Structural, optical and chemical characterization of 300°C, MeV ion implanted and 1700°C annealed 6H-SiC

Published online by Cambridge University Press:  21 March 2011

R. Nipoti ,
A. Carnera  and
G. Mattei
R. Nipoti
Affiliation:
CNR-Istituto LAMEL, via Gobetti 101, I-40129 Bologna, Italy
A. Carnera
Affiliation:
Dipartimento di Fisica and INFM, Università degli Studi di Padova, via Marzolo 8, 1-35131 Padova, Italy
G. Mattei
Affiliation:
CNR-Istituto IMAI, via Salaria km 20.300, I-00016 Montelibretti, Roma, Italy
Get access

Abstract

This work deals with the structural, optical and chemical characterization of ion implanted and annealed crystalline SiC. N+ or Al+ ions with various MeV energy and fluence values were implanted at 300°C in 6H-SiC wafers. These processes produced about 1 μm thick doping profiles characterized by a sequence of peaks and valleys across an average plateau value. The annealing process was done in a radio frequency furnace at 1700°C for 30 min in high purity Ar atmosphere. The hot implanted layers show the presence of a weak damage amount, whose profile was estimated by confocal micro-Raman measurements. The annealed samples, in spite of a good crystal recovery, showed the formation of secondary defects as inferred by the Rutherford Back Scattering-Channeling spectrometry. The relative magnitude and position of peaks and valleys in the doping profiles were preserved by the high temperature annealing but the annealed doping profile was displaced towards the surface with respect to the as-implanted profile as shown by the Secondary Ion Mass Spectrometry measurements. No material loss but material densification due to the reordering of the crystalline structure can explain the trend of the chemical profiles.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 640: Symposium H – Silicon Carbide-Materials, Processing, and Devices , 2000 , H5.28
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Hallen, P.O.Å. Persson, A. Yu. Kutznetsov, L. Hultman and Svensson, B.G., Material Science Forum, 338–342, 869 (2000).Google Scholar
2. Turrel, G. and Dhamelincourt, P., in “Modern Technique in Raman Spectroscopy”, ed. Laserna, J.J. (Wiley,Chichester, 1996) pp. 109–142.S.Google Scholar
3. Nakashima and Harima, H., Phys. Stat.Sol.(a) 162, 39 (1997).Google Scholar
4. Nakashima, S. and Hangyo, M., IEEE Quantum Electronics, 25, 965 (1989).Google Scholar
5. Albertazzi, E. and Lulli, G., Nucl. Instr. and Meth. in Phys. Res., B 120, 147 (1996).Google Scholar
6. Lazar, M., Ottaviani, L., Locatelli, M.L., Planson, D., Canut, B. and Chante, J. P, Materials Science Forum, Vol.338–342, 921 (2000).Google Scholar
7. Pankin, D., Wirth, H., Anwand, W., Brauer, G. and Skorupa, W., Material Science Forum, 338–342, 877 2000).Google Scholar
8. Cai, B., Ren, B., Li, X.Q., She, C.X., Liu, F.M., Cai, X.W. and Tian, Z.Q., Surf. Sci., 406, 9 (1998).Google Scholar
9. Campos, F.J., Mestres, N., Pascual, J., Morvan, E., Godignon, P. and Millan, J., J. Appl. Phys., 85, 99 (1999).Google Scholar
10. Hoffman, M., Zywietz, A., Karch, K. and Bechstedt, F., Phys. Rev. B 50, 13401 (1994).Google Scholar
11. Nipoti, R., Albertazzi, E., Bianconi, M., Lotti, R., Lulli, G., Cervera, , and Carnera, A., Appl. Phys. Lett., 70, 3425 (1997).Google Scholar