Strain Shift Coefficients for Phonons in Si-Ge Heterostructures

Published online by Cambridge University Press:  22 February 2011

J.-M. Baribeau  and
D. J. Lockwood
J.-M. Baribeau
Affiliation:
Institute for Microstructural Sciences, National Research Council Canada, Ottawa, KIA 0R6, CANADA.
D. J. Lockwood
Affiliation:
Institute for Microstructural Sciences, National Research Council Canada, Ottawa, KIA 0R6, CANADA.
Get access

Abstract

Strain shift coefficient measurements for longitudinal optical phonons in molecular beam epitaxy grown metastable pseudomorphic Si1−xGex layers on (100) Si (0 < x < 0.35) and Ge (0.80 < x < 1) are reported. Strain in partially relaxed annealed specimens was obtained by double-crystal x-ray diffractometry and the corresponding strain phonon shift was measured by Raman scattering spectroscopy. For epilayers grown on Si it was found that the epilayer Si-Si phonon frequency varies linearly with strain. The magnitude of the strain shift coefficient b however showed a small composition dependence varying from b ≈ -700 cm-1 at x = 0 to b ≈ -950 cm-1 at x = 0.35, corresponding to a stress factor τ = 0.40 + 0.57x: + 0.13x2 cm-1/kbar. For the Ge-Ge vibration mode in epilayers grown on Ge, b decreased from ∼-425 cm-1 at x = 1 to ∼-500 cm-1 at x = 0.8, corresponding to a stress factor τ ≈ 0.52 – 0.14x - 0.08x2 cm-1/kbar.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 239: Symposium D – Thin Films: Stresses and Mechanical Properties III , 1991 , 449
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Anastassakis, E., Pinczuk, A., Bursiein, E., Pollack, F.H. and Cardona, M., Solid Slate Commun. 8, 133 (1970).Google Scholar
2 Ccrdeira, F., Buchenauer, C.J., Poliak, F.H. and Cardona, M., Phys. Rev. B 5, 580 (1972).CrossRefGoogle Scholar
3 Chandrasekhar, M., Renucci, J.B. and Cardona, M., Phys. Rev. B 17, 1623 (1978).Google Scholar
4 Englert, T., Abstreiter, G. and Pontcharra, J., Solid State Electronics 23, 31 (1980).Google Scholar
5 Anastassakis, E., Cantarero, A. and Cardona, M., Phys. Rev. B 41, 7529 (1990).Google Scholar
6 Sui, Z., Herman, I.P. and Bevk, J. Appl. Phys. Lett. 58, 2351 (1991).Google Scholar
7 Renucci, J.B., Renucci, M.A. and Cardona, M., Solid State Commun. 9, 1651 (1971).CrossRefGoogle Scholar
8 Brya, W.J., Solid State Commun. 12, 253 (1973).CrossRefGoogle Scholar
9 Zinger, G.M., Ipatova, I.P. and Subashiev, A.V.. Sov. Phys.-Semicond. 11, 383 (1977).Google Scholar
10 Ishidate, T., Katagiri, S., Inoue, K., Shibuya, M., Tsuji, K. and Minomura, S., J. Phys. Soc. Jpn. 53, 2584(1984).CrossRefGoogle Scholar
11 Alonso, M.I. and Winer, K., Phys. Rev. B 39, 10056 (1989).Google Scholar
12 Cerdeira, F., Pinczuk, A., Bean, J.C., Battlogg, B. and Wilson, B.A., Appl. Phys. Lett. 45, 1138 (1984).Google Scholar
13 Halliwell, M.A.G., Lyons, M.H., Davey, S.T., Hockly, M., Tuppen, C.G. and Gibbings, C.J., Semicond. Sci. Technol. 4, 10 (1989).CrossRefGoogle Scholar
14 Baribeau, J.-M., Jackman, T.E., Maignć, P., Houghton, D.C. and Denhoff, M.W., J. Vac. Sci. Technol. A 5, 1898 (1987).Google Scholar
15 Simulation performed with RADS software, BEDE Scientific Instruments Ltd, Durham, UK.Google Scholar
16 Dismukes, J.P., Ekstrom, L. and Paff, R.J., J. Phys. Chem. 10, 3021 (1964).Google Scholar
17 Neuberger, M., “Handbook of Electronic Materials, Vol. 5”, (IFI, Plenum, New york, 1971).Google Scholar
18 Timbrell, P.Y., Baribeau, J.-M., Lockwood, D.J. and McCaffrey, J.P., J. Appl. Phys. 67, 6292 (1990); J. Electron. Mater. 19, 657 (1990).Google Scholar
19 Lockwood, D.J., Rajan, K., Fenton, E.W., Baribeau, J.-M., and Denhoff, M.W., Solid State Commun. 61, 465(1987).Google Scholar
20 Perovic, D.D., Weatherly, G.C., Baribeau, J.-M. and Houghton, D.C., Thin Solid Films 183, 141 (1989).CrossRefGoogle Scholar
21 Abstreiter, G., Brugger, H., Wolf, T., Zachai, R. and Zeller, C. in “Two-Dimensional Systems: Physics and New Devices” Edited by Bauer, G., Kuchar, F. and Heinrich, H. (Springer-Verlag, Berlin, 1986), p. 130.Google Scholar