In this study, we used thermo–mechanical control process (TMCP) technique to investigate the effect of arisen dislocation density and texture components on hydrogen induced cracking susceptibility in as-received API X60 pipeline steel. Dislocations and texture components appeared during cold rolling and annealing treatments. X-ray diffraction and electron backscatter diffraction measurements were used to study these phenomena. We observed that the cold rolling and annealing treatments produced higher dislocation density in deformed and recovered regions. The increase of dislocation density also caused the increased hydrogen trap density. Macro-texture studies by x-ray method indicates that initial weak texture of as-received X60 steel was changed from ζ-fiber to γ-fiber and θ-fiber in 90% cold rolled and annealed specimen. Therefore, the number of grains with 〈100〉||ND orientation which had a harmful effect on hydrogen induced cracking susceptibility increased. The {100} dominant texture and high density of hydrogen traps mitigated against any possible benefits of the other microstructural parameters such as coincidence site lattice boundaries and grain size. As a result, we could not consider this process as a suitable method to increase hydrogen induced cracking resistance in pipeline steel.

Electron backscatter diffraction (EBSD) has become a common technique for measuring crystallographic orientations at spatial resolutions on the order of tens of nanometers and at angular resolutions <0.1°. In a recent search of EBSD papers using Google Scholar™, 60% were found to address some aspect of deformation. Generally, deformation manifests itself in EBSD measurements by small local misorientations. An increase in the local misorientation is often observed near grain boundaries in deformed microstructures. This may be indicative of dislocation pile-up at the boundaries but could also be due to a loss of orientation precision in the EBSD measurements. When the electron beam is positioned at or near a grain boundary, the diffraction volume contains the crystal lattices from the two grains separated by the boundary. Thus, the resulting pattern will contain contributions from both lattices. Such mixed patterns can pose some challenge to the EBSD pattern band detection and indexing algorithms. Through analysis of experimental local misorientation data and simulated pattern mixing, this work shows that some of the rise in local misorientation is an artifact due to the mixed patterns at the boundary but that the rise due to physical phenomena is also observed.