Annealing effect on in-plane alignment and surface morphology of epitaxial Bi4Ti3O12 thin films prepared by the chemical solution deposition

Published online by Cambridge University Press:  31 January 2011

K. Hwang  and
Y. Park
K. Hwang
Affiliation:
School of Automotive & Mechanical Engineering, Nambu University, 864–1 Wolgye-dong, Kwangsan-gu, Kwangju 506–302, Republic of Korea
Y. Park
Affiliation:
Department of Dental Materials & Dental Materials Research Institute, School of Dentistry, Chonnam National University, 5 Hak 1 dong, Dong-gu, Kwangju 501–190, Republic of Korea
Get access

Abstract

Bi4Ti3O12 thin films were grown epitaxially on SrTiO3(100) substrates by chemical solution deposition using metal naphthenates as starting materials. Homogeneous Bi–Ti solution with toluene was spin-coated onto the substrates and pyrolyzed at 500 °C for 10 min in air. Highly c-axis-oriented Bi4Ti3O12 thin films were crystallized by annealing pyrolyzed films at ≥650 °C. The x-ray pole-figure analysis indicated that the Bi4Ti3O12 thin films have an epitaxial relationship with the SrTiO3(100) substrates. The surface morphology of the films annealed at lower temperature, i.e., 650 °C, exhibited flat and smooth surfaces, while films annealed at higher temperatures, i.e., 750 and 800 °C, were characterized by three-dimensional outgrowth.

Type
Articles
Information
Journal of Materials Research , Volume 16 , Issue 9 , September 2001 , pp. 2519 - 2525
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1Dorrian, J.F., Newnham, R.E., Smith, D.K., and Kay, M.I., Ferro-elecrics 3, 17 (1971).Google Scholar
2Cummins, S.E. and Cross, L.E., J. Appl. Phys. 39, 2268 (1968).CrossRefGoogle Scholar
3Parks, B.H., Hyun, S.J., Moon, C.R., Choe, B.D., Lee, J., Kim, C.Y., Jo, W., and Noh, T.W., J. Appl. Phys. 84, 4428 (1998).Google Scholar
4Alexe, M., Scott, J.F., Curran, C., Zakharov, N.D., Hesse, D., and Pignolet, A., Appl. Phys. Lett. 73, 1592 (1998).CrossRefGoogle Scholar
5Alexe, M., Gruverman, A., Harnagea, C., Zakharov, N.D., Pignolet, A., Hesse, D., and Scott, J.F., Appl. Phys. Lett. 75, 1158 (1999).CrossRefGoogle Scholar
6Nakamura, T., Muhammet, R., Shimizu, M., and Shiosaki, T., Jpn. J. Appl. Phys. 32, 4086 (1993).Google Scholar
7Jo, W., Kim, K.H., and Noh, T.W., Appl. Phys. Lett. 66, 3120 (1995).Google Scholar
8Choopun, S., Matsumoto, T., and Kawai, T., Appl. Phys. Lett. 67, 1072 (1995).CrossRefGoogle Scholar
9Gu, H., Bao, D., Wang, S., Gao, D., Kuang, A., and Li, X., Thin Solid Films 81, 283 (1996).Google Scholar
10Hwang, K.S., Kim, B.H., Manabe, T., Yamaguchi, I., Kumagai, T., and Mizuta, S., Jpn. J. Appl. Phys. 38, 219 (1999).Google Scholar
11NanoScope Command Reference Manual, Ver. 4.42 (Digital In-struments, Inc., Santa Barbara, CA, 1999), pp. 12.19–12.45.Google Scholar
12Subbarao, E.C., Phys. Rev. 122, 804 (1961).CrossRefGoogle Scholar
13Hamada, M., Tabata, H., and Kawai, T., Jpn. J. Appl. Phys. 37, 5174 (1998).CrossRefGoogle Scholar