The different types of iron oxide phases associated with the surfaces of two suites of kaolins from Georgia, U.S.A., and from the Southwest Peninsula of England, have been identified using electron spin resonance (ESR) spectroscopy combined with magnetic-filtration, thermal, and chemical treatments. It has been shown that the English kaolins are coated with a lepidocrocitelike phase, which is readily removed by de Endredy's method of deferrification, while the Georgia kaolins are coated with a hematite- or goethitelike phase, which is not removed by this treatment. Throughout the course of this study, the effects of the various physical and chemical treatments on the brightness values of the kaolins were examined.

“Kaolinites” from classic, large deposits of kaolin are shown commonly in scanning electron micrographs to be mixtures, at least in part, in microdimensions, of kaolin-mineral polymorphs.

Artificial mixtures of selected kaolin polymorphs simulating the natural mixtures, also micrographed, show crystallinities intermediate between the crystallinities of the end members in X-ray powder diffractograms. Thus, apparent crystallinity interpreted from diffractograms of a kaolin specimen may be a product of kaolin-mineral mixture in microdimensions as well as from ordering in the crystals. Evaluation of the crystallinity of a kaolin from powder diffraction may be suspect if independent means, such as SEM, are not used to assess the monomineralic character of that kaolin specimen.

Analogous to the apparent crystallinity of a “kaolinite” being the product of a mixture, so may other widely ranging properties of “kaolinite” be products of kaolin-mineral mixtures in microdimensions. These properties include DTA, IR, chemical composition, free energies of formation, and industrial applications.

Specifications for a monomineralic, nearly ideal kaolinite are considered—the Keokuk geode variety possesses desired crystallographic and chemical properties.

Varieties of kaolin, a rock, may be classified geologically, mineralogically, crystallographically, genetically, texturally, morphologically, by industrial use, and in other ways which are desired. In this paper, the first-order of classification used is geological, i.e., transported and residual, after which other categories are used as subdivisions.

Scan electron micrographs, SEM, of the textures of kaolin show that distinctive textures characterize the several categories of classification. Varieties in texture of kaolin include similarities to those typical of sedimentary, igneous and metamorphic rocks. Because word descriptions of the textures are inadequate in comparison to pictures of them, the reader is referred to the micrographs.

SEM's illustrate differences between kaolins which were transported, formed, or deposited from solution, a colloidal phase, or as orthodox clastic particles. The parent source of kaolin deposited, or “grown,” from solution may be difficult to ascertain. It is suggested that the total role of solution work in kaolin petrology can be more important than has ordinarily been credited.

The Upper Cretaceous (Maastrichtian) Whitemud Formation is a potentially commercial kaolin deposit located in southern Saskatchewan and southeastern Alberta. The Whitemud Formation contains a lower kaolinitic sandstone, a middle lignite and carbonaceous shale, and an upper interbedded siltstone and claystone. The sediments that comprise the rocks of the Whitemud Formation were deposited on alluvial or upper deltaic plains located along the northwest flank of the Williston Basin.

Mineralogy and textures were determined by X-ray powder diffraction, scanning electron microscopy, and optical microscopy. Kaolinite abundance increases upward from the underlying rocks of the Eastend Formation through the Whitemud Formation, and the abundance of smectite, micas, and feldspars decreases from the Eastend Formation into the Whitemud Formation. Vermiform kaolinite crystals are in close spatial association with feldspar and mica grains. Near the top of the Whitemud Formation, etched quartz and feldspar grains, and gibbsite suggest the presence of a strong chemical leaching environment.

Mineral distributions, presence of root remains, pedologic mottles, grain coatings composed of clay, and soil horizons indicate the Whitemud Formation sediments were modified by intense weathering in a paleosol environment.

Kaolin concentrated from selected kaolinitic sandstone deposits, and beneficiated by oxidation, leaching, and high-intensity wet-magnetic separation has a product brightness up to filler quality. Recovery of lowabrasion kaolin is low and viscosity of a fine-particle kaolin fraction is high. Economics of producing a wet-processed filler-grade kaolin is marginal.

Measurements of the differential heats of K-Ca exchange are used to show that 6 groups of sites (ranging from −13.8 to −5.1 kJ/eq and with as many as 4 in any one sample) exist in kaolins that range from 0 to 15% in their 2:1 phyllosillicate content. These heat values, coupled with entropies of exchange, suggest that 0.1−10% vermiculitic, micaceous, and smectitic layers are present, presumably interstratified with kaolinitic layers which are assumed to have no permanent charge. Changes in the activity coefficients of adsorbed K with K saturation confirm these conclusions qualitatively. Thus, fK values at x ↑ 0 correlate inversely (r2 = 0.655) with the content of vermiculite + partially expanding micas, and x values at maximum fK indicate the content of vermiculite + nonexpanding mica + partially expanding micas (r2 = 0.732).

Several new, room-temperature luminescent phenomena, resulting from the interaction of kaolin and various amino compounds, have been observed. The emission of light from kaolin pastes (treated with quinoline, pyridine, hydrazine, monoethanolamine, n-butylamine, and piperidine) was shown to decay monotonically over a period of hours to days. More light was released by a given amino compound after it was dried and purified. Hydrazine, in addition to the monotonically decaying photon release, produces delayed pulses of light with peak emission wavelength of 365 nm which last between several hours and several days. These photon bursts are acutely sensitive to the initial dryness of the hydrazine, both in the number of bursts and the integrated photon output. The amount of light and the capacity of the kaolin to produce the delayed burst appeared to be strongly dependent on preliminary heating and on gamma-irradiation, analogous to the dehydration-induced light pulse previously reported from the Ames Research Center. A small, delayed burst of photons occurred when piperidine and n-butylamine were removed by evaporation into an H2SO4 reservoir.

The influence of added sodium and calcium nitrate electrolyte on the particle aggregates in the colloid fraction of natural bentonite and kaolin was studied. Clays were flocculated in distilled water and various electrolyte concentrations. Aggregate size was studied by sedimentation analysis; the mean radius of the aggregates was plotted against the concentrations of Na+ and Ca2+. For bentonite, the mean radii decreased with an increase of Na+ and Ca2+ concentration, reaching a minimum; and further increases in concentration led to an increase of the mean radii of the aggregates. For kaolin, an increase in Na+ and Ca2+ concentration gave rise to an increase in the mean radii of aggregates.

Scanning electron micrographs showed different types of aggregates, depending on the physico-chemical conditions of a sedimentation process. In bentonite and kaolin sediments formed from a distilled water slurry, the dominant aggregate was an edge-face type. The small addition of salts to a bentonite slurry led to the formation of edge-edge-type aggregates; for kaolin edge-face-type aggregates formed, although within the microaggregate face-face associations were observed. The highest concentrations of electrolytes for sediments of both clays led to formation of compact, face-face-type aggregates.

A 14-Å mineral coexisting with kaolin minerals, mica, and gibbsite in a Korean Ultisol and showing X-ray powder diffraction features of “chloritized” vermiculite was studied by a combination of methods. The 14-Å mineral collapsed on saturation with K+ after extraction with hot 1/3 M sodium citrate, but the Si/Al ratio of the extracted material was close to 1.0 and kaolin minerals dissolved, as indicated by difference infrared spectroscopy. The 14-Å mineral was also collapsed by heating at or above 350°C. The difference infrared spectra and the X-ray powder diffraction patterns indicated that two forms of kaolin mineral are present that differ in thermal stability; one decomposed by heating at or below 375°C and the other by heating above 375°C. The former kaolin mineral is probably associated with vermiculite and the latter is present as a discrete form. The 14-Å mineral was inferred to be an intergradient vermiculite-kaolin mineral, in which most vermiculite layers each partially transform into double kaolin layers, and to represent an intermediate phase during the transformation of 2:1 to 1:1 layer silicates in acid soils.

The reaction of kaolin with NaCl was followed by dynamic thermal analysis and mass spectrometry under N2, CO2, and air atmospheres and in a 10−5-torr vacuum. The weight loss was a function of the atmosphere used and, according to mass spectrometry, was due to the evolution of H2O, HCl, and very small amounts of H2. HCl was formed only after the release of 85% of the hydroxyl content of the kaolin. When the clay was pretreated with saturated salt solution, H2O and HCl evolved in more or less the same temperature range, indicating that only some of the OH groups reacted with the chloride ion. High-temperature X-ray powder diffraction patterns showed that the sodium ion reacted with the noncrystalline metakaolin to give NaAlSiO4. Chemical analysis showed that the reaction of kaolinite and sodium chloride started below 400°C. The rate of the reaction increased at higher water vapor concentration. From mass spectrometric data, the NaCl-treated kaolin appeared to adsorb CO2. Desorption at several distinct temperatures suggests that CO2 was adsorbed by different parts of the structure, i.e., holes and channels. X-ray powder diffraction and infrared absorption data indicate that the kaolinite structure persisted even after it had been heated with NaCl in a CO2 atmosphere to as high as 800°C.

A mineralogical investigation of the highly kaolinized Chanon granite and albite-muscovite granite of the Montebras cupola, Creuse, France, indicates that the magmatic stage was followed by two hydrothermal events related to successive cooling stages and by late weathering. The hydrothermal alteration was accompanied first by greisen formation and then a broad kaolinization process, which pervasively affected the granitic bodies. In the Chanon granite, the greisens are characterized by a trilithionite-lepidolite-quartz-tourmaline assemblage and are surrounded by concentric alteration zones. From the greisen to the fresh granite three zones were distinguished: (1) a zone characterized by secondary brown biotite (<400°C), (2) a zone characterized by secondary green biotite and phengite (300–350°C), and (3) a zone characterized by the presence of corrensite (180°–200°C) located around greisen veinlets. In the albite-muscovite granite the greisen is composed of lepidolite and quartz. This mineral assemblage was followed locally by Li-tosudite crystallization. During the second hydrothermal event (<100°C) an assemblage of kaolinite, mixed-layer illite/smectite (I/S), and illite formed pervasively and in crack fillings; the smectite layers of the US are potassic. Weathering produced Fe oxide and kaolinite. This kind of alteration developed mainly in the overlying Chanon granite. Here, Ca-Mg-montmorillonite formed in subvertical cracks, which transect the two granitic bodies, and hydrothermal I/S was obliterated by Ca-Mg-montmorillonite.

The hydrothermal parageneses were apparently controlled by magmatic albitization and the bulk chemistry of the two granitic bodies. The albitization, the formation of large micaceous greisens, and the successive recrystallizations of biotite (which was the most susceptible phase to alteration) provide information on the temperature range and chemical mobility during successive cooling stages. Si and Mg activities increased as the temperature of alteration decreased, and secondary Mg-biotite and Mg-phengite crystallized as long as the K activity was sufficient. The crystallizations of secondary biotite and phengite were followed by the crystallization of I/S during stages of low K activity. Secondary hydrothermal phases in the Chanon granite contain substantial Fe and Mg. Secondary hydrothermal phases in the albite-muscovite granite contain only small amounts of Fe and Mg, suggesting a lack of chemical exchange between the enclosing Chanon granite and the albite-muscovite granite, which is depleted in Fe-Mg-rich primary phases, such as biotite.

Kaolin floc structures of commercial utility are produced by adsorption of hexamethylenediamine. These flocs are largely face-to-face structures with small diameter platelets of colloidal kaolinite aggregated on larger platelets of kaolinite and muscovite. Because of its higher charge density, muscovite is more effective than kaolinite in scavenging colloidal particles.

Although earlier workers have been at odds as to where amines adsorb on kaolinite, the present work indicates that both edge and basal surfaces are involved. Evidence for this contention is two-fold: (1) Face-to-face and edge-to-face flocculation of hexamethylenediamine kaolins has been observed. (2) Polyesters have been observed adsorbed on basal and edge surfaces of ethylenediamine-treated kaolins.

The mechanism by which kaolinite particles are bonded together into floc structures is unclear. Bridging by hexamethylenediammonium ions is a probable mechanism up to satisfaction of the cation-exchange capacity; further amine addition continues to promote flocculation. From this observation it is inferred that, in addition to bridging, hydrogen bonding and, perhaps, van der Waals forces are instrumental in floc formation. Although rheologically inferior to the untreated equivalent, these chemically induced flocs of kaolinite provide loosely packed, randomly oriented structures in paper coatings. Improved brightness, opacity, and printability of paper coatings arise from this structure.

Six standard polytypes of micas exist that have c-periodicities between 1 and 6 layers; these can be subdivided into groups A and B according to whether the octahedral cations are in the same set of positions in every layer or alternate regularly between I and II possible sets of positions (alternate slant directions), respectively. Correspondingly, 12 standard polytypes exist for 1:1 layers of the serpentine-type structures, which are divisible into four groups A-D. Groups A and B differ as in the micas, as do groups C and D. Groups A and B have ±a/3 interlayer shifts, whereas groups C and D have zero or ±b/3 interlayer shifts. Six structural types of semi-randomly or regularly stacked 1-layer chlorites exist that differ in the slant of the interlayer sheet (I or II) and its position (a or b) relative to 6-member rings in adjacent 2:1 layers.

Criteria have been established that permit the X-ray diffraction identification of the above-mentioned groups as well as the individual polytypes within each group. These criteria involve inspection of the strong X-ray diffraction reflections of index k = 3n for identification of the groups and of the generally weaker k ≠ 3n reflections for identification of the polytypes (assuming indexing on orthohexagonal axes throughout for convenience). In all hydrous phyllosilicates the octahedral cations and anions repeat at intervals of b/3 and thus contribute strongly to X-ray diffraction reflections of index k = 3n. The intensities of these reflections identify the two mica groups, the four serpentine-type groups, and the six chlorite groups. The periodicities of these reflections along Z* is that between identical octahedral sheets. The basal oxygen atoms do not repeat at intervals of b/3 and are a primary contributor to the intensities of k ≠ 3n reflections. The period along Z* for these reflections is that between identical basal oxygen planes, and the periodicity plus the symmetry identify the individual trioctahedral polytypes. For dioctahedral polytypes of the kaolin-group minerals and chlorites, the position of the vacant octahedral site must be considered also.

These general principles can be illustrated especially well by single-crystal precession photographs and extrapolated to powder photographs.

57Fe Mössbauer spectra have been used to interpret the effects of different cleaning processes on the iron mineralogy of a Weipa, Australia, kaolin. A magnetically separated fraction contained 28% of its iron as hematite likely of secondary origin. An initial centrifugal size separation was shown to give an improved final product, and oxalic acid was found to be more efficient at removing Fe from the kaolinite surface than dithionite bleach. The Mössbauer spectra clearly show that beneficiation steps which give a substantial increase in kaolin brightness result in only minor changes in the clay iron mineralogy. Similar results were also obtained for two commercially available kaolins.

Mineralogy, kaolin crystallinity, Fe content, δO18, and δD were determined for late Cretaceous “soft” and early Tertiary “hard” Georgia kaolins. The crystallinity of the <0.5-, 0.5–1.0-, and 1.0–2.0- μm size fractions of soft kaolins was higher than that of equivalent size fractions of hard kaolins. δO18 and δD of the soft and hard kaolins ranged between 18.5 to 23.1‰, and −64 to −41‰, respectively, and could not be used to discriminate soft from hard kaolins. The trends of crystallinity vs. δO18 were different for kaolins collected at different localities, and, for a given sample, δO18 generally decreased with increasing crystallinity and with increasing crystallite size. These data indicate that the Tertiary kaolins could not have been simply derived from the Cretaceous kaolins by winnowing unless post-sedimentation recrystallization of one or both occurred. δD vs. δO18 systematics indicate that the late Cretaceous to early Tertiary Georgia kaolins crystallized over a temperature range of about 15°C in the presence of waters that varied little in isotopic composition.

Six well-characterized soil kaolins from widely separated sites in south-western Australia and four reference kaolins were studied by 57Fe Mössbauer spectroscopy at room temperature after removal of non-structurally-bound iron with dithionite-citrate-bicarbonate solution. The soil kaolins and one of the reference kaolins were also studied at temperatures near 16 K. The soil kaolins were remarkably similar in crystal size, crystallinity, dehydroxylation temperature, cation exchange capacity, surface area and iron content. Müssbauer spectra of the soil kaolins at room temperature were also essentially identical consisting of a quadrupole-split doublet superimposed on a broad component which indicated that all of the iron was present as Fe(III) and that slow paramagnetic relaxation effects were present. Mean values for the chemical isomer shift and quadrupole splitting of the doublet for the soil kaolins were 0.33 and 0.55 mm/s respectively which indicates that the iron is in the octahedral sites of the kaolin lattice. The spectra of the soil kaolin samples at temperatures near 16 K showed a further slowing down of the paramagnetic relaxation and confirmed that no discrete iron oxide minerals were present.

Mössbauer spectra of the four reference kaolins at room temperature showed a doublet component similar to those for the soil kaolins. Three of them showed evidence for other spectral components including, in two cases, a component due to the presence of Fe(II).

The level of Fe impurities in 2 well-crystallized kaolinites was modified (by addition or chemical removal treatment) to analyze the Fe influence in the aluminosilicate zeolite synthesis.

The original and modified clays were heat-treated in order to change their reactivity for zeolite A synthesis, and their thermal transformations were studied by X-ray diffraction (XRD), determination of point of zero charge (PZC) and infrared (IR) techniques. It was established that many structural changes took place, regardless of the Fe clay content. Furthermore, the presence of Fe species in alkaline solution or in the solid phase did not seem to greatly influence the zeolite crystallization, because only small differences in the conversion values among samples with different Fe contents were registered. The crystallization process seemed to be related mainly to AI coordination changes produced by the thermal and Fe removal treatments used.

Diffuse reflectance spectra of kaolins have been recorded in samples from different environments. They show the systematic presence of Fe-oxides, even in bleached kaolins, with no contribution from the Fe3+ ions substituted in kaolinite. Second derivative spectra of various Fe-phases (hematite, goethite, lepidocrocite, maghemite, akaganeite, ferrihydrite and Fe-polymer) may be differentiated by the position of a diagnostic band corresponding to the 2(6A1) → 2(4T1(4G)) transition. The systematic comparison of diffuse reflectance spectra of unbleached and bleached kaolins has demonstrated the differences between the Fe-oxides occurring as coatings and as occluded phases. The features observed in second derivative spectral curves are consistent with assignments of crystal field transitions to goethite, hematite, akaganeite, and aged hydrous ferric oxides. The optical determination of the Fe-phases associated to kaolins assists in the interpretation of the formation conditions of these minerals.