Measurement of residual stress by load and depth sensing indentation with spherical indenters

Published online by Cambridge University Press:  31 January 2011

J. G. Swadener ,
B. Taljat  and
G.M. Pharr
J. G. Swadener
Affiliation:
Oak Ridge National Laboratory, Metals and Ceramics Division, P.O. Box 2008, MS-6093, Oak Ridge, Tennessee 37831–6093, and the University of Tennessee, Department of Materials Science and Engineering, Knoxville,Tennessee 37996–2200
B. Taljat
Affiliation:
STEEL Group 31054 Motto di Livenza, Travois, Italy, and Faculty of Mechanical Engineering, University of Ljubljana, Slovenia
G.M. Pharr
Affiliation:
Oak Ridge National Laboratory, Metals and Ceramics Division, P.O. Box 2008, MS-6093, Oak Ridge, Tennessee 37831–6093, and the University of Tennessee, Department of Materials Science and Engineering, Knoxville, Tennessee 37996–2200
Get access

Abstract

A new experimental technique is presented for making measurements of biaxial residual stress using load and depth sensing indentation (nanoindentation). The technique is based on spherical indentation, which, in certain deformation regimes, can be much more sensitive to residual stress than indentation with sharp pyramidal indenters like the Berkovich. Two different methods of analysis were developed: one requiring an independent measure of the material's yield strength and the other a reference specimen in the unstressed state or other known reference condition. Experiments conducted on aluminum alloys to which controlled biaxial bending stresses were applied showed that the methods are capable of measuring the residual stress to within 10–20% of the specimen yield stress. Because the methods do not require imaging of the hardness impressions, they are potentially useful for making localized measurements of residual stress, as in thin films or small volumes, or for characterization of point-to-point spatial variations of the surface stress.

Type
Articles
Information
Journal of Materials Research , Volume 16 , Issue 7 , July 2001 , pp. 2091 - 2102
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Kokubo, S., Science Reports of the Tohoku Imperial University 21, 256 (1932).Google Scholar
2.Kostron, H., Technisches Versuchsant Mitteilungen January, 17 (1932).Google Scholar
3.Kostron, H., Metallwirtschaft 12, 473 (1933).Google Scholar
4.Sines, G. and Carlson, R., ASTM Bulletin 180, 35 (1952).Google Scholar
5.Blain, P.A., Sheet Metal Ind. 26, 135 (1949).Google Scholar
6.Blain, P.A., Metal. Progress, 99 (1957).Google Scholar
7.Alamen, J.O., Prod. Eng., 121 (1950).Google Scholar
8.Oppel, G.U., Exp. Mech. 21, 135 (1964).CrossRefGoogle Scholar
9.Simes, T.R., Mellor, S.G., and Hills, D.A., J. Strain Anal. 19, 135 (1984).CrossRefGoogle Scholar
10.Vitovec, F.H., in Microindentation Techniques in Materials Science and Engineering, edited by Blau, P.J. and Lawn, B.R. (AST. 889, Philadelphia, PA, 1986), p. 175.Google Scholar
11.LaFontain, W.R., Yost, B., and Li, C-Y., J. Mater. Res. 5, 776 (1990).CrossRefGoogle Scholar
12.Doerner, M.F., Gardner, D.S., and Nix, W.D., J. Mater. Res. 1, 845 (1986).CrossRefGoogle Scholar
13.Tsui, T.Y., Oliver, W.C., and Pharr, G.M., J. Mater. Res. 11, 752 (1996).CrossRefGoogle Scholar
14.Bolshakov, A., Oliver, W.C., and Pharr, G.M., J. Mater. Res. 11, 760 (1996).CrossRefGoogle Scholar
15.Bolshakov, A. and Pharr, G.M., J. Mater. Res. 13, 1049 (1998).CrossRefGoogle Scholar
16.Suresh, S. and Giannakopoulos, A.E., Acta Mater. 46, 5755 (1998).CrossRefGoogle Scholar
17.Taljat, B. and Pharr, G.M., in Thin Films: Stresses and Mechanical Properties VIII, edited by Vinci, R., Kraft, O., Moody, N., and Shaffer II, E. (Mater. Res. Soc. Symp. Proc. 594, Warrendale, PA, 2000), p. 519.Google Scholar
18.Johnson, K.L., J. Mech. Phys. Solids 18, 115 (1970).CrossRefGoogle Scholar
19.Johnson, K.L., Contact Mechanics (Cambridge University Press, Cambridge, United Kingdom, 1985).CrossRefGoogle Scholar
20.Hertz, H., Miscellaneous Papers, edited by Jones, D.E. and Schott, G.H. (Macmillan, London, 1896), p. 163.Google Scholar
21.Tabor, D., The Hardness of Metals (Clarendon Press, Oxford, United Kingdom, 1951).Google Scholar
22.Francis, H.A., J. Eng. Mater. Technol. 98, 272 (1976).CrossRefGoogle Scholar
23.Tirupataiah, Y. and Sundararajan, G., Metall. Trans. A 22A, 2375 (1991).CrossRefGoogle Scholar
24.The Aluminum Association, Aluminum Standards and Data (The Aluminum Association, New York, 1968), p. 28.Google Scholar
25.Swadener, J.G. and Pharr, G.M., in Thin Films: Stresses and Mechanical Properties VII, edited by Vinci, R., Kraft, O., Moody, N., and Shaffer VIII, E. (Mater. Res. Soc. Symp. Proc. 594, Warrendale, PA, 2000), p. 525.Google Scholar
26.Swadener, J.G. and Pharr, G.M., Philos. Mag. A 81, 447 (2001).CrossRefGoogle Scholar
27.Field, J.S. and Swain, M.V., J. Mater. Res. 8, 297 (1993).CrossRefGoogle Scholar
28.Oliver, W.C. and Pharr, G.M., J. Mater. Res. 7, 1564 (1992).CrossRefGoogle Scholar
29.Mroz, Z. (private communication, Chicago, IL, August 31, 2000).Google Scholar
30.Norbury, A.L. and Samuel, T., J. Iron Steel Inst. 117, 673 (1928).Google Scholar
31.Taljat, B., Zacharia, T., and Pharr, G.M. in Fundamentals of Nanoindentation and Nanotribology, edited by Moody, N.R., Gerberich, W.W., Burnham, N., and Baker, S.P. (Mater. Res. Soc. Symp. Proc. 522, Warrendale, PA, 1998), p. 33.Google Scholar