X-ray Topography Study of Surface Damage in Single-Crystal Sapphire

Published online by Cambridge University Press:  10 February 2011

D. Black ,
R. Polvani ,
K. Medicus  and
H. Burdette
D. Black
Affiliation:
NIST, Gaithersburg, MD 20899, [email protected]
R. Polvani
Affiliation:
NIST, Gaithersburg, MD 20899, [email protected]
K. Medicus
Affiliation:
NIST, Gaithersburg, MD 20899, [email protected]
H. Burdette
Affiliation:
NIST, Gaithersburg, MD 20899, [email protected]
Get access

Abstract

X-ray diffraction topography was used to investigate the relationship between subsurface damage, near-surface microstructure, and fracture strength in a series of sapphire modulus of rupture (MOR) bars which had been fabricated to proof test fabrication processes. The strength of the bars was determined by failure in four point bending. The tensile surface of the bars was also examined using optical microscopy and non-contacting surface profilometry. Both show that the bars have good surface finish, with a typical RMS roughness of 0.7 nm. No correlation was found between RMS surface finish and fracture strength. Although the bars appeared to be indistinguishable, topographs taken prior to fracture testing revealed that they are of two distinct types. Type 1 has an oriented microstructure consisting of a pattern of linear features running the length of the bars. Type 2 was typical of well-polished sapphire, containing individual dislocations and occasional damage from handling. We attribute the Type 1 microstructure to fabrication damage that was not removed by subsequent processing and/or polishing. Fracture strength data showed that the Type I (damaged) bars had strengths less than 70 % of the bars without damage. Topography is sensitive to near-surface damage that can be correlated to fracture strength. Neither low magnification optical microscopy nor conventional surface finish statistics could be correlated to strength.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 590: Symposium R – Applications of Synchrotron Radiation Techniques…V , 1999 , 279
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. ) “Final Report for the Sapphire Statistical Characterization and Risk Reduction (SSCARR) Program”, in preparation, to be published by Nichols Research, Huntsville, AL. Google Scholar
2. ) Certain commercial equipment, instruments, or materials are identified in this paper in order to specify the experimental procedure adequately. Such identification is not intended to imply recommendation or endorsement by the National Institute of Standards and Technology, nor is it intended to imply that the materials or equipment identified are necessarily the best available for the purpose.Google Scholar
3. ) , Creath, , Katherine, “Phase-Measurement Interferometry Techniques” in Progress in Optics, Vol. XXVI, pp. 349–393, (1988).Google Scholar
4. ) Hockey, B.J., Proc. 20 of the British Ceramic Society, The British Ceramic Society, Stokeon-Trent, G.B., pp. 95–115, (1972).Google Scholar
5. ) Black, D., Polvani, R., Braun, L., Hockey, B. and White, G. in Window and Dome Technologies and Materials V, edited by Tustison, Randall W. (SPIE Proc. 3060, Bellingham, WA, 1997) p. 102–114.10.1117/12.277036Google Scholar