Fatigue cracking in polycrystalline NiTi was investigated using a multiscale experimental framework for average grain sizes (GS) from 10 to 1500 nm for the first time. Macroscopic fatigue crack growth rates, measured by optical digital image correlation, were connected to microscopic crack opening and closing displacements, measured by scanning electron microscope DIC (SEM-DIC) using a high-precision external SEM scan controller. Among all grain sizes, the 1500 nm GS sample exhibited the slowest crack growth rate at the macroscale, and the largest crack opening level (stress intensity at first crack opening) and minimum crack opening displacements at the microscale. Smaller GS samples (10, 18, 42, and 80 nm) exhibited nonmonotonic trends in their fatigue performance, yet the correlation was strong between macroscale and microscale behaviors for each GS. The samples that exhibited the fastest crack growth rates (42 and 80 nm GS) showed a small crack opening level and the largest crack opening displacements. The irregular trends in fatigue performance across the nanocrystalline GS samples were consistent with nonmonotonic values in the elastic modulus reported previously, both of which may be related to the presence of residual martensite only evident in the small GS samples (10 and 18 nm).

The increasing demand for portable and low-power electronics for applications in self-powered devices and sensors has spurred interest in the development of efficient piezoelectric materials, via which mechanical energy from ambient vibrations can be transformed into electrical energy for autonomous devices, or which can be used in strain-sensitive applications. Semiconducting piezoelectric materials are ideal candidates in the emerging field of piezotronics and piezophototronics, where the development of a piezopotential in response to stress/strain can be used to tune the band structure of the semiconductor and hence its electronic and/or optical properties. Furthermore, research into nanowires of these materials has intensified due to the enhancement of piezoelectric properties at the nanoscale. In this regard, nanowires of ZnO and the III-nitrides have been extensively studied, but the piezoelectric properties of non-nitride III–V semiconductor nanowires remain less-explored. Indeed, direct measurements of the piezoelectric properties of single III–V nanowires are tellingly rare due to the difficulties associated with measurements of piezoelectric properties of nanoscale objects using conventional scanning probe microscopy techniques. This review addresses the challenges related to the study of piezoelectricity in III–V nanowires and the opportunities that lie therein in terms of device applications.

Transition metal perovskite chalcogenides, a class of materials with rich tunability in functionalities, are gaining increased attention as candidate materials for renewable energy applications. Perovskite oxides are considered excellent n-type thermoelectric materials. Compared to oxide counterparts, we expect the chalcogenides to possess more favorable thermoelectric properties such as lower lattice thermal conductivity and smaller band gap, making them promising material candidates for high temperature thermoelectrics. Thus, it is necessary to study the thermal properties of these materials in detail, especially thermal stability, to evaluate their potential. In this work, we report the synthesis and thermal stability study of five compounds, α-SrZrS3, β-SrZrS3, BaZrS3, Ba2ZrS4, and Ba3Zr2S7. These materials cover several structural types including distorted perovskite, needle-like, and Ruddlesden–Popper phases. Differential scanning calorimeter and thermogravimetric analysis measurements were performed up to 1200 °C in air. Structural and chemical characterizations such as X-ray diffraction, Raman spectroscopy, and energy dispersive analytical X-ray spectroscopy were performed on all the samples before and after the heat treatment to understand the oxidation process. Our studies show that perovskite chalcogenides possess excellent thermal stability in air at least up to 550 °C.

The powder-bed laser additive manufacturing (AM) process is widely used in the fabrication of three-dimensional metallic parts with intricate structures, where kinetically controlled diffusion and microstructure ripening can be hindered by fast melting and rapid solidification. Therefore, the microstructure and physical properties of parts made by this process will be significantly different from their counterparts produced by conventional methods. This work investigates the microstructure evolution for an AM fabricated AlSi10Mg part from its nonequilibrium state toward equilibrium state. Special attention is placed on silicon dissolution, precipitate formation, collapsing of a divorced eutectic cellular structure, and microstructure ripening in the thermal annealing process. These events alter the size, morphology, length scale, and distribution of the beta silicon phase in the primary aluminum, and changes associated with elastic properties and microhardness are reported. The relationship between residual stress and silicon dissolution due to changes in lattice spacing is also investigated and discussed.

Recently, significant progress in the field of grain boundary segregation was achieved, for example, in better understanding and modeling the stabilization of nanocrystalline structures by grain boundary segregation, searching for more advanced approaches to theoretical calculation of segregation energies and development of the complexion approach. Nevertheless, with each progress, new important questions appear which need to be solved. Here, we focus on two basic questions appearing recently: How can be the experimental results on the grain boundary segregation compared reliably to their theoretical counterparts? Is the preferred segregation site of a solute in the grain boundary core substitutional or interstitial? We also show that the entropy of grain boundary segregation is a very important quantity which cannot be neglected in thermodynamic considerations as it plays a crucial role, for example, in prediction of thermodynamic characteristics of grain boundary segregation and in the preference of the segregation site at the boundary.

Single photon sources (SPS) are an important building block for realizing quantum technologies for computing, communication, and sensing. For industrialization, electrically controllable color centers acting as SPS are required. We have demonstrated the creation of electrically controllable silicon vacancies (VSis) in the SiC pn junction diode fabricated by proton beam writing (PBW). PBW was successfully used to introduce electrically controllable VSi without degradation of the diode performance. The dependence of the electroluminescence (EL) and photoluminescence (PL) intensities from VSi on H+ fluence revealed that the emission efficiency of EL is less than that of PL. For EL, the supply of carriers (electrons and/or holes) was restricted due to the resistive region around each VSi introduced by PBW. The results suggest that further improvement in the VSi creation process without defects acting as majority carrier removal centers (highly resistive region) and nonradiative centers by optimization of PBW conditions are key points to realize highly sensitive quantum sensors using VSi.

Engineering the surface structure, together with the incorporation of a second metal, is an effective strategy for boosting the catalytic activities of Pt-based catalysts toward various reactions. Here, we report a facile approach to the synthesis of Pt–Ag octahedral and tetrahedral nanocrystals covered by concave surfaces. The presence of the Ag(I) precursor not only facilitated the reduction of the Pt(IV) precursor but also led to the formation of concaved facets on the Pt–Ag nanocrystals. Besides, poly(vinylpyrrolidone) (PVP) was demonstrated to serve as a co-reductant, in addition to its role as a colloidal stabilizer. Using PVP with different molecular weights, we were able to tune the size of the Pt–Ag nanocrystals in the range of 9–25 and 14–32 nm for the octahedral and tetrahedral shapes, respectively. The Pt–Ag nanocrystals exhibited 4.6- and 2.0-fold enhancements in terms of specific and mass activities, respectively, toward methanol oxidation, when benchmarked against the commercial Pt/C catalyst. After 1000 cycles of the accelerated tests, the specific and mass activities of the Pt–Ag nanocrystals were still 3.6 and 1.6 times as high as those of the original commercial Pt/C.

In this work, the deformation mechanisms underlying the room temperature deformation of the pseudomorphic body centered cubic (BCC) Mg phase in Mg/Nb nanolayered composites are studied. Nanolayered composites comprised of 50% volume fraction of Mg and Nb were synthesized using physical vapor deposition with the individual layer thicknesses h of 5, 6.7, and 50 nm. At the lower layer thicknesses of h = 5 and 6.7 nm, Mg has undergone a phase transition from HCP to BCC such that it formed a coherent interface with the adjoining Nb phase. Micropillar compression testing normal and parallel to the interface plane shows that the BCC Mg nanolayered composite is much stronger and can sustain higher strains to failure than the HCP Mg nanolayered composite. A crystal plasticity model incorporating confined layer slip is presented and applied to link the observed anisotropy and hardening in the deformation response to the underlying slip mechanisms.

We present a method for measuring the shear complex modulus of hydrogels by oscillatory nanoindentation, with unprecedented attention to procedure and uncertainty analysis. The method is verified by testing a typical low-molecular-weight gelator formed from the controlled hydrolysis of glucono-δ-lactone. Nanoindentation results are compared with those obtained by rheometry using both vane-in-cup and parallel-plate fixtures. At 10 Hz, the properties measured by oscillatory nanoindentation were G′ = 38.1 ± 2.8 kPa, tan δ = 0.22 ± 0.02. At the same frequency, the properties measured by rheometry were G′ = 15.3 ± 2.9 kPa, tan δ = 0.11 ± 0.016 (vane-in-cup) and G′ = 7.9 ± 1.1 kPa, tan δ = 0.05 ± 0.004 (parallel-plate). The larger shear modulus measured by nanoindentation is due to the scale of testing. Whereas rheometry characterizes the bulk material response, nanoindentation probes the fibrous network of the gel. The procedure and analysis presented here are valuable for nanoindentation testing of other compliant materials such as hydrogels, soft biological tissue, and food products.

Room-temperature liquid metals, such as eutectic gallium–indium–tin (galinstan), dispersed in a polymer matrix present unique potential as conductors that may have minimal influence on the host polymer mechanical performance while providing enhanced electrical performance. Work described herein systematically evaluates the influence of uncured polydimethylsiloxane (PDMS) viscosity and galinstan loading on final dispersion viscosity and cured modulus. Dispersions of up to 80 vol% galinstan were obtained with relative permittivity values up to 170 that otherwise exhibited similar uncured rheological changes to a solid filler. Cured galinstan-in-PDMS dispersions, however, exhibited a reduced stiffness increase with respect to the host polymer relative to a solid filler. At a critical PDMS viscosity and metal, loading phase inversion to a conductive PDMS-in-metal dispersion was observed. It is anticipated that this work will enable the development of liquid metal polymer composites with independently controlled mechanical and electrical properties for a wide variety of stretchable electronic applications.

Fused deposition modeling (FDM) 3D printing is an additive manufacturing process capable of rapidly building three-dimensional computer-modeled objects. The technology offers an inexpensive and efficient technique to manufacture customized objects with intricate geometries using a simple printing process. However, FDM is currently restricted in application due to a limited availability of functional materials. Research in the field has focused on incorporating functional characteristics into printable polymers to expand application of FDM technology. In this work, neutron radiation shielding was targeted as an addition to FDM materials. By creating a composite material using a thermoplastic polymer matrix and boron nitride additive, neutron shielding of FDM-printed samples was enhanced from 50% attenuation in polymer specimens to 72% in composite specimens. The enhanced functionality of this new material enables FDM technology to be used in the manufacture of aerospace components, where neutron radiation presents a significant hazard.

In the emerging era of Internet of Things (IoT), power sources for wireless sensor nodes in conjunction with efficient and secure wireless data transfer are required. Energy harvesting technologies are promising solution toward meeting the requirements for sustainable power sources for the IoT. In this review, we focus on approaches for harvesting stray vibrations and magnetic field due to their abundance in the environment. Piezoelectric materials and piezoelectric–magnetostrictive [magnetoelectric (ME)] composites can be used to harvest vibration and magnetic field, respectively. Currently, such harvesters use modified lead zirconate titanate (or lead-based) piezoelectric materials and ME composites. However, environmental concerns and government regulations require the development of a suitable lead-free replacement for lead-based piezoelectric materials. In the past decade, several lead-free piezoelectric compositions have been developed and demonstrated with promising piezoelectric response. This paper reviews the significant results reported on lead-free piezoelectric materials with respect to high-density energy harvesting, covering novel processing techniques for improving the piezoelectric response and temperature stability. The review of the state-of-the-art studies on vibration and magnetic field harvesting is provided and the results are used to discuss various strategies for designing high-performance energy harvesting devices.