White saponite occurs in joints and open fracture zones in metamorphosed dolomitic limestone near Ballarat, California. The saponite appears to have formed by hydrothermal alteration, possibly during Pliocene times. The material shows a 06l X-ray powder diffraction peak at 1.529 Å, A12O3 and MgO contents of about 4.4 and 23.5%, respectively, and a half-cell octahedral atoms summation value of about 2.82. The saponite appears to consist of a single, uniform clay species; the main impurities are fine shards of diopside and tremolite. The infrared and thermal properties of the Ballarat saponite are similar to those of the Allt Ribhein saponite. It has a lower water-holding capacity than montmorillonite and is characterized by lower Atterberg limits and expansion pressures and higher compaction densities. The apparent density of the saponite, 2.865 g/cm3, is greater than that of montmorillonite. This saponite is available from the Source Clays Repository of The Clay Minerals Society.

Additional well-crystallized kaolin from Washington County, Georgia, has been supplied to the Clay Minerals Society Source Clay Repository to replace the exhausted supply of KGa-1. This kaolin is called KGa-1B and is from a geographic location and stratigraphic position close to where KGa-1 was collected. Slight mineralogical and chemical differences are observed between KGa-1 and KGa-1B. KGa-1B crude appears slightly better crystalline than KGa-1, and it has a slightly higher titania content than KGa-1. The Al2O3, SiO2, Fe2O3, alkali, and alkaline earth contents appear similar for both samples. KGa-1 has a slightly coarser particle size than KGa-1B crude. More intensive post-depositional alteration may have cleansed and crystallized the KGa-1B material to a slightly greater degree than the KGa-1 material.

For more than forty years, The Clay Minerals Society has dispensed a set of source clays which have enabled a large number of researchers to work on similar materials. Many of these source clays remained unchanged over the years but, conversely, other clays have gone out of stock and thus were replaced. This was the fate of montmorillonite STx-1a, which was replaced by STx-1b. Although STx-1a and STx-1b share many basic chemical and mineralogical features, some minor differences exist that can affect behavior. A baseline characterization of the source clay STx-1b, which was the objective of this study, was, therefore, necessary to provide researchers a tool useful not only for new investigation but also to compare new results obtained on STx-1b with literature data on STx-1a. This characterization was gained using traditional and advanced methods that included: 1) chemical composition (major and trace elements); 2) cation exchange capacity determination; 3) thermal analyses coupled with evolved gas mass spectrometry; 4) quantitative mineralogical characterization using powder X-ray diffraction and Rietveld- RIR (Reference Intensity Ratio) refinement; 5) X-ray absorption spectroscopy at the Fe K-edge; 6) diffuse reflectance ultraviolet-visible and infrared spectroscopies; and 7) 29Si, 27Al, and 1H magic-angle spinning nuclear magnetic resonance measurements. According to this multi-analytical approach, the chemical formula for STx-1b is [4](Si7.753Al0.247) [6](Al3.281Mg0.558Fe0.136Ti0.024Mn0.002) [12](Ca0.341Na0.039 K0.061)O20(OH)4.