Structures and microwave dielectric properties of Ba6−3x(Nd,Biy)8+2xTi18O54 (x = 2/3) solid solution

Published online by Cambridge University Press:  31 January 2011

Yong Jun Wu  and
Xiang Ming Chen
Yong Jun Wu
Affiliation:
Institute of Materials Physics and Microstructures, Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China
Xiang Ming Chen*
Affiliation:
Institute of Materials Physics and Microstructures, Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China
*
a)Address all correspondence to this author.
Get access

Abstract

The effects of Bi substitution for Nd in Ba6−3xNd8+2xTi18O54 (x = 2/3) solid solution upon the microstructures and microwave dielectric properties were investigated. The solid solubility limit of Bi in Ba6−3xNd8+2xTi18O54 (x = 2/3) solid solution was about 15 mol%, the same as that for x = 0.5, and densification of the present solid solutions could be performed well at lower temperatures. However, the variation tendency of microwave dielectric properties with composition in the present ceramics quite differed from that for x = 0.5: (1) The temperature coefficient of resonant frequency in the present ceramics showed a continuous variation from positive to negative and did not indicate extreme value at the solid solubility limit. (2) Near-zero temperature coefficient of resonant frequency combined with high-ε and high-Qf values could be obtained in the present ceramics, while that for x = 0.5 had a lower limit of +15 ppm/°C. (3) The dielectric constant also showed a continuous increase for the present compositions, while that in x = 0.5 had an extreme at solid solubility limit. Ceramics with composition of Ba6−3x(Nd0.85,Bi0.15)8+2xTi18O54 (x = 2/3) showed excellent dielectric properties of ε = 99.1, Qf = 5290 GHz, and τf = −5.5 ppm/°C.

Type
Articles
Information
Journal of Materials Research , Volume 16 , Issue 6 , June 2001 , pp. 1734 - 1738
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Suvorov, D., Valant, M., and Kolar, D., J. Mater. Sci. 32, 6483 (1997).CrossRefGoogle Scholar
2.Kolar, D., Stadler, Z., Gaberscek, S., and Suvorov, D., Ber. Dt. Keram. Ges. 55(7), 346 (1978).Google Scholar
3.Valant, M., Suvorov, D., and Kolar, D., J. Mater. Res. 11(4), 928 (1996).CrossRefGoogle Scholar
4.Laffez, P., Desgardin, G., and Raveau, B., J. Mater. Sci. 30, 267 (1995).CrossRefGoogle Scholar
5.Webhofer, A. and Feltz, A., J. Mater. Sci. Lett. 18, 719 (1999).CrossRefGoogle Scholar
6.Ohsato, H., Imaeda, M., Takagi, Y., Komura, A., and Okuda, T., Proceeding of the Eleventh IEEE International Symposium on Applications of Ferroelectrics, August 24–27, 1998, Montreux, Switzerland (IEEE, Piscataway, NJ, 1998), Vol. 509.Google Scholar
7.Wu, Y.J. and Chen, X.M., J. Eur. Ceram. Soc. 19, 1123 (1999).CrossRefGoogle Scholar
8.Durand, J.M. and Boilot, J.P., J. Mater. Sci. Lett. 6, 134 (1987).CrossRefGoogle Scholar
9.Kolar, D., Gaberscec, S., Stadler, Z., and Suvorov, D., Ferroelectrics 27, 269 (1980).CrossRefGoogle Scholar
10.Kim, J.S., Cheon, C.I., Park, T-R., and Shim, H-S., J. Mater. Sci. 35, 1487 (2000).CrossRefGoogle Scholar
11.Hakki, B.W. and Coleman, P.D., IRE Trans. Microwave Theory Tech. 8, 402 (1960).CrossRefGoogle Scholar
12.Ohsato, H., Ohhashi, T., Kato, H., Nishigaki, S., and Okuda, T., Jpn.J. Appl. Phys. 34, 187 (1995).CrossRefGoogle Scholar
13.Nomura, S., Tomaya, K., and Kaneta, K., Jpn. J. Appl. Phys. 22, L624 (1982).CrossRefGoogle Scholar