noncrystalline materials mixed with a superparamagnetic component. Microbeam electron diffraction indicated that these mixtures contained poorly crystalline goethite, poorly crystalline ferrihydrite, and a noncrystalline component. If the material was prepared with no aging of the alkaline Fe3+ solution before the addition of Na2HPO4 or Na2SiO3, materials were obtained containing little if any superparamagnetic component. If the alkaline Fe3+ solution was aged for 48 hr before the addition, goethite nuclei formed and apparently promoted the precipitation of a superparamagnetic phase. The Mössbauer-effect hyperfme parameters and the saturation internal-hyperfine field obtained at 4.2 K were typical of those of goethite; however, the Mössbauer spectra indicated that the ordering temperature, as reflected in the relaxation rate and/or the blocking temperature, decreased with increasing incorporation of Si and P. The complete loss of crystallinity indicates that Si and P did not substitute for Fe, but rather adsorbed on crystal-growth sites, thereby preventing uniform crystal growth.

In alkaline media and at 70°C dilute suspensions of ferrihydrite transformed to goethite between pH 11.2 and 14 and to a mixture of goethite and hematite above and below this pH range. Increasing the temperature of the transformation or the concentration of the suspension reduced the pH range in which goethite alone formed. The morphology of goethite was chiefly a function of the pH of the system. Acicular crystals formed at all pHs and exclusively above pH 12.2. Epitaxial twinned crystals predominated at pHs below 11, and twins free from hematite formed at higher pHs. Increasing the suspension concentration, ionic strength, or temperature extended the pH range over which twinned crystals formed. Electron micrographs showed that twins formed mainly during the initial stage of the transformation, whereas acicular crystals formed over a longer period. Thus, the twins appeared to nucleate in the ferrihydrite; nucleation of acicular particles took place in solution.

Ferrihydrite prepared in different manners was kept under relative humidities ranging from 75 to 100% and at temperatures of 45° and 55°C for 180 days. Ferrihydrite transformed to hematite and goethite at relative humidities close to 100%, but at lower relative humidities the transformation was less pronounced and hematite was highly favored over goethite. Increasing temperature also favored hematite over goethite, and Al substitution completely prevented goethite formation. These results suggest that hematite can form in relatively dry, warm soils or sediments, although more slowly than in moister environments.

The kinetics of hydroquinone oxidation by aqueous suspensions of pure hematite and goethite-ferrihydrite mixtures at pH 6.0, 7.4, and 9 was studied using an on-line analysis system. The electron transfer between hydroquinone and the Fe oxides was monitored by UV-visible and electron spin resonance spectroscopy. The adsorption of organics on the Fe oxide surface was detected by Fourier-transform infrared spectroscopy. For different Fe oxides, a higher surface area was correlated with a greater oxidizing ability and greater adsorption of organics, suggesting that the oxidation reaction was a surface process. A reversal of the initially rapid redox reaction was found in this system, suggesting a delayed release of Fe2+ into solution as the reduction of the Fe oxide proceeded. Redox potential calculations confirmed the thermodynamic favorability of the reaction reversal. A distribution of the reduced state over neighboring Fe atoms on the oxide surface probably was responsible for the initial suppression of Fe2+ release into the aqueous phase. Based upon these observations and detection of the semiquinone radical as an intermediate of hydroquinone oxidation, an inner-sphere one-electron transfer mechanism for the oxidation of hydroquinone at the oxide surface is proposed.

An ochreous precipitate isolated from a stream receiving acid-sulfate mine drainage was found to consist primarily of goethite and lesser amounts of ferrihydrite-like materials. The Fe-oxide fraction, including goethite, was almost totally soluble in acid ammonium oxalate. Similar materials were produced in the laboratory by hydrolysis of ferric nitrate solutions containing 250 to 2000 μg/ml sulfate as Na2SO4. Initial precipitates of natrojarosite transformed to Fe-oxides upon aging for 30 days at pH 6.0. The proportion of goethite in the final products decreased with increasing sulfate (SO4/Fe = 0.2 to 1.8) in the initial hydrolysis solutions; only ferrihydrite-like materials were produced at SO4/Fe ratios > 1.5. Variations in SO4/Fe solution ratios also produced systematic changes in the color (10R to 7.5YR) and surface areas (49 to 310 m2/g) of the dried precipitates, even though total S contents were relatively constant at 2.5 to 4.0%.

To provide a greater understanding of the crystallization of iron oxides under natural aqueous conditions, the combined effect of an inorganic ion (Mn2+) and a reducing organic ligand (L-cysteine) on the conversion of noncrystalline ferric hydroxide to goethite and/or hematite was investigated at pH 8.

At cysteine: Fe ratios ≥ 0.2, L-cysteine caused noncrystalline iron(III) hydroxide to transform rapidly into goethite at pH 8; in the absence of the organic ligand, hematite was the predominant reaction product. The presence of Mn (≥9 mole %) in the cysteine-ferric hydroxide system retarded crystallization and reduced the goethite-promoting effect of cysteine.

Polarographic measurements showed that the adsorption of cysteine on noncrystalline iron(III) hydroxide was immediately followed by the oxidation of cysteine to the disulfide with simultaneous reduction of a proportion of the interracial ferric ions. The partly reduced noncrystalline iron(III) hydroxide dissolved at pH 8 more rapidly than the original material, thus facilitating the formation of goethite. In Mn(II)-noncrystalline iron(III) hydroxide coprecipitates, the interfacial oxidation/reduction reaction with cysteine (and hence the partial reduction of the noncrystalline phase) was reduced, due to replacement of some interfacial Fe(III) by non-reducible Mn.

At pH 8, uptake of Mn by crystalline iron oxides was low (< 5 mole %). Mn precipitated preferentially as pure Mn phases, either rhodochrosite (in NaHCO3 buffer) or hausmannite (in NH4Cl/NH3 buffer).

Fifteen iron oxide accumulations from the bottoms of two Finnish lakes (“lake ores”) were found to contain as much as 50% Fe. Differential X-ray powder diffraction and selective dissolution by oxalate showed that the samples consisted of poorly crystallized goethite and ferrihydrite. The crust ores of one lake had higher ferrihydrite to goethite ratios than the nodular ores of the other lake. The higher ferrihydrite proportion was attributed to a higher rate of Fe2+ supply from the ground water and/or a higher rate of oxidation as a function of water depth and bottom-sediment permeability.

Values of Al-for-Fe substitution of the goethites determined from unit-cell dimensions agreed with those obtained from chemical extraction if the unit-cell volume rather than the c dimension was used. In very small goethite crystals a slight expansion of the a unit-cell dimension is probaby compensated by a corresponding contraction of the c dimension, so that a contraction of the c dimension need not necessarily be caused by Al substitution.

The goethites of the two lakes differed significantly in their Al-for-Fe substitutions and hence in their unit-cell sizes, OH-bending characteristics, dehydroxylation temperatures, dissolution kinetics, and Möss-bauer parameters. The difference in Al substitution (0 vs. 7 mole %) is attributed to the Al-supplying power of the bottom sediments: the silty-clayey sediments in one lake appear to have supplied Al during goethite formation, whereas the gravelly-sandy sediments in the other lake did not. The compositions of the goethites thus reflect their environments of formation.

Ferrihydrite samples having Si/Fe molar ratios ranging from 0 to 1 were synthesized by the reaction of Fe2(SO4)3 and Na2SiO3 with NaOH to an equilibrium pH of 8.2. Hematite formed by incubating the ferrihydrite (Si/Fe molar ratios ≤0.05) at pH 12.5 and 91°C for 36 hr had a globular morphology. Hematite formed from Si-free ferrihydrite gave infrared (IR) bands at 548, 471, 397, and 337 cm−1, whereas, hematite formed from Si-containing ferrihydrite having 0.001 to 0.05 Si/Fe molar ratios gave broad IR bands at about 550, 450, and 330 cm−1. Ferrihydrite having Si/Fe molar ratios ≥0.10 did not transform to hematite following the aqueous-thermal treatment.

The ferrihydrite samples were thermally treated for 2 hr at consecutive 100°C intervals from 100° to 800°C. The Si-free ferrihydrite transformed at 300°C to poorly crystalline hematite. Transmission electron microscopic analyses indicated that the hematite consisted of aggregates of spheroidal particles of 20–80 Å cross sections. Broad IR bands were observed at 529 and 452 cm−1; however, after heating the sample to 800°C, the particle cross sections increased to about 150–600 Å, and additional IR bands were present at 378 and 325 cm−1. The differences in the IR patterns of hematite formed from ferrihydrite at 300° and 800°C were probably due to increases in particle size and aggregation and improved crystallinity of the hematite particles following the higher temperature treatment. The hematite formed by the thermal transformation of the ferrihydrite having a 0.01 Si/Fe molar ratio was also spheroidal, and IR vibrations were present at about 528 and 443 cm−1. An increase in the temperature of the thermal treatment, however, did not result in additional IR bands.

Differences in the IR vibrations of hematite formed during aqueous- and dry-thermal treatments of the ferrihydrite samples were probably due to differences in the particle size and morphology of the product. The Si content, due to its effect on particle size of the precursor and the prevention of sintering and particle growth of hematite, influenced the IR pattern of the product. Particle morphology and IR spectroscopy may therefore be useful indicators of the precursor of hematite and the conditions of hematite formation in soil.

The transformation of ferrihydrite to goethite and/or hematite in alkaline media is strongly retarded by the presence of silicate species. These species probably stabilize ferrihydrite by adsorbing on the particles of ferrihydrite and linking them into an immobile network.

At concentrations low enough for the transformation to proceed, silicate species promote the formation of hematite and hinder the nucleation of goethite. The presence of silicate species modifies the morphology of both reaction products. Hematite forms ellipsoidal single crystals, commonly displaying outgrowths of goethite. Silicate species in solution appear to enhance the development of the (021) faces of goethite, probably by preferential adsorption on these faces; at high levels of silicate species, goethite crystals adopt a pseudohexagonal habit. This morphology has not been observed previously for goethite.

The transformation of ferrihydrite to goethite and hematite in the pH range 9–13 is retarded by the presence of simple sugars (>- 10-4 M concentration). The retarding effect is related to the extent of adsorption of the sugar on ferrihydrite. Maltose and glucose adsorb strongly and inhibit the transformation by preventing both aggregation and dissolution of the ferrihydrite. Sucrose adsorbs to a much lesser extent than the other sugars and appears to hinder the nucleation and growth of goethite in solution.

Hematite formation relative to that of goethite is favored by the sugars in the order: maltose >glucose ≫ sucrose. Maltose and glucose cause hematite to grow as prismatic crystals rather than as hexagonal plates and also lead to a new type of twinned goethite; one with epitaxial outgrowths of goethite on a prismatic crystal of hematite. In alkaline media glucose and maltose are partly transformed into a mixture of different sugars and hydroxycarboxylic acids, and it is probable that modification of the hematite crystal shape is due to the presence of the degradation products rather than to the nature of the original sugar.

The results of this work suggest that cyclic molecules influence the transformation of ferrihydrite to a lesser extent than do acyclic molecules.