Stress Effects on Nanocrystal Formation by Ni-Induced Crystallization of Amorphous Si

Published online by Cambridge University Press:  01 February 2011

Yaocheng Liu ,
Michael D. Deal ,
Mahmooda Sultana  and
James D. Plummer
Yaocheng Liu
Affiliation:
Center for Integrated Systems, Stanford University, CA
Michael D. Deal
Affiliation:
Center for Integrated Systems, Stanford University, CA
Mahmooda Sultana
Affiliation:
Department of Chemical Engineering, University of Southern California, CA
James D. Plummer
Affiliation:
Center for Integrated Systems, Stanford University, CA
Get access

Abstract

Metal-induced crystallization (MIC) of amorphous Si is gaining increased interest because of its potential use for low-temperature fabrication of integrated circuits. In this work, the MIC technique was used to make Si nanocrystals and the effects of stress on the crystallization were studied. Amorphous Si films were deposited onto the Si substrate with thermal oxides on top by low-pressure chemical vapor deposition (LPCVD) and then patterned into nanoscale pillars by electron beam lithography and reactive ion etching. A conformal low-temperature oxide (LTO) layer was deposited to cover the pillars, followed by an anisotropic etch back to form a spacer, leaving only the top surface of the pillars exposed to the 5 nm Ni sputtering deposition afterwards. An HF dip was used to partially remove the LTO spacers on the pillars, leading to different LTO thicknesses on different samples. These samples were then annealed to crystallize the amorphous Si pillars, forming Si nanocrystals. Transmission electron microscope (TEM) observations after anneal found a clear dependence of the crystallization rate on the pillar size as well as the LTO thickness. The crystallization rate was lower for pillars with thicker LTO spacers, while for the same LTO thickness the crystallization rate was lower for pillars with narrower width. A model based on the stress in the pillars is proposed to explain this dependence. This model suggests some methods to control the nickel-induced crystallization process and achieve higher quality Si nanocrystals.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 762: Symposium A – Amorphous and Nanocrystalline Silicon-Based Films – 2003 , 2003 , A16.2
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Bae, S., and Fonash, S. J., Appl. Phys. Lett. 76, 595 (2000).Google Scholar
2. Makihira, K., and Asano, T., Appl. Phys. Lett. 76, 3774 (2000).Google Scholar
3. Meng, Z., Wang, M., and Wong, M., IEEE Trans. Electron Devices 47, 404 (2000).Google Scholar
4. Huh, H., and Shin, J. H., Appl. Phys. Lett. 79, 3956 (2001).Google Scholar
5. Yoon, S. Y., Park, S. J., Kim, K. H., Jang, J., and Kim, C. O., J. Appl. Phys. 87, 609 (2000).Google Scholar
6. Chan, V. W. C., and Chan, P. C. H., IEEE Electron Device Lett. 22, 80 (2001).Google Scholar
7. Hayzelden, C., and Batstone, J. L., J. Appl. Phys. 73, 8279 (1993).Google Scholar
8. Batstone, J.L., Hayzelden, C., Inst. Phys. Conf. Ser. n134: section 4, 165–172 (1993).Google Scholar
9. Witvrouw, A. and Spaepen, F., J. Appl. Phys. 74 7154 (1993).Google Scholar