Scandium on the formation of in situ TiB2 particulates in an aluminum matrix

Published online by Cambridge University Press:  28 June 2018

Dan Huang ,
David Yan ,
Siming Ma  and
Xiaoming Wang
Dan Huang
Affiliation:
School of Engineering Technology, Purdue University, West Lafayette, Indiana 47906, USA
David Yan
Affiliation:
Department of Aviation and Technology, San Jose State University, San Jose, California 95192, USA
Siming Ma
Affiliation:
School of Engineering Technology, Purdue University, West Lafayette, Indiana 47906, USA
Xiaoming Wang*
Affiliation:
School of Engineering Technology, Purdue University, West Lafayette, Indiana 47906, USA
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

TiB2 particulates were formed in situ in an aluminum matrix via chemical reactions between an aluminum melt and the mixture of K2TiF6 and KBF4 salts. Different effects of Sc addition on the formation of the TiB2 particulates were revealed depending on the participation of Sc at different stages of the formation of the particulates. The metal–salt reactions resulted in boride layers along the α-Al grain boundaries in the presence of Sc, while the addition of Sc after the metal–salt reactions broke up the boride layers improving the dispersion of the TiB2 particulates to a limited degree. Sc promoted the growth of the TiB2 particulates, resulting in the coarsening of TiB2 particulates. The participation of Sc in the formation of TiB2 particulates altered the coarsening of the TiB2 particulates, resulting in different morphologies of the TiB2 particulates depending on the participation of Sc in the formation of the TiB2 particulates at different stages.

Keywords

in situ TiB2aluminum alloyAl–Ti–Bmetal matrix compositeAl–Sc alloy
Type
Article
Information
Journal of Materials Research , Volume 33 , Issue 18 , 28 September 2018 , pp. 2721 - 2727
Copyright
Copyright © Materials Research Society 2018 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Tjiong, S.C. and Ma, Z.Y.: Microstructural and mechanical characteristics of in situ metal matric composites. Mater. Sci. Eng., R 29, 49 (2000).CrossRefGoogle Scholar
Lloyd, D.J.: Particulate reinforced aluminium and magnesium matrix composites. Int. Mater. Rev. 39, 1 (1994).CrossRefGoogle Scholar
Prasad, S.V. and Asthana, R.: Aluminum metal-matrix composites for automotive application: Tribological considerations. Tribol. Lett. 17, 445 (2004).CrossRefGoogle Scholar
Ibrahim, I.A. and Mohamed, F.A.: Particulate reinforced metal matrix composites—A review. J. Mater. Sci. 26, 1137 (1991).CrossRefGoogle Scholar
Arnberg, L., Bäckerud, L., and Klang, H.: Intermetallic particulates in Al–Ti–B-type master alloys for grain refinement of aluminium. Met. Technol. 9, 7 (1982).CrossRefGoogle Scholar
Jones, G.P. and Pearson, J.: Factors affecting the grain-refinement of aluminum using titanium and boron additives. Metall. Trans. B 7, 223 (1976).CrossRefGoogle Scholar
Wang, X., Song, J., Vian, W., Ma, H., and Han, Q.: The interface of TiB2 and Al3Ti in molten aluminum. Metall. Mater. Trans. B 47, 3285 (2016).CrossRefGoogle Scholar
Guzowski, M.M., Sigworth, G.K., and Sentner, D.A.: The role of boron in the grain. Metall. Trans. A 18, 603 (1987).CrossRefGoogle Scholar
McCartney, D.G.: Grain refining of aluminium and its alloys using inoculants. Int. Mater. Rev. 34, 247 (1989).CrossRefGoogle Scholar
Wang, X., Brydson, R., Jha, A., and Ellis, J.: Microstructural analysis of Al alloys dispersed with TiB2 particulate for MMC application. J. Microsc. 196, 137 (1999).CrossRefGoogle Scholar
Ramesh, C.S., Pramod, S., and Keshavamurthy, R.: A study on microstructure and mechanical properties of Al6061-TiB2 in situ composites. Mater. Sci. Eng., A 528, 4152 (2011).CrossRefGoogle Scholar
Wang, X. and Han, Q.: Relationship of diboride phases in Al–Ti(Zr)–B alloys. Mater. Sci. Technol. 31, 874 (2015).CrossRefGoogle Scholar
Fjellstedt, J. and Jarfors, A.: On the precipitation of TiB2 in aluminum melts from the reaction with KBF4 and K2TiF6. Mater. Sci. Eng., A 413–414, 527 (2005).CrossRefGoogle Scholar
Suresh, S., Shenbaga, N., and Moorthi, V.: Aluminium–titanium diboride (Al–TiB2) metal matrix composites: Challenges and opportunities. Procedia Eng. 38, 89 (2012).CrossRefGoogle Scholar
Zhang, Q., Wu, G., Chen, G., Jiang, L., and Luan, B.: The thermal expansion and mechanical properties of high reinforcement content SiCp/Al composites fabricated by squeeze casting technology. Composites, Part A 34, 1023 (2003).CrossRefGoogle Scholar
Liu, Z., Rakita, M., Xu, W., Wang, X., and Han, Q.: Ultrasound assisted salts-metal reaction for synthesizing TiB2 particulates at low temperature. Chem. Eng. J. 263, 317 (2015).CrossRefGoogle Scholar
Mortensen, A. and Jin, I.: Solidification processing of metal matrix composites. Int. Mater. Rev. 37, 101 (1992).CrossRefGoogle Scholar
Davies, P., Kellie, J.L.F., and Wood, J.V.: Development of cast aluminum metal matrix composites. Key Eng. Mater. 77–78, 357 (1992).CrossRefGoogle Scholar
Kennedy, A., Karantzalis, A., and Wyatt, S.: The microstructure and mechanical properties of TiC and TiB2-reinforced cast metal matrix composites. J. Mater. Sci. 4, 933 (1999).CrossRefGoogle Scholar
Wood, J.V., Davies, P., and Kellie, J.L.F.: Properties of reactively cast aluminium–TiB2 alloys. Mater. Sci. Technol. 9, 833 (1993).CrossRefGoogle Scholar
Birol, Y.: An improved practice to manufacture Al–Ti–B master alloys by reacting halide salts with molten aluminium. J. Alloys Compd. 420, 71 (2006).CrossRefGoogle Scholar
Birol, Y.: Improved halide salt process to produce Al–B master alloys. Mater. Sci. Technol. 12, 1846 (2011).CrossRefGoogle Scholar
Wang, X.: The formation of AlB2 in an Al–B master alloy. J. Alloys Compd. 403, 283 (2005).CrossRefGoogle Scholar
Wang, X.: Boride phase formation in the production of Al–B master alloys. J. Alloys Compd. 722, 302 (2017).CrossRefGoogle Scholar
Wang, X., Liu, Z., Dai, W., and Han, Q.: On the understanding of aluminum grain refinement by Al–Ti–B type master alloys. Metall. Mater. Trans. B 46, 1620 (2015).CrossRefGoogle Scholar
Moldovan, P., Butu, M., Popescu, G., Buzatu, M., Usurelu, E., Soare, V., and Mitrica, D.: Thermodynamics of interactions in Al–K2TiF6–KBF4 system. Rev. Chim. (Bucharest, Rom.) 9, 828 (2010).Google Scholar
Tjong, S.C., Wang, G.S., and Mai, Y.W.: High cycle fatigue response of in situ Al-based composites containing TiB2 and Al2O3 submicron particulates. Compos. Sci. Technol. 65, 1537 (2005).CrossRefGoogle Scholar
Agrawal, S., Ghose, A., and Chakrabarty, I.: Effect of rotary electromagnetic stirring during solidification of in situ Al–TiB2 composites. Mater. Des. 113, 195 (2017).CrossRefGoogle Scholar
Chen, F., Chen, Z., Mao, F., Wang, T., and Cao, Z.: TiB2 reinforced aluminum based in situ composites fabricated by stir casting. Mater. Sci. Eng., A 625, 357 (2015).CrossRefGoogle Scholar
Herbert, M.A., Maiti, R., Mitra, R., and Chakraborty, M.: Wear behaviour of cast and mushy state rolled Al–4.5Cu alloy and in situ Al4.5Cu–5TiB2 composite. Wear 265, 1606 (2008).CrossRefGoogle Scholar
Kumar, S., Chakraborty, M., Subramanya Sarma, V., and Murty, B.S.: Tensile and wear behaviour of in situ Al–7Si/TiB2 particulate composites. Wear 265, 134 (2008).CrossRefGoogle Scholar
Mandal, A., Maiti, R., Chakraborty, M., and Murty, B.S.: Effect of TiB2 particulates on aging response of Al–4Cu alloy. Mater. Sci. Eng., A 386, 296 (2004).CrossRefGoogle Scholar
Taghiabadi, R., Mahmoudi, M., Emamy Ghomy, M., and Campbell, J.: Effect of casting techniques on tensile properties of cast aluminium alloy (Al–Si–Mg) and TiB2 containing metal matrix composite. Mater. Sci. Technol. 19, 497 (2003).CrossRefGoogle Scholar
Birol, Y.: Effect of silicon content in grain refining hypoeutectic Al–Si founday alloys with boron and titanium additions. Mater. Sci. Technol. 28, 385 (2012).CrossRefGoogle Scholar
Spittle, J.A., Keeble, J.M., and Meshhedani, M.A.: The grain refinement of Al–Si foundry alloy. Light Met., 795 (1997).Google Scholar
Liu, X., Liu, Y., Huang, D., Han, Q., and Wang, X.: Tailoring in situ TiB2 particulates in aluminum matrix composites. Mater. Sci. Eng., A 705, 55 (2017).CrossRefGoogle Scholar
Røyse, J. and Ryum, N.: Scandium in aluminium alloys. Int. Mater. Rev. 50, 19 (2005).CrossRefGoogle Scholar
Pramod, S.L., Prasada Rao, A.K., Murty, B.S., and Bakshi, S.R.: Effect of Sc addition on the microstructure and wear properties of A356 alloy and A356-TiB2 in situ composite. Mater. Des. 78, 85 (2015).CrossRefGoogle Scholar
Fjellstedt, J., Jarfors, A., and Svendsen, L.: Experimental analysis of the intermediary phase AlB2, AlB12, and TiB2 in the Al–B and Al–Ti–B systems. J. Alloys Compd. 283, 192 (1999).CrossRefGoogle Scholar
Arnberg, L., Backerud, L., and Klang, H.: 1: Production and properties of master alloys of Al–Ti–B type and their ability to grain refine aluminum. Cosmet. Technol. 9, 1 (1982).Google Scholar
Quested, T.E.: Understanding mechanism of grain refinement of aluminium alloy by inoculation. Mater. Sci. Technol. 20, 1357 (2004).CrossRefGoogle Scholar
Maxwell, I. and Hellawell, A.: The constitution and aolidification of peritectic alloys in the system Al–Ti. Acta Metall. Mater. 23, 895 (1975).CrossRefGoogle Scholar
Maxwell, I. and Hellawell, A.: An analysis of the peritectic reaction with particular reference to Al–Ti alloys. Acta Metall. Mater. 23, 901 (1975).CrossRefGoogle Scholar
Abdel-Hamid, A.A., Hamar-Thibault, S., and Hamar, R.: Crystal morphology of the compound TiB2. J. Cryst. Growth 71, 744 (1985).CrossRefGoogle Scholar