Supporting metal catalysts on modified carbon nanocones to optimize dispersion and particle size

Published online by Cambridge University Press:  31 January 2011

Paolo Matelloni ,
David M. Grant  and
Gavin S. Walker
Paolo Matelloni
Affiliation:
[email protected], University of Nottingham, Nottingham, United Kingdom
David M. Grant
Affiliation:
[email protected], University of Nottingham, Nottingham, United Kingdom
Gavin S. Walker
Affiliation:
[email protected], University of Nottingham, Nottingham, United Kingdom
Get access

Abstract

Carbon nanocones are the fifth allotropic form of carbon, first synthesized in 1997. They have been selected for investigating hydrogen storage capacity, because initial temperature programmed desorption experiments found a significant amount of hydrogen was evolved at ambient temperatures. The aim of this work was to study the effect of impregnation conditions on metal catalyst dispersion and to investigate whether the metal loaded cones had improved hydrogen storage characteristics. Pre-treatment of carbon nanocones with hydrogen peroxide was carried out, followed by metal decoration in aqueous solution by an incipient wetness technique. Two methods of reducing the metal catalyst have been applied: in hydrogen at room temperature (RT) and in an aqueous solution of NaBH4. XRD confirmed the complete metal reduction and TEM showed that the reduction technique affected the catalyst dispersion. Very fine dispersions of ca. 1 nm diameter metal clusters at catalyst loadings of 5 wt.% were achieved and high dispersions were retained for loadings as high as 15 wt.%. Hydrogen uptakes at RT were measured and an increase with metal loading was observed.

Keywords

Pdgrain sizehydrogenation
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1216: Symposium W – Hydrogen Storage Materials , 2009 , 1216-W02-02
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Wang, H. et al. , Carbon, 2009. 47(9): P. 2259–2268.Google Scholar
2. Poirier, E. Chahine, R. and Bose, T.K.. International Journal of Hydrogen Energy, 2001. 26(8): P. 831–835.Google Scholar
3. Gupta, B.K. and Srivastava, O.N.. International Journal of Hydrogen Energy, 2000. 25(9): P. 825–830.Google Scholar
4. Liu, C. et al. , Science, 1999. 286(5442): P. 1127–1129.Google Scholar
5. Lupu, D. et al. , International Journal of Hydrogen Energy, 2004. 29(1): P. 97–102.Google Scholar
6. Yang, F.H. and Yang, R.T. Carbon, 2002. 40(3): P. 437–444.Google Scholar
7. Kuznetsova, A. et al. , The Journal of Chemical Physics, 2000. 112(21): P. 9590–9598.Google Scholar
8. Zhu, H. et al. , Materials Chemistry and Physics, 2003. 78(3): P. 670–675.Google Scholar
9. Lueking, A.D.Y., R.T., , AIChE Journal, 2003 (49): p. 1556.Google Scholar
10. Wang, W.H., Lin, Y.T. and Kuo, C.T. Diamond and Related Materials, 2005. 14(3-7): p. 907–912.Google Scholar
11. Furtado, C., Moraes, F. and Carvalho, A.M. de M., Physics Letters A, 2008. 372(32): P. 5368–5371.Google Scholar
12. Sattler, K., Carbon, 1995. 33(7): P. 915–920.Google Scholar
13. Heiberg-Andersen, H., Skjeltorp, A.T. and Sattler, K. Journal of Non-Crystalline Solids, 2008. 354(47-51): p. 5247–5249.Google Scholar
14. Zhang, W. et al. , Carbon, 2009. 47(12): P. 2763–2775.Google Scholar
15. Lueking, A.D. et al. , Carbon, 2007. 45(4): P. 751–759.Google Scholar
16. Yu, X. et al. , Applied Surface Science, 2008. 255(5, Part 1): p. 1906–1910.Google Scholar
17. Ansón, A. et al. , Journal of Alloys and Compounds, 2007. 436(1-2): p. 294–297.Google Scholar
18. Antolini, E. et al. , Materials Chemistry and Physics, 2007. 101(2-3): p. 395–403.Google Scholar
19.http//rsbweb.nih.gov/ij/ij/.Google Scholar
20. Hernadi, K. et al. , Solid State Ionics, 2001. 141-142: p. 203–209.Google Scholar
21. Feng, Y. et al. , Chemical Physics Letters, 2003. 375(5-6): p. 645–648.Google Scholar
22. Chen, C.H. and Huang, C.C. International Journal of Hydrogen Energy, 2007. 32(2): P. 237–246.Google Scholar
23. Yang, J.Q., Liu, B.H. and Wu, S.. Journal of Power Sources, 2009. 194(2): P. 824–829.Google Scholar
24. Suttisawat, Y. et al. , International Journal of Hydrogen Energy, 2009. 34(16): P. 6669–6675.Google Scholar
25. Sun, Z.P. et al. . Electrochemistry Communications, 2009. 11(3): P. 557–561.Google Scholar
26. Calò, V., Nacci, A. and Monopoli, A. Journal of Molecular Catalysis A: Chemical, 2004. 214(1): P. 45–56.Google Scholar
27. Schmid, G., Clusters and Colloids. 1994, Weinheim: VCH.Google Scholar
28. Zhu, J. et al. , Applied Catalysis A: General, 2009. 352(1-2): p. 243–250.Google Scholar
29. Beletskaya, I.P. and Cheprakov, A.V. Chemical Reviews, 2000. 100(8): P. 3009–3066.Google Scholar
30. Flanagan, T. B. W.A.O., , Annual Review of Materials Science 1991. 21: p. 269–304.Google Scholar
31. Rather, S.u. et al. , Chemical Physics Letters, 2007. 441(4-6): p. 261–267.Google Scholar
32. Zacharia, R. et al. , Chemical Physics Letters, 2005. 412(4-6): p. 369–375.Google Scholar