Surface Over-Melt During Laser Polishing of Indirect-SLS Metal Parts

Published online by Cambridge University Press:  11 February 2011

J. A. Ramos ,
D. L. Bourell  and
J. J. Beaman
J. A. Ramos
Affiliation:
Texas Materials Institute, Department of Mechanical Engineering, The University of Texas at Austin
D. L. Bourell
Affiliation:
Texas Materials Institute, Department of Mechanical Engineering, The University of Texas at Austin
J. J. Beaman
Affiliation:
Texas Materials Institute, Department of Mechanical Engineering, The University of Texas at Austin
Get access

Abstract

Laser polishing of indirect-SLS parts made from 420 stainless powder infiltrated with bronze has been achieved using CO2 and Nd:YAG lasers. Two mechanisms have been previously proposed for the reduction in surface roughness, namely: shallow surface melting (SMM) and surface over-melt (SOM). In SMM reflow of the molten surface minimizes the peak-valley height driven by capillary pressure and liquid curvature. On the other hand, during SOM the melting depth is such that the entire surface becomes liquid and formation of surface periodical structures dominates driven by a surface tension gradient. This surface morphology was identified by means of optical and scanning electron microscopy (SEM). The onset of this regime is dictated by the energy density (i.e., ratio of laser power to scan speed and beam diameter) as well as the initial roughness Ra value prior to laser surface polishing. In contrast with SMM, onset of the latter mechanism increases the roughness Ra with speed reduction. A thermo-physical model is presented, signaling good agreement with roughness Ra and characteristic surface wavelength results obtained for varying laser beam scan speeds. Understanding the surface over-melt mechanism is critical for determining the optimum polishing conditions that minimize roughness.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 758: Symposium LL – Rapid Prototyping Technologies , 2002 , LL1.9
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Beaman, J.J., Barlow, J.W., Bourell, D.L., and Crawford, R.H., Solid Freeform Fabrication: A New Direction in Manufacturing, (Kluwer Academic 1997).Google Scholar
2. McDonald, J.A., Ryall, C.J. and Wimpenny, D.I., Rapid Prototyping Casebook, (Professional Engineering Publishing 2001).Google Scholar
3. Lü, L., Fuh, J. and Wong, Y.S., Laser Induced Materials and Processes for Rapid Prototyping, (Kluwer Academic 2001).Google Scholar
4. Connolly, J., Direct Rapid Manufacturing – Is it Possible?, Time Compression Technologies, May (2001), pp. 46–47.Google Scholar
5. Ramos, J.A., Murphy, J., Wood, K., Bourell, D.L. and Beaman, J.J., Surface Roughness Enhancement of Indirect-SLS Metal Parts by Laser Surface Polishing, SFF Symposium Proc., 12 (2001).Google Scholar
6. Ramos, J.A. and Bourell, D.L., in Rapid Prototyping of Materials, edited by Marquis, F.D.S. and Bourell, D.L., (TMS, Warrendale PA, 2002), pp. 191–201.Google Scholar
7. Ramos, J.A., Bourell, D.L., and Beaman, J.J., Surface Characterization of Laser Polished Indirect-SLS Parts, SFF Symposium Proc., 13 (2002).Google Scholar
8. Prokhorov, A.M., Konov, V.I., Ursu, I. and Mihäilescu, I.N., Laser Heating of Metals, (Adam Hilger, 1990) pp.115–124.Google Scholar
9. Anthony, T.R. and Cline, H.E., J. Applied Physics, Vol. 48, No 9, 3888–3894 (1977).Google Scholar
10. Avanesov, V.S. and Zuev, M.A., “Investigation of surface topography after melting by laser beam”, SPIE, Vol. 2713, 340–343.Google Scholar
11. Rosenthal, D., Trans. ASME, Vol. 68, 849–865 (1946).Google Scholar
12. Grong, Ø., Christensen, N., J. Mater. Sci. and Tech., Vol. 2, 967–973 (1986).Google Scholar
13. Kurz, W., Fisher, D.J., Fundamentals of Solidification, 4th ed. (Trans Tech Publications, Zuerich, 1998) p. 164.Google Scholar