The Influence of Stress-Induced Voiding on the Electromigration Behavior of AlCu Interconnects

Published online by Cambridge University Press:  17 March 2011

A.E. Zitzelsberger  and
A.H. Fischer
A.E. Zitzelsberger
Affiliation:
Infineon Technologies Reliability Methodology Otto Hahn Ring 6 D-81739 Munich, Germany
A.H. Fischer
Affiliation:
Infineon Technologies Reliability Methodology Otto Hahn Ring 6 D-81739 Munich, Germany
Get access

Abstract

The influence of stress-induced voiding on the electromigration (EM) behavior has been investigated on narrow via-line structures. For this purpose the EM performance of metal lines containing stress-induced voids already before the electrical operation has been compared with samples without stress-induced voids. We found, that pre-existing stress voids in the metal lines do not affect the activation energy Ea and lead only to a small decrease of the EM median time to failure, but cause a relevant reduction of the current density exponent down to n = 1. As a consequence, a tremendous decrease of the electromigration limited life time is obtained.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 612: Symposium D – Materials, Technology & Reliability for Advanced Interconnects.. , 2000 , D8.9.1
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Lee, S.G. et al. , to be published in proceedings of the IITC meeting (1999).Google Scholar
[2] Besser, P. et al. , Proc. AMC, 699–704 (1998).Google Scholar
[3] Sullivan, T.D., proposed as JEDEC standard, JC-14.2-98-189 (1998).Google Scholar
[4] Fischer, A.H. et al. , „Stressmigration behavior of multilevel ULSI AlCu Metallization“, to be published in this proc.Google Scholar
[5] Lloyd, J.R., „Electromigration in integrated circuit conductors“, J. Phys. D: Appl. Phys. 32, R109–118 (1999).10.1088/0022-3727/32/17/201Google Scholar
[6] Lloyd, J.R., „Electromigration and mechanical stress“, Microelectronic Engineering 49, 51–64 (1999).10.1016/S0167-9317(99)00429-3Google Scholar
[7] Zitzelsberger, A.E. and Lehr, M., IRW final report, 10–13 (1999).Google Scholar