The Study of Hafnium Silicate by Various Nitrogen Gas Annealing Treatment

Published online by Cambridge University Press:  01 February 2011

Dong Chan Suh ,
Kwun Bum Chung ,
Mann-Ho Cho ,
Young Dae Cho  and
Dae-Hong Ko
Dong Chan Suh
Affiliation:
[email protected], Yonsei University, Ceramic Engineering, Seo Dae Mun-gu Shinchon dong, Seoul, 120749, Korea, Republic of
Kwun Bum Chung
Affiliation:
[email protected], North Carolina State University, Department of Physics, Raleigh, NC, 8202, United States
Mann-Ho Cho
Affiliation:
[email protected], Yonsei University, Department of Physics, Seoul, 120749, Korea, Republic of
Young Dae Cho
Affiliation:
[email protected], Yonsei University, Department of Ceramic Engineering, Seoul, 120749, Korea, Republic of
Dae-Hong Ko
Affiliation:
[email protected], Yonsei University, Department of Ceramic Engineering, Seoul, 120749, Korea, Republic of
Get access

Abstract

Post annealing of Hf-silicate thin film grown by ALD was done with different kind of nitrogen gas and order of annealing. Annealing conditions are as follows: (1) NO gas only, (2) NH3 gas only, (3) NO gas + NH3 gas, and (4) NH3 + NO gas. With these conditions, the physical and electrical properties of nitrided Hf-silicate films were analyzed. Content of nitrogen is decreased with post NO gas annealing. In case of NH3, content of nitrogen is much higher than NO case. Most nitrogen atoms were distributed between Si substrate and Hf-silicate film for NO gas annealing. However, with NH3 gas annealing, nitrogen atoms were distributed in the whole Hf-silicate film evenly. Leakage current was decreased with post NO gas annealing and flat band voltage was also decreased.

Keywords

atomic layer depositionannealingchemical reaction
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1073: Symposium H – Materials Science of High-k Dielectric Stacks—From Fundamentals to Technology , 2008 , 1073-H04-21
Copyright
Copyright © Materials Research Society 2008

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Wallace, R.M. and Wilk, G.D. Crit. Rev. Solid State Mater. Sci. 28. 213 (2003).Google Scholar
2. Cho, M.-H., Roh, Y.S. Whang, C.N. Jeong, K. Choi, H.J. Nam, S.W. Ko, D.-H., Lee, J.H. Lee, N.I. and Fujihara, K. Appl. Phys. Lett. 81, 1071 (2002).Google Scholar
3. Wilk, G.D. Wallace, R.M. and Anthony, J. M. J. Appl. Phys. 89, 5243 (2001).Google Scholar
4. Quevedo-Lopez, M., El-Bouanani, M., Addepalli, S. Duggan, J.L. Gnade, B.E. Wallace, R.M., Visokay, M.R. Douglas, M. and Colombo, L. Appl. Phys. Lett. 79, 4192 (2001).Google Scholar
5. Kamiyama, S. Miura, T. Nara, Y. and Arikado, T. Appl. Phys. Lett. 86, 222904 (2005).Google Scholar
6. Ramanathan, S. McIntyre, P.C. Luning, J. Lysaght, P.S. Yang, Y., Chen, Z. and Stemmer, S., J. Electrochem. Soc. 150, F173 (2003).Google Scholar
7. Akbar, M.S. Cho, H.-J., Choi, R. Kang, C.S. Kang, C.Y. Choi, C.H. Rhee, S.J. Kim, Y.H. and Lee, J.C. IEEE Electron Devices Lett. 25, 465 (2004).Google Scholar
8. Quevedo-Lopez, M.A., Chambers, J. J. Visokay, M.R. Shanware, A. and Colombo, L. Appl. Phys. Lett. 87, 012902 (2005).Google Scholar
9. Kido, Y. and Koshikawa, T. J. Appl. Phys. 67, 187 (1990)Google Scholar