This study examines the origin and distribution of clay minerals of the pedological horizons of Kori Ouallam watershed (south-western Niger). It is based on field sampling campaigns and a series of laboratory analyses. A total of 49 samples were analysed, 28 from surface horizons (0–10 cm depth) and 21 from pedological profiles (0–1 m depth). The samples were analysed by X-ray diffraction on bulk and clay (<2 μm) fractions, X-ray fluorescence spectrometry, laser granulometry, organic matter and calcium carbonate content, macroscopic observations (binocular loupe) and scanning electron microscopy equipped with an energy-dispersive spectrometry system. The pedological horizons are characterized by low organic matter contents (<1%) and no calcium carbonate. The particle-size distribution shows net textural differentiation, with a predominance of sandy loam to sandy clay loam textures in the upper horizons and clay loam to clay in the deep horizons. The main major oxides were SiO2 (46.3–89.0%), Al2O3 (5.0–24.2%) and Fe2O3 (1.0–27.9%). Kaolinite (64–98%) is the predominant clay mineral at all horizons, associated with low to moderate proportions of illite (1–34%) and traces of chlorite. Kaolinite is essentially inherited from the parent rock, whereas illite results from chemical alteration by bisialitization of the primary minerals initially rich in potassium feldspar contained in the parent rock. However, soil texture and organic matter vary independently with clay mineralogy. An extended study of all of the pedological facies that make up south-western Niger, combined with supplementary analyses, would further improve our understanding of clay mineralogy in the Sahelian zone.

The rheological properties of three Na-activated, trioctahedral Mg-bentonites (hectorite clay from the CMS Source Clay Project repository, saponite clay from Spain and stevensite clay from Rhassoul, Morocco) and a sepiolite clay from Greece were examined after dynamic ageing at temperatures up to 230°C. The 5% w/v suspensions were prepared by dispersing the clay mineral samples in distilled water. The suspensions underwent dynamic, thermal ageing for 16 h before determination of the viscosity, filtration loss, filter cake thickness and pH and the concentration of dissolved Na+ and Mg2+. Thermal ageing contributed to the dispersion of clay particles, with a direct effect on plastic and apparent viscosity, introducing pseudoplastic behaviour. With the exception of the stevensite clay at 230°C that displayed limited dissolution at 230°C and partial conversion to kerolite, the clays were stable at high temperatures. The Na-activation of all clays except for stevensite was not adversely affected by thermal ageing. Thermal ageing of stevensite at 230°C facilitated Na exchange and yielded suspension with high viscosity and low filtrate loss. Only the suspensions of hectorite and those of stevensite aged at 230°C met with American Petroleum Institute specifications. The thermal behaviour and rheological properties of the clays might be interpreted according to the intrinsic properties of the clay minerals, such as layer charge and charge distribution.

In the present study, a comparison of the thermal-insulation and mechanical performances of cement and heat-stabilized compressed earthen blocks (CEBs) was carried out to determine the factors which influence those properties. The raw clays used consist mainly of kaolinite, orthoclase and quartz. The mechanical strength increased with increase in both the amount of cement added and the firing temperature. However, the responses are better for cement-stabilized CEBs. The thermal insulation of fired bricks is greater than that of cement-stabilized bricks. This difference was related to the decrease in porosity and the formation of continuous-surface. The decrease in thermal insulation is mainly related to the formation of continuous-surface in cement-stabilized CEBs, whereas in the fired CEBs, it is due to the modification of pore volume. The mineralogy of the raw clays is statistically correlated to porosity and continuous-surface development that were confirmed as the main factors in the modification of both the mechanical strength and the thermal insulation. In cement-stabilization, the decrease in insulation is due to the development of continuous surface, while for heat-stabilization, mineral transformations during the sintering reduced continuous-surface formation and the insulation was controlled by both radiation and reduced surface conduction. The influence of the mineralogy of the raw material shows that clay content favours the insulation in fired bricks obtained at T ≤ 1000°C, while sand contents favour densification. In contrast, clay contents reduce the mechanical response of cement-stabilized material due to limited cement–clay interactions. In general, the mechanical response is more favourable in cement stabilization, while thermal insulation is better in fired bricks.

Nine halloysite nanotubes (HNTs) have been examined using scanning electron microscopy (SEM), atomic force microscopy (AFM) and (cross-sectional) transmission electron microscopy (TEM) to evaluate details of their external and internal morphologies. The samples span morphologies within the cylindrical to prismatic-polygonal framework proposed by Hillier et al. (2016). The ‘carpet roll’ model assumed in the conceptualization of most technological applications of HNTs is shown to be far too simplistic. Both cylindrical and prismatic forms have abundant edge steps traversing their surfaces that, by analogy with plates of kaolinite, correspond to prism faces. The mean value for the diameter of the central lumen of the tubes is 12 nm. Numerous slit-like nanopores, with diameters up to 18 nm, also occur between packets of layers, particularly in prismatic forms at the junction between a central cylindrical core and outer packets of planar layers. These pores expose aluminol and siloxane surfaces, but unlike the lumen, which is assumed only to expose an aluminol surface, they do not extend along the entire length of the nanotube. Edge steps seen most clearly by AFM correspond in height to the packets of layers seen in TEM. TEM cross-sections suggest that tube growth occurs by accretion of a spiralled thickening wedge of layers evolving from cylindrical to polygonal form and reveal that planar sectors may be joined by either abrupt angular junctions or by short sections of curved layers. A more realistic model of the internal and external morphologies of HNTs is proposed to assist with understanding of the behaviour of HNTs in technological applications.

Natural tuff samples in western Anatolia (Türkiye) originating from Miocene rhyolitic–pyroclastic rocks with >80 wt.% heulandite/clinoptilolite zeolites were investigated for their surface characteristics determined according to nitrogen adsorption after degassing at 150°C (specific surface area, pore volume and pore diameter). Additionally, these surface characteristics were correlated with the cationic compositions of the heulandite/clinoptilolite group minerals. The examined samples were characterized by two main pore diameters that were not related to specific surface area and pore volume but were partially related to the types and occupancy of extra-framework cations. One set of samples has a pore diameter of ~24 Å, total cation content (Na + K + Ca + Mg) ranging from 3.46 to 4.40 and a (Na + K)/(Ca + Mg) ratio ranging from 0.34 to 0.92. The total cation contents and (Na + K)/(Ca + Mg) ratios of the remaining samples with a pore diameter of ~37 Å are 4.30–5.08 and 1.48–2.85, respectively. After degassing at 300°C, there is a slight difference in the pore diameters of these two sets of samples (~37 and 38 Å). The pore sizes of the samples with a (Na + K)/(Ca + Mg) ratio < 1 (heulandite composition) increased from 24 to 36–38 Å with increasing degassing temperature, whereas the pore sizes of the samples with a (Na + K)/(Ca + Mg) ratio > 1 (clinoptilolite composition) increased from 37 to only 38–39 Å. However, there is no correlation between the Si/Al ratios and the cation-exchange capacities of the samples and their surface characteristics obtained by degassing at the two temperatures.

Three clay materials (codded MY3, KG and KK) from western Cameroon were selected and investigated for the production of refractory bricks. Samples MY3 and KG are kaolinite-rich materials, having clay mineral contents of 88% and 72%, respectively, whereas KK is a sand-rich material with a total clay content of 44%. Chamottes were prepared using each clay, and the ground chamottes were later used in the refractory formulation, with each raw clay used as a binding phase. After firing, the X-ray diffraction analyses of all of the refractory bricks indicated the same mineral assemblage made of quartz, cristobalite and mullite. The cristobalite is due to high-temperature conversion of quartz, whereas the mullite is due to clay mineral conversion. The evaluation of the linear shrinkage, physical properties (including bulk density and open porosity) and mechanical testing through refractoriness under load and compressive strength indicates that all of these clays could be used as raw materials for standard clay refractory materials. These results stand as a proof for the potential for these locally available materials to be used as raw materials for refractories that could be locally produced to reduce the cost of access to refractory raw materials faced by industries located in Cameroon.

The retreat of the Dead Sea and the lowering of the base level in recent decades have led to the exposure of the littoral clay sediments on the shore, the occurrence of exposed mudflats and the development of ground subsidence along strips (‘subsidence strips’) and clustered sinkholes. Based on field observations and laboratory analyses, the present study characterizes the clayey sediments in the environment of the exposed mudflats on the western Dead Sea shore. The clayey sediments of the exposed mudflats (‘mudflat sediments’) consist of fine-grained laminated calcareous clays. The mineral composition of the bulk mudflat sediments consists of clay and carbonate minerals (calcite, aragonite and dolomite) with some quartz and feldspar, and frequently gypsum and halite. The clay mineral composition of these samples is smectitic illite–smectite and kaolinite with some discrete illite and palygorskite. The smectitic illite–smectite is randomly interstratified (1.7 nm illite–smectite type R = 0). Although the detrital smectitic illite–smectite in the mudflat sediments is situated in the saline environment of the Dead Sea shore, no significant illitization is observed in the depositional detrital clay. Subsidence strips with clustered sinkholes were formed in the exposed mudflats as part of the adjustment of the Dead Sea periphery to the lowering of the base level as a result of the retreat. The field observations in the studied area reveal that the subsiding of mudflat sediments in the formation of the subsidence strips usually involves mud sagging of wet clayey sediments in the subsurface and sediment collapse of dry clayey sediments near the surface.

Bentonites are proposed to be used as buffers in high-level radioactive waste repositories. The elevated temperatures in repositories may, however, affect bentonites’ desired properties. For instance, heating under dry conditions can cause cation fixation, potentially affecting swelling properties. The kinetics of mineral dissolution and precipitation reactions will equally be influenced by temperature. Redistributions of Ca-sulphates and -carbonates have been observed, as well as illitization of smectite. Illitization, however, has only been observed in laboratory experiments at large solution/solid ratios, whereas it has not yet been unambiguously identified in large-scale experiments. In many large-scale tests, cation exchange is the first observable geochemical reaction. In addition, an enrichment of Mg close to the heater is found in many such tests. The thermal gradient and (incongruent) smectite dissolution are suspected to play a role with respect to the Mg enrichment, but the underlying mechanism has not been unravelled so far. To predict the long-term performance of a bentonite buffer, numerical modelling is required in order to be able to simulate the reactions of all accompanying mineral phases. Smectites, which dominate the bentonite composition, are therefore particularly difficult to characterise, as their dissolution is often observed to be non-stoichiometric. Various model approaches exist to simulate smectite reactions, mostly based on kinetic rate reactions, ideally considering the effect of pH (congruent or incongruent dissolution), temperature and the degree of saturation of the solution. Reassessing and improving the thermodynamic/kinetic data of smectites are prerequisites for improving long-term buffer performance assessment.

Clay minerals are effective adsorbents used for the remediation of toxic heavy metals from wastewater due to their large surface areas and great cation-exchange capacities. In this study, the removal of lead ions from aqueous solutions via adsorption was investigated using raw and iron-modified Turkish sepiolite. The aim of this study was to examine the effects of modification and environmental conditions on the sorptive properties of sepiolite samples. Initially, the raw sepiolite (Sep) and magnetic sepiolite/Fe2O3 composite (MagSep) prepared using the co-precipitation method were characterized via mineralogical and petrographical means and the physicochemical properties were determined. Then, the batch adsorption of lead (Pb2+) ions on the sepiolite samples was examined under various conditions (solution pH, adsorbent dosage, contact time, initial Pb2+ ion concentration, temperature, shaking rate). The adsorption capacity of MagSep was found to be greater than that of Sep under all experimental conditions. The results showed that the adsorption process followed a pseudo-second-order kinetic model, and the Langmuir isotherm best correlated with the experimental data. The maximum adsorption capacities were found to be 60.6 and 90.1 mg g–1 for Sep and MagSep, respectively. The characterization of the Pb-adsorbed sepiolite samples showed that lead formed covalent bonds with the sepiolite samples and attached to the sepiolite surface mainly through ion exchange. MagSep can be used efficiently in the field of wastewater treatment for the removal of Pb2+ ions as it does not release any toxic pollutants and can be separated easily with the use of a magnetic field.

Over several decades, a wealth of literature has been devoted to correlations between the chemistries of phyllosilicates and their crystallographic unit-cell parameter values. The c parameter is currently used because of its relation to the layer-to-layer distance, characteristic of the various families of phyllosilicates. The b parameter is also of interest because it allows measurement of the layer lateral dimensions and inherent structural adjustments. This unit-cell distance can be extracted from X-ray diffraction traces from the (06ℓ;33ℓ) diffraction region and by attributing the main diffraction peak observed to a 060 reflection, leading to the relationship b = 6.d(060). The aim of this paper is to revisit the relationships between the b value (or equivalent) of the phyllosilicate (i.e. TO, TOT and TOTO) or hydroxide (i.e. hydroxide, oxyhydroxide and layered double hydroxide) families and the layer chemistry based on a mean ionic radius R of octahedral cations, calculated as $R = \mathop \sum \nolimits_{i = 1}^n ( {r_i.x_i} )$, where ri is the ionic radius of the octahedral cation i and xi is its molar fraction over n types of octahedral cations ($\mathop \sum \nolimits_{i = 1}^n ( {x_i} ) = 1$). The data were collected from the literature and involved both natural and synthetic samples with both dioctahedral and trioctahedral structures of the octahedral sheet. The results showed that b values can be linked strongly to R, leading to suitable linear regressions for all of the studied structures. All correlations were found to be applicable irrespective of the di- or trioctahedral nature of the octahedral sheet, and these are discussed in light of (1) the lateral dimension of the octahedral sheet and (2) the dimensional misfit between the tetrahedral and octahedral sheets. For hydroxide families, all data can be gathered on a single b vs R correlation line, and the dimensional properties of the octahedral sheet can be interpreted simply based on an oxygen–cation–oxygen mean distance. For TO structures, two general b vs R correlation trends were reported, and these were assigned to two adjustment mechanisms corresponding to distinct types of tetrahedral and octahedral distortions. For the mica TOT family, two main trends were also reported, whereas the use of the synthetic mica series allowed us to demonstrate that the obtained scattering of data was mainly driven by the presence of multiple limited solid solutions. Such chemical complexity was also noted for smectites, especially regarding the tetrahedral composition and associated variability in layer charge. This variability made it difficult to propose a general regression correlating b to R values for smectites, although the regression obtained for neutral TOT layers can apply as a first-order relation. Finally, a single general b vs R correlation was obtained for chlorites, and the observed slope of the regression was interpreted according to the role played by the isolated hydroxide sheet on the evolution of the lateral dimension of the structures.

In this study, stable and radioactive lead removal from aqueous solution by adsorption using bentonite, zeolite and perlite minerals obtained from various locations in Türkiye was studied in batch experiments. The adsorbents were first characterized using X-ray diffraction (XRD), X-ray fluorescence (XRF), Fourier-transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS), and then the physicochemical properties were determined. The effects of various factors that influence adsorption, such as solution pH, adsorbent dosage, contact time, initial Pb2+ ion concentration, temperature and shaking rate, were studied. The adsorption of Pb2+ was modelled using the Langmuir, Freundlich and Dubinin–Radushkevich isotherms. The adsorption capacities of the minerals for Pb2+ followed the order: bentonite > zeolite > perlite, and the maximum adsorption capacities were 131.6, 36.1 and 21.5 mg g–1, respectively. The adsorption data fit well with the Langmuir isotherm. The bonding of lead ions on the adsorbents was confirmed by XRF and FTIR analyses after the adsorption process. The adsorption of Pb2+ ions on the adsorbents was spontaneous and endothermic. The adsorption process took place by cation exchange in addition to electrostatic interaction. Furthermore, radioactive 210Pb2+ adsorption on bentonite, zeolite and perlite was studied, with the analyte being analysed using a liquid scintillation counter. It was seen that in addition to Pb(II) ions, these minerals also adsorbed the radioactive decay products of 210Pb, which were 210Po and 210Bi. The removal percentages of 210Pb were 95%, 38% and 30% and those of 210Po were 75%, 60% and 74% for bentonite, zeolite and perlite, respectively.

The Clay Minerals Group (CMG), the first of the Special Interest Groups of the Mineralogical Society of the UK and Ireland, was inaugurated in January 1947. The CMG, together with its Belgian equivalent (originally the Comité Belge pour l'Etude des Argiles, later the Belgian Clay Group, now defunct), formed the world's first organizations dedicated to clay mineral research. The CMG celebrated its 75th anniversary in 2022. The Group's aims are to stimulate interest in clay mineralogy, to facilitate an exchange of information between members by providing facilities for reading and discussing papers on research on clay minerals (and allied topics) and to expedite their publication and to encourage practical applications of such research, and these have remained reassuringly the same throughout its history. A founder and active member of both the European Clay Groups Association and the Association Internationale Pour L'Etude des Argiles, the CMG has promoted clay science through the publication of the highly regarded journal Clay Minerals and a series of influential book titles, organizing international and national scientific conferences and meetings, the George Brown Lecture series, providing bursaries and grants to assist researchers and hosting the Images of Clay archive. The initial and sustained success of the CMG has been largely due to the labours of many officers and committee members, some of whom have been recognized for their science and service with awards from the Mineralogical Society of the UK and Ireland and elsewhere. By maintaining this effort, the evident, continuing demand for clay mineral research to assist with changing societal needs should ensure the relevance and health of the CMG for the foreseeable future.

Clays have been used widely as sorbents of potentially toxic elements, especially Pb. However, their adsorption efficiency has been studied mostly under static experimental conditions, which are labour-intensive. In this study, dynamic adsorption experiments were established using micro-columns to assess the adsorption behaviour of natural Fe-Mg-rich clays for Pb ions by varying the inlet solution pH, Pb concentration and flow rate. The clays, consisting of varying amounts of palygorskite and Fe-smectite, were diluted with quartz (Qz) sand to enhance their permeability. Greater adsorption capacity was observed for the mixed palygorskite/Fe-smectite-rich clay beds (45.2 ± 0.01 mg g–1) followed by the Fe-smectite-rich (35.7 ± 0.07 mg g–1) and palygorskite-rich (20.0 ± 0.03 mg g–1) clay beds. The results indicated that the greater adsorption efficiency of palygorskite/Fe-smectite-rich clays could be attributed to synergistic effects due to the coexistence of palygorskite and Fe-smectite clay phases, which have distinct physicochemical characteristics. Moreover, the results obtained showed good agreement with the static experiments, implying that the use of micro-columns could describe adsorption adequately over shorter experimental times.

Samples from the pyrophyllite reserves in the Malatya–Pütürge region, used in the production of the whitest cement in Europe, were beneficiated using flotation. The mineralogical composition of the natural pyrophyllite, as determined using X-ray diffraction, includes pyrophyllite, kaolinite, quartz, illite–mica and feldspar. The chemical composition of pyrophyllite contains 69.75% SiO2 and 23.04% Al2O3. The pyrophyllite percentage (40–45 wt.%) of the natural sample increased to 60–80 wt.% after flotation. In flotation experiments, the effects of reagent amounts, types and their mixtures were investigated. Methyl isobutyl carbinol (MIBC) and pine oil as frothers and kerosene as a collector were used in the flotation studies. The use of reagents as mixtures has a positive effect on the beneficiation compared to use on their own. The best result was obtained for a mixture of MIBC with kerosene, which is a non-ionic hydrocarbon oil, yielding a concentrate containing 26.63% Al2O3. Improved results were also observed for kerosene plus frother mixtures after flotation cleaning circuits. The bubbles formed during flotation were photographed and the bubble diameters were measured using the ImageJ program. The Al2O3 content was evaluated by correlating the bubble diameters. In general, selectivity decreased during experiments in which bubble diameters were reduced.

Mineral reactions in soils demonstrably take place on a human timescale. The weathering of silicate ‘rock-forming’ minerals releases nutrients that are essential for plant growth, including silica. This process consumes CO2, which is ultimately derived from the atmosphere, through enhanced rock weathering. From a human perspective, the weathering process has two beneficial functions – crop nutrition and climate mitigation – through the removal of atmospheric CO2. By considering these as a coupled process, the release of silica during weathering can be matched to what is taken from the soil by a crop (e.g. wheat). A simple analysis shows that the amount of silica that accumulates in wheat during a 4 month growing period is readily released by the weathering of pyroxene and plagioclase, minerals that commonly occur in basaltic igneous rocks. In contrast, the dissolution rate for quartz is so low that it cannot supply the silica taken up by the crop and is inert. Similarly, dissolution of clay minerals releases sufficient silica for plant uptake. Rapid weathering of silicate minerals within soils is evident from images of surfaces of grains exposed in soils for periods of 10–100 years. The evidence for silicate rock weathering as part of the soil system that sustains humanity is provided by the vegetation that we see around us.

This paper reports a novel approach in the study of trace-element mobility during the argillization of volcanic glass that is based on in situ laser ablation inductively coupled plasma mass spectrometry glass analyses and that of spatially related illite-smectite collected in the form of fraction separates. The material studied originates from lacustrine sediments of the Dinaride Lake System that bear evidence of intensive weathering of distal tephra during the Miocene climatic optimum. Yttrium and HREE were probably mobilized from decomposing glass in the form of carbonate complexes and were consequently depleted significantly in the clays studied. On the other hand, the Mg-rich illite-smectite demonstrates an elevated adsorption potential of solvated LREE complexes. This may be explained through clay surface geochemistry controlled largely by Mg for Al octahedral substitution. This paper highlights the role of eogenetic 2:1 clay aluminosilicates that, under favourable geological conditions, may be conducive to secondary REE enrichment and the formation of potential ion adsorption-type deposits.

Sediments from the ST5 deep-sea bottom core collected from the south-east Aegean Sea between Symi and Tilos islands, Greece, were examined by quantitative mineralogical analysis and geochemical analysis to infer provenance and palaeoenvironmental control over sediment deposition. The mineralogical composition comprises carbonates (mainly calcite and Mg-calcite), quartz, feldspars, serpentine, amphibole and clay minerals. Chlorite is the most abundant clay mineral, whereas smectite and illite are less abundant than in the sediments in the south-west Aegean and the Cretan Sea. Semi-quantitative analysis of clay minerals from oriented clay fractions overestimates significantly the smectite content and underestimates the abundances of illite, chlorite and kaolinite. The studied sediments are enriched in MgO, Ni and Cr, which decrease in abundance with decreasing depth, following the distribution of serpentine. By contrast, the abundances of SiO2, Al2O3, Fe2O3, Na2O and K2O increase upcore. The regional S1 sapropel horizon is enriched in V and Co and has considerably greater Ba/Al ratios than the remaining sequence. The mineralogical and geochemical relationships indicate a strong ultrabasic influence, probably from the Marmaris ophiolite in the Lycian nappes. The clay mineral distribution suggests that the smectite was mainly of volcanogenic origin, the illite was supplied by the nearby landmasses of west Anatolia and the islands of Rhodes, Tilos and Symi and the contribution from the south-east Mediterranean was limited or totally lacking. The combined use of the mineralogical and geochemical analysis of bulk sediments rather than the clay fractions is not only extremely useful in tracing sediment provenance in relatively closed basins, but it also enables a more realistic assessment of the importance of water circulation patterns on sedimentation processes in such environments.

Acid activation was carried out by heating muds prepared from Ca-rich bentonite (CaB), sulfuric acid (H2SO4) and distilled water, yielding various bleaching earths (BEs). The roles of each of the process variables, namely mass fraction of H2SO4 (x) in the dried CaB and pure H2SO4 mixture, heating temperature (T) and contact time (t), in the activation were tested. The raw CaB and each BE were examined with X-ray diffraction, chemical analyses, N2 adsorption/desorption, pH-metry and tintometry. The BE contents in both the aqueous and oily suspensions were set to 2% by mass in order to measure the pH value and the bleaching power, respectively. The optimum conditions for the activation to obtain a BE having the same bleaching power (0.60) as Tonsil® Optimum Bleaching Earth for soybean oil were determined as x = 0.35, T = 100°C and t = 2 h. The bleaching power increased only marginally upon increasing the activation time from 2 h up to 10 h at a given x and T. After 10 h, significant changes did not take place in the bleaching power of the BE. The mass fraction of total structural metal oxide (y), pH value, specific pore volume (V), specific surface area (S) and mean internal diameter (D) of the mesopores for the optimized BE are y = 0.10, pH = 3.0, V = 0.31 cm3 g–1, S = 225 m2 g–1 and D = 7 nm. The pH and D values were more important for bleaching the alkaline refined soybean oil compared to the other parameters tested.

The objective of this work was to use air-dried sepiolite granules as an additive in cigarette filter tips to increase the removal yield of tar and nicotine from mainstream smoke. Granules with a mass of 95 mg per cigarette filter and a mean particle size (D) of 0.05–0.41 mm were used to constrain the effects of the mean particle size and mass of sepiolite in the removal process. The granules were sandwiched in common cellulose acetate filter tips. Maximum removal yields of 90% were obtained when D ≤ 0.10 mm. Filters containing granules with a mean size of 0.10 mm and mass variations from 35 to 95 mg were tested, and increasing amounts of sepiolite added led to progressively greater yields of tar and nicotine from 20% to 90%. The sepiolite granules were examined using scanning electron microscopy with energy-dispersive X-ray spectroscopy, Fourier-transform infrared spectroscopy and X-ray diffraction techniques both before and after smoke experimentation. It is suggested that tar and nicotine were condensed both on the fibre clusters of the sepiolite granules and in the voids between them during the flow of the mainstream smoke.