Investigation of the phase equilibria at 773 K and metallic glass regions in the Ag–Al–Zr ternary system

Published online by Cambridge University Press:  09 January 2018

Hsien-Ming Hsiao
Affiliation:
Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 10672, Taiwan, Republic of China Institute of Nuclear Energy Research, Taoyuan 32546, Taiwan, Republic of China
Yung-Chin Lan
Affiliation:
Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 10672, Taiwan, Republic of China
Gita Novian Hermana
Affiliation:
Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 10672, Taiwan, Republic of China
Hao Chen
Affiliation:
Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 10672, Taiwan, Republic of China
Get access

Abstract

Forty-eight different Ag–Al–Zr ternary alloys were prepared in various compositions to determine the metallic glass region in the Ag–Al–Zr ternary system. Experimental results indicated that the metallic glass region in the Ag–Al–Zr ternary system is Ag20–30Al10–30Zr50–60. The Ag20Al30Zr50 and Ag30Al20Zr50 alloys are supposed to have the best glass-forming ability in the Ag–Al–Zr ternary system. The phase equilibria of the Ag–Al–Zr ternary system at 773 K (500 °C) were investigated and compared with the metallic glass region results in the Ag–Al–Zr ternary system. Ternary isothermal sections of the Ag–Al–Zr system at 773 K (500 °C) were established and two ternary intermetallic phases were observed in this isothermal section.

Type
Research Letters
Copyright
Copyright © Materials Research Society 2018 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Inoue, A.: Bulk Amorphous Alloys: Preparation and Fundamental Characteristics (Trans Tech Publications, Zurich, Swiss, 1998).Google Scholar
2. Chu, J.P., Chiang, C.L., Nieh, T.G., and Kawamura, Y.: Superplasticity in a bulk amorphous Pd-40Ni-20P alloy: a compression study. Intermetallics 10, 1191 (2002).Google Scholar
3. Zhang, W. and Inoue, A.: Formation and mechanical strength of new Cu-based bulk glassy alloys with large supercooled liquid region. Mater. Trans. JIM 45, 1210 (2004).CrossRefGoogle Scholar
4. Nishiyama, N., Amiya, K., and Inoue, A.: Bulk metallic glasses for industrial products. Mater. Trans. JIM 45, 1245 (2004).CrossRefGoogle Scholar
5. Inoue, A.: Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater. 48, 279 (2000).Google Scholar
6. Turnbull, D.: Under what conditions can a glass be formed? Contemp. Phys. 10, 473 (1969).CrossRefGoogle Scholar
7. Lu, Z.P., Liu, Y., and Liu, C.T.: Evaluation of glass-forming ability, in Bulk Metallic Glasses, In Bulk Metalic Glasses: An overview edited by Miller, M. and Liaw, P. (Springer, Boston, MA, 2008), pp. 87115.Google Scholar
8. Yuan, Z.Z., Bao, S.L., Lu, Y., Zhang, D.P., and Yao, L.: A new criterion for evaluating the glass-forming ability of bulk glass forming alloys. J. Alloys Compd. 459, 251 (2008).Google Scholar
9. Lu, Z.P., and Liu, C.T.: A new glass-forming ability criterion for bulk metallic glasses. Acta Mater. 50, 3501 (2002).Google Scholar
10. Inoue, A., Zhang, T., and Masumoto, T.: Preparation of bulky amorphous Zr-Al-Co-Ni-Cu alloys by copper mold casting and their thermal and mechanical properties. Mater. Trans. JIM 36, 391 (1995).CrossRefGoogle Scholar
11. Inoue, A. and Zhang, W.: Formation, thermal stability and mechanical properties of Cu-Zr-Al bulk glassy alloys. Mater. Trans. 43, 2921 (2002).Google Scholar
12. McAlister, A.J.: The Ag–Al (silver–aluminum) system. Bull. Alloy Phase Diagr. 8, 526 (1987).Google Scholar
13. Karakaya, I., and Thompson, W.T.: The Ag–Zr (silver–zirconium) system. J. Phase Equilib. 13, 143 (1992).Google Scholar
14. Murray, J., Peruzzi, A., and Abriata, J.P.: The Al–Zr (aluminum–zirconium) system. J. Phase Equilib. 13, 277 (1992).Google Scholar
15. Rieger, W., Nowotny, H., and Benesovsky, F.: Crystallochemical investigation of systems containing ternary elements, (Cu, Ag) and (Al, Ga). Monatsh. Chem. 95, 1573 (1964).Google Scholar
16. Kotur, B. and Verbovytsky, Y.: Phase equilibria in the {Zr, Hf}-Ag-Al systems at 500 °C and crystal structure of the ternary compounds. Prace Nauk. WSP Chem. 8, 7 (2003).Google Scholar
17. American Ceramic Society: JCPDS-International Centre for Diffraction Data (Swarthmore, PA, 2003).Google Scholar