Strontium Barium Niobate Thin Films Prepared by Pulsed Laser Deposition

Published online by Cambridge University Press:  15 February 2011

Y. Liu ,
C.W. Ong ,
P.W. Chan  and
C.L. Choy
Y. Liu
Affiliation:
Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong.
C.W. Ong
Affiliation:
Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong.
P.W. Chan
Affiliation:
Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong.
C.L. Choy
Affiliation:
Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong.
Get access

Abstract

Strontium barium niobate Sr0.55Ba0.45Nb2O6 thin films were prepared on Si (111) substrates by pulsed laser deposition (PLD). The film composition was determined as a function of the fluence φ and wavelength λ of the laser beam, the oxygen ambient pressure Po2 and the substrate temperature Ts. The results show that the film composition is very close to that of the target, and is almost independent of φ from 1 to 8 J cm−2, λ = 355, 532 and 1064 nm, Po2 from 0 to 150 mTorr, and Ts from 25 to 700°C. These results suggest that PLD is excellent for preparing SBN films with compositions congruent to that of the target. The x-ray diffraction data show that all the samples deposited at room temperature are amorphous. The x-ray diffraction results also indicate that the samples deposited at 700°C have a tungsten-bronze-(TB-) type structure with preferred crystallite orientation, while the room-temperature-deposited samples after annealing at 800°C for 30 minutes are polycrystalline and have random crystallite orientation.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 361: Symposium I2 – Ferroelectric Thin Films IV , 1994 , 557
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Neurgaonkar, R.R., Kalisher, M.H., Lim, T.C., Staples, E.J. and Keester, K.L., Mater. Res. Bull. 15, 1235 (1980).Google Scholar
2. Glass, n.A.M., J. Appl. Phys. 40, 4699 (1969).Google Scholar
3. Oliver, J.R. and Neurgaonkar, R.R. and Cross, L.E., J. Appl. Phys. 64, 37 (1988).Google Scholar
4. Xu, Y., Chen, C.J., Xu, R., and Mackenzie, J.D., Phys. Rev. B 44, 35 (1991).Google Scholar
5. Krupanidhi, S.B., J. Vac. Sci. Technol. A 10, 1569 (1992).Google Scholar
6. Thöny, S.S., Youden, K.E., Harris, J.S. Jr, and Hesselink, L., Appl. Phys. Lett. 65, 2018 (1994).Google Scholar
7. Saenger, K.L., Processing of Advanced Materials 3, 63 (1993).Google Scholar
8. Saenger, K.L., Roy, R.A., Etzold, K.F., and Cuomo, J.J., Mat. Res. Soc. Symp. Proc. 200, 115 (1990).Google Scholar
9. Venkatesan, T., Wu, X.D., Inam, A. and Wachtman, J.B., Appl. Phys. Lett. 52, 1193 (1988).Google Scholar
10. Koren, G., Gupta, A., Baseman, R.J., Lurwyche, M.I. and Laibowitz, R.B., Appl. Phys. Lett. 55, 2450 (1989).Google Scholar