Two crystals of the uranyl carbonate mineral grimselite, ideally K3Na[(UO2)(CO3)3](H2O), from Jáchymov in the Czech Republic were studied by single-crystal X-ray diffraction and electron-probe microanalysis. One crystal has considerably more Na than the ideal chemical composition due to substitution of Na into KO8 polyhedra; the composition of the other crystal is nearer to ideal, and similar to synthetic grimselite. The presence of Na atoms in KO8 polyhedra, which are located in channels in the crystal structure, reduces their volume, and as a result the unit-cell volume also decreases. Structure refinement shows that the formula for the sample with the anomalously high Na content is (K2.43Na0.57)Σ3.00Na[(UO2)(CO3)3](H2O). The unit-cell parameters, refined in space group P2c, are a = 9.2507(1), c = 8.1788(1) Å, V = 606.14(3) Å3 and Z = 2. The crystal structure was refined to R1 = 0.0082 and wR1 = 0.0185 with a GOF = 1.33, based on 626 observed diffraction peaks [Iobs>3σ(I)].

Crystals of the compound Na4(UO2)(CO3)3 have been synthesized and the structure has been solved. It is trigonal with a= 9.3417(6), c = 12.824(1) Å, V = 969.2(1) Å3, space group Pc1 and Z = 4. The structure was refined on the basis of F2 (wR2 = 4.2%) for all unique data collected using Mo-Kα X-radiation and a CCD-based detector. The final R1 was 2.0%, calculated for 534 unique observed (Fo ≥ 4σF) reflections, and the goodness-of-fit (S) was 0.91. The structure contains a uranyl tricarbonate cluster composed of a uranyl hexagonal bipyramid that shares three equatorial edges with CO3 triangles. The uranyl tricarbonate clusters are connected through NaO6 and NaO5 polyhedra, forming a heteropolyhedral framework structure. This compound may be related to a uranyl carbonate phase with the same composition which has been reported as an alteration phase on the surface of Chernobyl ‘lava’, and as a mineral in the Jachymov ore district, Czech Republic.

Leószilárdite (IMA2015-128), Na6Mg(UO2)2(CO3)6·6H2O, was found in the Markey Mine, Red Canyon, White Canyon District, San Juan County, Utah, USA, in areas with abundant andersonite, natrozippeite, gypsum, anhydrite, and probable hydromagnesite along with other secondary uranium minerals bayleyite, čejkaite and johannite. The new mineral occurs as aggregates of pale yellow bladed crystals flattened on ﹛001﹜ and elongated along [010], individually reaching up to 0.2 mmlong. More commonly it occurs as pale yellow pearlescent masses to 2 mm consisting of very small plates. Leószilárdite fluoresces green under both longwave and shortwave ultraviolet light, and is translucent with a white streak, hardness of 2 (Mohs), and brittle tenacity with uneven fracture. The new mineral is readily soluble in room temperature H2O. Crystals have perfect cleavage along ﹛001﹜, and exhibit the forms ﹛110﹜,﹛001﹜,﹛100﹜,﹛101﹜ and ﹛101﹜. Optically, leószilárdite is biaxial (-), α= 1.504(1), β= 1.597(1), γ= 1.628(1) (white light); 2V (meas.) = 57(1)°, 2V (calc.) = 57.1°; dispersion r > v, slight. Pleochroism: X= colourless, Y and Z= light yellow; X<Y ≈ Z The average of six wavelength dispersive spectroscopic analyses provided Na2O 14.54, MgO 3.05, UO3 47.95, CO2 22.13, H2O 9.51, total 97.18 wt.%. The empirical formula is Na5.60Mg0.90U2O28C6H12.60, based on 28 O apfu. Leószilárdite is monoclinic, C2/m, a = 11.6093(21), b = 6.7843(13), c = 15.1058(28) Å, β = 91.378(3)°, V= 1189.4(4) Å3 and Z = 2. The crystal structure (R1 = 0.0387 for 1394 reflections with Iobs > 4σI), consists of uranyl tricarbonate anion clusters [(UO2)(CO3)3]4- held together in part by irregular chains of NaO5(H2O) polyhedra sub parallel to [010]. Individual uranyl tricarbonate clusters are also linked together by three-octahedron units consisting of two Na-centred octahedra that share the opposite faces of a Mg-centred octahedron at the centre (Na–Mg–Na), and have the composition Na2MgO12(H2O)4. The name of the new mineral honours the Hungarian-American physicist, inventor and biologist Dr. Leó Szilárd (1898–1964).

Kamotoite-(Y) is a rare supergene product of uraninite hydration–oxidation weathering and its structure is unknown. Based on single-crystal X-ray diffraction data collected with high-redundancy using a microfocus source, kamotoite-(Y) is monoclinic, has space group P21/n,with a = 12.3525(5), b = 12.9432(5), c = 19.4409(7) Å, β = 99.857(3)°, V = 3069.8(2) Å3 and Z = 4. Crystals are pervasively twinned (two-fold rotation around [0.75 0 0.75]), giving a strongly pseudo-orthorhombic diffractionpattern. The pseudoorthorhombic pattern can be described with an orthorhombic super-cell (transformation matrix 0,1,0/1,0,1/3,0,1), approximately four times larger in volume then a true monoclinic unit cell. This unit-cell is the same as the cell given elsewhere for the structure of bijvoetite-(Y),another (REE)-containing uranyl carbonate. The successful structure solution and refinement (R = 0.044 for 6294 unique observed reflections), carried out using our choice of unit cell, as well as the superstructure refinement and comparison of the original structure data forbijvoetite-(Y) reveal that these two crystal structures are identical. The crystal structure of kamotoite-(Y) consists of electroneutral sheets of the bijvoetite-(Y) uranylanion topology and an interlayer with H2O molecules not-coordinated directly to any metal cation. Despite determinationof the kamotoite-(Y) structure and demonstration that bijvoetite-(Y) has the same structure, the identity of these two minerals cannot be proved without additional study of the holotype material.