Study Using Elements from Group IIA as Barriers for Dopant Penetration into Gate Dielectrics and Getters for Metallic Ion Contamination

Published online by Cambridge University Press:  01 February 2011

Vladimir Zubkov ,
Grace Sun ,
Sheldon Aronowitz  and
Margaret A. Gabriel
Vladimir Zubkov
Affiliation:
LSI Logic Corporation, Milpitas, CA 95035, U.S.A.
Grace Sun
Affiliation:
LSI Logic Corporation, Milpitas, CA 95035, U.S.A.
Sheldon Aronowitz
Affiliation:
LSI Logic Corporation, Milpitas, CA 95035, U.S.A.
Margaret A. Gabriel
Affiliation:
Department of Chemistry, University of Washington, Seattle, WA, U.S.A.
Get access

Abstract

Various mechanical and chemical processes may introduce contamination, such as metallic ions, during the creation of an integrated circuit. This can cause device degradation and leakage current. Neutral dopants such as boron can penetrate the silicon substrate from a highly doped polysilicon gate during anneal cycles causing leakage and threshold voltage shifts. Quantum mechanical modeling using periodic boundary conditions and a cluster approximation were performed in a search for a modification of silicon dioxide that would attract or trap ions and fast diffusing dopant species to reduce or eliminate such problems. Examination of calcium and strontium interactions with some metal ions in silicon dioxide was conducted. Strong metal ion attraction to both calcium and strontium was found. Interaction of calcium with boron and fluorine in oxide and calcium interaction with boron in other dielectric materials was also studied. Attraction was predicted to occur between calcium and boron whether they were distributed in silicon dioxide, hafnium or zirconium orthosilicate. This study leads us to propose incorporation of calcium or strontium into critical dielectric layers as a promising approach to trap ions and reduce boron penetration through the gate oxide. Predictions were used to design relevant experiments which revealed that calcium implanted into oxide traps boron and fluorine.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 765: Symposium D – CMOS Front-End Materials and Process Technology , 2003 , D1.8
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Oborina, E., Campbell, S., Hoff, A. M., Gilbert, R., Persson, E., and Simpson, D., Mat. Res. Soc. Symp. Proc., 716, B13.4 (2002).Google Scholar
2. Choi, B. D. and Schroder, D. K., Appl. Phys. Lett., 79, 2646 (2001)Google Scholar
3. Wolf, S., Silicon Processing for the VLSI Era Vol. 3, (Lattice Press, 1990), p.649 Google Scholar
4. Plummer, J. D., Deal, M. D., and Griffin, P. B., Silicon VLSI Technology, (Prentice Hall, 2000) pp. 347–350 Google Scholar
5. Kresse, G. and Hafner, J., Phys. Rev. B47, 558 (1993); ibid 49, 14251,1994; G.Kresse and J. Furthmuller, Comput. Mater. Sci. 6, 15 (1996); G. Kresse and J. Furthmuller, Phys. Rev. B54, 11169 (1996); G. Kresse and J. Hafner, J. Phys. Condens. Matter., 6, 8245, (1994).Google Scholar
6. Vanderbilt, D., Phys. Rev. B41, 7892 (1990).Google Scholar
7. Frisch, M.J., Trucks, G.W., Schlegel, B.H. et al., Gaussian 98, Revision A.5 (Gaussian, Inc., Pittsburgh, PA, 1998).Google Scholar
8. Zubkov, V., Senosian, J.P., Aronowitz, S., Sukharev, V., and Musgrave, C.B., Mat. Res. Soc. Symp. Proc., 610, B5.11 (2000).Google Scholar