Transient Enhanced Diffusion for Ultra Low Energy Boron, Phosphorus, and Arsenic Implantation in Silicon

Published online by Cambridge University Press:  10 February 2011

Ning Yu ,
Amitabh Jain  and
Doug Mercer
Ning Yu
Affiliation:
Silicon Technology Development, Texas Instruments, Dallas, TX 75243, USA.
Amitabh Jain
Affiliation:
Silicon Technology Development, Texas Instruments, Dallas, TX 75243, USA.
Doug Mercer
Affiliation:
Silicon Technology Development, Texas Instruments, Dallas, TX 75243, USA.
Get access

Abstract

The SIA roadmap predicts that junction depths of 500 angstroms are required for CMOS technology nodes of 0.18 μm or beyond by the year 2001. There are several ultra-shallow junction doping techniques currently under investigation. These include beamline ion implantation, plasma immersion ion implantation, and gas immersion laser doping. This study was based on beamline ion implantation of B, P, and As into single-crystal Si wafers at 0.25-2 keV to doses of (2- 10)×1014 at./cm2 with minimized beam energy contamination. Rapid thermal annealing was applied to the implanted wafers at 1000-1050 °C for 10-15 sec at ramp rates of 35- 50 °C/s in a N2 ambient. Transient enhanced diffusion was observed for all three implant species. For example, the depth of 0.25 keV B measured by SIMS increases from 250 to 520 A at a concentration level of l×1017 at./cm3 upon RTA. To minimize the TED, several schemes of defect engineering were applied prior to low energy implantation, including pre-amorphization and implantation of other species. A comparison of TED for different implantation conditions is given with the aim of process development for minimizing TED. The impact of energy contamination on ultra shallow junctions is also addressed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 532: Symposium EE – Silicon Front-End Technology - Materials Processing & Modeling , 1998 , 35
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Bousetta, A., van den Berg, J.A., Armour, D.G., and Zalm, P.C., Appl. Phys. Lett. 58, 1626 (1991).Google Scholar
[2] Collart, E.J.H., Weemers, K., Gravesteijin, D.J., van Berkum, J.G.M., J. Vac. Sci. Tech. B 16, 280 (1998).Google Scholar
[3] Downey, D.F., Osbum, C.M., and Marcus, S.D., “Ultrashallow junction formation by ion implant and RTA”, in Solid State Tech., p. 71 (1997).Google Scholar
[4] Qian, X.Y., Cheung, N.W., Lieberman, M.A., Felch, S.B., Brennan, B., and Current, M.I., Appl. Phys. Lett. 59, 348 (1991).Google Scholar
[5] Felch, S. B., Brunco, D.P., Lee, B.S., Ahmad, A., Prall, K., and Chapek, D.L., “Formation of deep sub-micron buried channel pMOSFET with plasma doping”, Proc. 11th Internat. Conf. on Ion Implant Tech. p. 753 (1997).Google Scholar
[6] Kramer, K., Talwar, S., Lewis, I.T., Davison, J.E., Williams, K.A., Benton, K.A., and Weiner, K.H., Appl. Phys. Lett. 68, 2320 (1996).Google Scholar
[7] Jones, K.S., Moller, K., Chen, J., Puga-Lambers, M., Freer, B., Berstein, J., and Rubin, L., J. Appl. Phys. 81, 6051 (1997).Google Scholar
[8] Stolk, P.A., Gossmann, H.-J., Eaglesham, D.J., Jacobson, D.C., Rafferty, C.S., Gilmer, G.H., Jaraiz, M., and Poate, J.M., J. Appl. Phys. 81, 6031 (1997) and references therein.Google Scholar
[9] Agarwal, A., Eaglesham, D.J., Gossmann, H.-J., Pelaz, L., Hemer, S.B., Jacobson, D.C., Haynes, T.E., Erokhin, Y., and Simonton, R., “Boron-enhanced-diffusion of boron: the limiting factorf or ultra-shallowj unctions”, in IEDM'97, p. 467 (1997).Google Scholar
[10] Goto, K, Matsuo, J., Tada, Y., Tanaka, T., Momiyama, Y., Sugii, T., and Yamada, I., “A high performance 50 nm pMOSFET using decaborane (B10H14) ion implantation and 2-step activation annealing process”, in IEDM'97, p. 471 (1997).Google Scholar
[11] Ziegler, J.F., Biersack, J.P., and Littmark, U., The Stopping and Range of Ions in Solids, (Pergamon, New York, 1985).Google Scholar
[12] Privitera, V., Priolo, F., Mannino, G., Campisano, S.U., Camera, A., Arena, G., and Spinella, C., Appl. Phys. Lett. 71, 1834 (1997).Google Scholar
[13] Wolf, S. and Tauber, R.N., Silicon processing, p. 251 (Lattice Press, Sunset Beach, CA, 1986)Google Scholar