Tribochemistry of ZDOL Decomposition on Carbon Overcoats in Ultra-High Vacuum (UHV)

Published online by Cambridge University Press:  10 February 2011

C.S. Bhatia ,
C.-Y. Chen ,
W. Fong  and
D.B. Bogy
C.S. Bhatia
Affiliation:
SSD/IBM, 5600 Cottle Road, San Jose, CA 95193, [email protected]
C.-Y. Chen
Affiliation:
Computer Mechanics Laboratory, Department of Mechanical Engineering, University of California at Berkeley, CA 94720
W. Fong
Affiliation:
Computer Mechanics Laboratory, Department of Mechanical Engineering, University of California at Berkeley, CA 94720
D.B. Bogy
Affiliation:
Computer Mechanics Laboratory, Department of Mechanical Engineering, University of California at Berkeley, CA 94720
Get access

Abstract

Tribochemical studies of the effect of lubricant bonding on the tribology of the head/disk interface (HDI) were conducted using hydrogenated (CHx) carbon disk samples coated with perfluoropolyether ZDOL lubricant. The studies involved drag tests with uncoated and carbon-coated A1203-TiC sliders and also thermal desorption experiments in an ultra-high vacuum (UHV) tribochamber. We observed that a larger mobile lubricant portion significantly enhances the wear durability of the (head/disk interface) HDI by providing a reservoir to constantly replenish the lubricant displaced in the wear track during drag tests. In the thermal desorption tests we observed two distinct temperatures of desorption. The mobile ZDOL layer is desorbed at the lower thermal desorption temperature and the residual bonded ZDOL layer is desorbed at the higher thermal desorption temperature. We also observed that the hydrogen evolution from CHx overcoats initiates lubricant catalytic decomposition with uncoated A1203/TiC sliders, forming CF3 (69) and C2F5(119). The generation of Hydroflouric acid (HF) during thermal desorption experiments provides the formation mechanism of Lewis acid, which is the necessary component for catalytic reaction causing Z-DOL lube degradation

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 593: Symposium U – Amorphous & Nanostructured Carbon , 1999 , 397
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Pacansky, J. and Waltman, R.J., Chem.Mater. 5,486–494 (1993).Google Scholar
2. Vurens, G Zehringer, R., and Saperstein, D. in Surface Science Investigations in Tribology edited by Chun, Y.W. Homola, A.M., and Street, B., Washinfgton, D. C., Amercan Chemical Society, 169–180 (1992).Google Scholar
3. Strom, B.D., and Bogy, D.B, Wear 168, 31–36 (1993).Google Scholar
4. Zehe, M.J. and Faut, O. O., ASME Tribology Trans. 33, 634–640 (1990).Google Scholar
5. Kasai, P.H., Adv. Info. Storage Syst. 4, 291–314 (1992).Google Scholar
6. Wei, J., Fong, W., Bogy, D.B., and Bhatia, C.S., Tribology Letters 5, 203–209 (1998).Google Scholar
7. Bhatia, C.S., Fong, W., Chen, C.-Y., Wei, J., Bogy, D.B., Anders, S., Stammler, T., and Stohr, J., IEEE Trans. on Magnetics 35 (2), 910–915 (1999).Google Scholar
8. Bogy, D.B., Yun, X.H., and Knapp, B.J., IEEE Trans on Magnetics 30 (5), 369–373 (1994).Google Scholar
9. Lin, J.-L., Bhatia, C.S., and Yates, J.T. Jr., J. Vac. Sci. Technol. A 13 (2), 63–168 (1995).Google Scholar
10. Vurens, G.H. and Mate, C.M., Applied Surface Science 59, 281–287 (1992).Google Scholar
11. Cornaglia, L. and Gellman, A.J., J. Vac. Sci. Technol. A 15 (5), 2755–2765 (1997).Google Scholar
12. Perry, S.S., Merrill, P.B., and Kim, H.I., Tribology Letters 2, 393–404 (1996).Google Scholar
13. Chen, C.-Y., Fong, W., Bogy, D.B., and Bhatia, C.S., CML Technical Report No. 98–016, ASME Tribology Trans., in press (1999).Google Scholar
14. Tyndall, G.W., Leezenberg, P.B., Waltman, R.J., and Castenada, J., Tribology Letters 4, 103–108 (1998).Google Scholar
15. Waltman, R.J., Pocker, D.J., and Tyndall, G.W., Tribology Letters 4, 267–275 (1998).Google Scholar
16. Karis, T.E., Tyndall, G.W., and Jhon, M.S., submitted to ASME Tribology Trans., March 1998.Google Scholar
17. Chen, C.-Y. Fong, W. Bogy, D.B., and Bhatia, C.S., CML Technical Report 99-007, Tribology Letters 7, 1–10 (1999).Google Scholar
18. Yun, X.H., Bogy, D.B., and Bhatia, C.S., ASME Tribology Trans. 119, 437–443 (1997).Google Scholar
19. Waltman, R.J., and Tyndall, G.W., submitted to J. Phys. Chem, 1999.Google Scholar
20. Steritwieser, A., and Heathcock, C. H., Introduction to Organic Chemistry, (Macmillan Publishing Co., Inc., New York, 1976).Google Scholar
21. Sianesi, D., Zamboni, V., Fontanelli, R., and Binaghi, M., Wear 18, 85–100 (1971).Google Scholar
22. Chen, C.-Y., Fong, W., Bogy, D.B., and Bhatia, C.S., CML Technical Report 99-011, Tribology letters, in press (1999).Google Scholar
23. O'Connor, T.M. Jhon, M S, Bauer, C.L., Min, B.G., Yoon, D.Y., and Karis, T.E., Tribology Letters 1, 219–223 (1995).Google Scholar
24. Ma, X., GUI, J., Smoliar, L., Grannen, K. Marchon, B., Jhon, M.S., and Bauer, C.L., J. of Chemical Physics 110 (6), 3129–3137 (1999).Google Scholar
25. Ma, X., Gui, J., Grannen, K., Smoliar, L. Marchon, B., Jhon, M.S., and Bauer, C.L., Tribology Letters 6, 9–14 (1999).Google Scholar
26. Ma, X., Gui, J., Smoliar, L., Grannen, K., Marchon, B., Jhon, M.S., and Bauer, C.L., Physical Review E 59 (1), 722–727 (1999).Google Scholar
27. Tyndall, G.W., Waltman, R.J., and Pocker, D.J., Langmuir 14, 7527–7536 (1998).Google Scholar
28. Chen, C.-Y., Fong, W., Bogy, D.B., and Bhatia, C.S., CML Technical Report 99-008, submitted to J. American Vacuum Society (1999).Google Scholar