Study of dielectric relaxation and AC conductivity of InP:S single crystal

Published online by Cambridge University Press:  05 July 2012

M.M. El-Nahass ,
H.A.M. Ali  and
E.A. El-Shazly
M.M. El-Nahass
Affiliation:
Department of Physics, Faculty of Education, Ain Shams University, Roxy 11757 Cairo, Egypt
H.A.M. Ali*
Affiliation:
Department of Physics, Faculty of Education, Ain Shams University, Roxy 11757 Cairo, Egypt
E.A. El-Shazly
Affiliation:
Department of Physics, Faculty of Education, Ain Shams University, Roxy 11757 Cairo, Egypt
*
ae-mail: [email protected]
Get access

Abstract

The dielectric relaxation and AC conductivity of InP:S single crystal were studied in the frequency range from 100 to 5.25 × 105 Hz and in the temperature range from 296 to 455 K. The dependence of the dielectric constant (ε1) and the dielectric loss (ε2) on both frequency and temperature was investigated. Since no peak was observed on the dielectric loss, we used a method based on the electric modulus to evaluate the activation energy of the dielectric relaxation. Scaling of the electric modulus spectra showed that the charge transport dynamics is independent of temperature. The AC conductivity (σAC) was found to obey the power law: Aωs. Analysis of the AC conductivity data and the frequency exponent showed that the correlated barrier hopping (CBH) model is the dominant mechanism for the AC conduction. The variation of AC conductivity with temperature at different frequencies showed that σAC is a thermally activated process.

Type
Research Article
Information
The European Physical Journal - Applied Physics , Volume 58 , Issue 3 , June 2012 , 30102
Copyright
© EDP Sciences, 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Shimizu, A., Nishizawa, J., Oyama, Y., Suto, K., J. Cryst. Growth 229, 119 (2001)CrossRef
Oztas, M., Chin. Phys. Lett. 25, 4090 (2008)CrossRef
Yamada, T., Kudo, T., Tajima, K., Otsuka, A., Narushima, T., Ouchi, C., Iguchi, Y., Mater. Trans. 45, 1306 (2004)CrossRef
Riad, A.S., Darwish, S., Afify, H.H., Thin Solid Films 391, 109 (2001)CrossRef
Lin, C.-M., Sheu, H.-S., Tsai, M.-H., Wu, B.-R., Jian, S.-R., Solid State Commun. 149, 136 (2009)CrossRef
Zeyada, H.M., El-Nahass, M.M., Makhlouf, M.M., Curr. Appl. Phys. 11, 1326 (2011)CrossRef
Suvarna, R.P., Rao, K.R., Subbarangaial, K., Bull. Mater. Sci. 25, 647 (2002)CrossRef
El-Nahass, M.M., Farid, A.M., Abd El-Rahman, K.F., Ali, H.A.M., Physica B: Condens. Matter 403, 2331 (2008)CrossRef
Dutta, A., Bharti, C., Sinha, T.P., Ind. J. Eng. Mater. Sci. 15, 181 (2008)
Macedo, P.B., Moynihan, C.T., Bose, R., Phys. Chem. Glasses 13, 171 (1972)
Mogus-Milankovic, A., Santic, B., Day, D.E., Ray, C.S., J. Non-Cryst. Solids 283, 119 (2001)CrossRef
Bishnoi, B., Mehta, P.K., Panchal, C.J., Desai, M.S., Kumar, R., J. Nano Electron. Phys. 3, 698 (2011)
Dutta, A., Sinha, T.P., Jena, P., Adak, S., J. Non-Cryst. Solids 354, 3952 (2008)CrossRef
Aziz, S.B., Abidin, Z.H.Z., Arof, A.K., Express Polym. Lett. 4, 300 (2010)CrossRef
Patro, L.N., Hariharan, K., Mater. Sci. Eng. B 162, 173 (2009)CrossRef
Karmakar, A., Majumdar, S., Giri, S., Phys. Rev. B 79, 094406 (2009)CrossRef
Jonscher, A.K., Nature 267, 673 (1977)CrossRef
Jonscher, A.K., Dielectric Relaxation in Solids (Chelsea Dielectric Press, London, 1983)Google Scholar
Ayouchi, R., Leinen, D., Martın, F., Gabas, M., Dalchiele, E., Ramos-Barrado, J.R., Thin Solid Films 426, 68 (2003) CrossRef
Elliott, S.R., Philos. Mag. B 36, 1291 (1977)CrossRef
Mott, N.F., Davis, E.A., Electronic Processes in Non-Crystalline Materials (Clarendon Press, Oxford, 1979)Google Scholar
Hegab, N.A., Atyia, H.E., J. Ovonic Res. 3, 93 (2007)