An Effect of Dopants on Contact Electromigration

Published online by Cambridge University Press:  15 February 2011

Eungsoo Kim
Affiliation:
Microprocess Development Team, Semiconductor R&D Center, Samsung Electronics Co., Buchun, Kyunggi-Do, Korea
Kyungwon Cho
Affiliation:
Microprocess Development Team, Semiconductor R&D Center, Samsung Electronics Co., Buchun, Kyunggi-Do, Korea
Hyungwoo Jang
Affiliation:
Microprocess Development Team, Semiconductor R&D Center, Samsung Electronics Co., Buchun, Kyunggi-Do, Korea
Soonkwon Lim
Affiliation:
Microprocess Development Team, Semiconductor R&D Center, Samsung Electronics Co., Buchun, Kyunggi-Do, Korea
Get access

Abstract

Recently, device reliability has been an important issue since the design rule is scaled down and complicated processing is involved. To improve the reliability, many problems should be solved. One of the problems in interconnection failure is short or open circuits at interconnection lines. Contact or via hole failure has been ignored while the metal line failure has been strongly studied by many researchers.

In this study, electromigration (EM) phenomena at the submicron size of contact hole are presented with respect to the type of dopants, boron and arsenic, implanted by high dose. In both cases, the failure mode at the contact hole, the values of the activation energy and the mean-time-to-failure (MTTF) are much different. For example the value of MTTF in boron is lower than that in As. The contact failure by EM is analyzed by SEM micrographs, FIB micrographs, EM measurement. One of the interesting results is void formation at the interface between implanted surface and silicon dioxide film, which is located between contact holes. This fact indicates that the interface migration of Si is much faster than the self-diffusion of Si because the current path is mainly formed along the interface.

Type
Research Article
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Blech, I.A. and Meieran, E.S., J. Appl. Phys., 40, 485 (1969).Google Scholar
2 Black, J.R., Proceedings of IEEE, 57, 1587 (1969).Google Scholar
3 Atakov, E.M., Clement, J.J. and Miner, B., Proceedings of IRPS, 1994, 213 Google Scholar
4 Learn, A.J., J. Elec. Materials, 3, 531 (1974).Google Scholar
5 Black, J.R., Proceedings of IRPS, 1978, 233.Google Scholar
6 Proko, G.S.p and Joseph, R.R., J. Appl. Phys., 43, (1972).Google Scholar
7 Repeta, M., Kolk, J., Saran, M. and Ho, V.Q., Proceedings of IEEE/VMIC, 1990, 351.Google Scholar
8 Gargini, P.A., Tseng, C. and Woods, M.H., Proceedings of IRPS, 1982 T 66.Google Scholar
9 Polcari, M.R. et al. , Proceedings of IRPS, 1980, 178.Google Scholar
10 Lloyd, J.R. et al. , Proceedings of IRPS, 1982, 47.Google Scholar
11 Murarka, S.P., Metallization; Theory and Practice for VLSI and ULSI. (Butterworth-Heinemann, MA, 1993), p. 97, p. 105.Google Scholar
12 Tsai, J.C.C., in Quick Reference Manual for Silicon Integrated Circuit Technology, edited by W.E, Beadle, Tsai, J.C.C. and Plummer, R.D. (John Wiley & Sons, New York, 1985), p. 631.Google Scholar