Tension gradient self-assembly to facilely fabricate polytetrafluoroethylene coatings for oil–water separation

Published online by Cambridge University Press:  23 May 2019

Dong Feng Open the ORCID record for Dong Feng [Opens in a new window] ,
Ding Weng ,
Chaolang Chen  and
Jiadao Wang
Dong Feng
Affiliation:
State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, P.R. China
Ding Weng
Affiliation:
State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, P.R. China
Chaolang Chen
Affiliation:
State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, P.R. China
Jiadao Wang*
Affiliation:
State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, P.R. China
*
Address all correspondence to Jiadao Wang at [email protected]
Get access

Abstract

A facile and low-cost method based for tension gradient self-assembly was developed to prepare polytetrafluoroethylene (PTFE) nanofiber coatings on stainless-steel fiber felts. The PTFE particles were used as building blocks and the self-assembly process was analyzed thoroughly. After being sintered, the PTFE particles were transformed into PTFE nanofibers. The felts coated with the PTFE nanofibers exhibited superhydrophobicity and superoleophilicity, and could separate a series of oil–water mixtures with high efficiency and good reusability. The coated felts also presented excellent chemical and thermal stabilities. Over all, this approach could easily fabricate ultra-robust oil–water separation materials suitable for industrial applications.

Type
Research Letters
Information
MRS Communications , Volume 9 , Issue 2 , June 2019 , pp. 690 - 696
Copyright
Copyright © Materials Research Society 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Yu, Y., Chen, H., Liu, Y., Craig, V.S., Wang, C., Li, L.H., and Chen, Y.: Superhydrophobic and superoleophilic porous boron nitride nanosheet/polyvinylidene fluoride composite material for oil-polluted water cleanup. Adv. Mater. Interfaces 2, 1400267 (2015).Google Scholar
2.Kwon, G., Post, E., and Tuteja, A.: Membranes with selective wettability for the separation of oil–water mixtures. MRS Commun. 5, 475 (2015).Google Scholar
3.Xue, Z., Cao, Y., Liu, N., Feng, L., and Jiang, L.: Special wettable materials for oil/water separation. J. Mater. Chem. A 2, 2445 (2014).Google Scholar
4.Yin, K., Chu, D., Dong, X., Wang, C., Duan, J.-A., and He, J.: Femtosecond laser induced robust periodic nanoripple structured mesh for highly efficient oil–water separation. Nanoscale 9, 14229 (2017).Google Scholar
5.Song, J., Huang, S., Lu, Y., Bu, X., Mates, J.E., Ghosh, A., Ganguly, R., Carmalt, C.J., Parkin, I.P., Xu, W., and Megaridis, C.M.: Self-driven one-step oil removal from oil spill on water via selective-wettability steel mesh. ACS Appl. Mater. Interfaces 6, 19858 (2014).Google Scholar
6.Wang, E., Wang, H., Hu, Y., Liu, Z., and Zhu, Y.: Corrosion-resistant engineering superhydrophobic and superoleophilic bulk materials with oil–water separation property. J. Mater. Sci. 52, 7130 (2017).Google Scholar
7.Wang, S., Song, Y., and Jiang, L.: Microscale and nanoscale hierarchical structured mesh films with superhydrophobic and superoleophilic properties induced by long-chain fatty acids. Nanotechnology 18, 015103 (2006).Google Scholar
8.Wang, L., Yang, S., Wang, J., Wang, C., and Chen, L.: Fabrication of superhydrophobic TPU film for oil–water separation based on electrospinning route. Mater. Lett. 65, 869 (2011).Google Scholar
9.Zhang, J. and Seeger, S.: Polyester materials with superwetting silicone nanofilaments for oil/water separation and selective oil absorption. Adv. Funct. Mater. 21, 4699 (2011).Google Scholar
10.Du, C., Wang, J., Chen, Z., and Chen, D.: Durable superhydrophobic and superoleophilic filter paper for oil–water separation prepared by a colloidal deposition method. Appl. Surf. Sci. 313, 304 (2014).Google Scholar
11.Wang, J., Shi, Z., Fan, J., Ge, Y., Yin, J., and Hu, G.: Self-assembly of graphene into three-dimensional structures promoted by natural phenolic acids. J. Mater. Chem. 22, 22459 (2012).Google Scholar
12.Chen, C., Du, C., Weng, D., Mahmood, A., Feng, D., and Wang, J.: Robust superhydrophobic polytetrafluoroethylene nanofibrous coating fabricated by self-assembly and its application for oil/water separation. ACS Appl. Nano Mater. 1, 2632 (2018).Google Scholar
13.Artyukhin, A.B., Bakajin, O., Stroeve, P., and Noy, A.: Layer-by-layer electrostatic self-assembly of polyelectrolyte nanoshells on individual carbon nanotube templates. Langmuir 20, 1442 (2004).Google Scholar
14.Tsukruk, V., Bliznyuk, V., Visser, D., Campbell, A., Bunning, T., and Adams, W.: Electrostatic deposition of polyionic monolayers on charged surfaces. Macromolecules 30, 6615 (1997).Google Scholar
15.Lu, H.-H., Yang, Y.-M., and Maa, J.-R.: Effect of artificially provoked Marangoni convection at a gas/liquid interface on absorption. Ind. Eng. Chem. Res. 35, 1921 (1996).Google Scholar
16.Sha, Y., Chen, H., Yin, Y., Tu, S., Ye, L., and Zheng, Y.: Characteristics of the Marangoni convection induced in initial quiescent water. Ind. Eng. Chem. Res. 49, 8770 (2010).Google Scholar
17.Young, N.O., Goldstein, J.S., and Block, M.J.: The motion of bubbles in a vertical temperature gradient. J. Fluid Mech. 6, 350 (1959).Google Scholar
18.Feng, D., Weng, D., and Wang, J.: A facile interfacial self-assembly of crystalline colloidal monolayers by tension gradient. Micromachines (Basel) 9, 297 (2018).Google Scholar
19.Luo, Z., Zhang, Z., Hu, L., Liu, W., Guo, Z., Zhang, H., and Wang, W.: Stable bionic superhydrophobic coating surface fabricated by a conventional curing process. Adv. Mater. 20, 970 (2008).Google Scholar
20.Luo, Z., Zhang, Z., Wang, W., Liu, W., and Xue, Q.: Various curing conditions for controlling PTFE micro/nano-fiber texture of a bionic superhydrophobic coating surface. Mater. Chem. Phys. 119, 40 (2010).Google Scholar
21.Zhang, W., Liu, N., Cao, Y., Chen, Y., Xu, L., Lin, X., and Feng, L.: A solvothermal route decorated on different substrates: controllable separation of an oil/water mixture to a stabilized nanoscale emulsion. Adv. Mater. 27, 7349 (2015).Google Scholar
22.Accardo, A., Shalabaeva, V., Di Cola, E., Burghammer, M., Krahne, R., Riekel, C., and Dante, S.: Superhydrophobic surfaces boost fibril self-assembly of amyloid β peptides. ACS Appl. Mater. Interfaces 7, 20875 (2015).Google Scholar
23.Xue, Z., Sun, Z., Cao, Y., Chen, Y., Tao, L., Li, K., Feng, L., Fu, Q., and Wei, Y.: Superoleophilic and superhydrophobic biodegradable material with porous structures for oil absorption and oil–water separation. RSC Adv. 3, 23432 (2013).Google Scholar
24.Pi, P., Hou, K., Zhou, C., Li, G., Wen, X., Xu, S., Cheng, J., and Wang, S.: Superhydrophobic Cu2S@Cu2O film on copper surface fabricated by a facile chemical bath deposition method and its application in oil–water separation. Appl. Surf. Sci. 396, 566 (2017).Google Scholar
25.Yu, S. and Guo, Z.: Superhydrophobic surfaces based on polypyrrole with corrosion resistance and the separation of oil/water mixture properties. RSC Adv. 5, 107880 (2015).Google Scholar
26.Roach, P., Shirtcliffe, N.J., and Newton, M.I.: Progress in superhydrophobic surface development. Soft Matter 4, 224 (2008).Google Scholar
27.Bi, Z. and Mueller, D.W.: Friction predication on pin-to-plate interface of PTFE material and steel. Friction, Published online 10 August 2018.Google Scholar
28.Bayer, I.S., Davis, A.J., Loth, E., and Steele, A.: Water jet resistant superhydrophobic carbonaceous films by flame synthesis and tribocharging. Mater. Today Commun. 3, 57 (2015).Google Scholar
29.Bayer, I., Caramia, V., Fragouli, D., Spano, F., Cingolani, R., and Athanassiou, A.: Electrically conductive and high temperature resistant superhydrophobic composite films from colloidal graphite. J. Mater. Chem. 22, 2057 (2012).Google Scholar
Supplementary material: File

Feng et al. supplementary material

Feng et al. supplementary material 1

Download Feng et al. supplementary material(File)
File 12.2 MB