Solid state MAS NMR spectroscopic characterization of plasma damage and UV modification of low k dielectric films

Published online by Cambridge University Press:  01 February 2011

Thomas Abell ,
Kristof Houthoofd ,
Francesca Iacopi ,
Piet Grobet  and
Karen Maex
Thomas Abell
Affiliation:
Intel affiliate at IMEC, Kapeldreef 75, 3001 Leuven, Belgium ([email protected])
Kristof Houthoofd
Affiliation:
Department of Surface Chemistry and Catalysis, KU Leuven, Belgium
Francesca Iacopi
Affiliation:
IMEC, Kapeldreef 75, 3001 Leuven, Belgium
Piet Grobet
Affiliation:
Department of Surface Chemistry and Catalysis, KU Leuven, Belgium
Karen Maex
Affiliation:
IMEC, Kapeldreef 75, 3001 Leuven, Belgium Department of Electrical Engineering, KU Leuven, Belgium
Get access

Abstract

29Si magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy was employed to characterize short-range atomic structure modifications to low k dielectric films that were subjected to post-deposition plasma exposure or UV curing. Comparison of spectra from single thick depositions of a CVD low k film (k∼3.0) with sequential thin depositions of the same film revealed ∼3% increase in Si-O crosslinking that was attributed to interfacial plasma damage. Comparison of a second CVD low k film (k∼3.0) before and after UV curing revealed ∼11% increase in Si-O crosslinking with commensurate losses of Si-OH and Si-CH3 groups. UV curing was believed to result in bulk modification. This crosslinking was found to increase the Young's modulus of the film from 11 to 16 GPa as measured on 700 nm films by nanoindentation. NMR analysis was found to provide significant information beyond that provided by FTIR but required special sample preparation and extensive data collection.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 863: Symposium B – Materials, Technology and Reliability of Advanced Interconnects , 2005 , B1.8
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Bohr, M., Tech. Dig., Int. Electron Devices Meet., IEEE Electron Devices Society, Washington D.C. USA, 1995, p.241, December 10-13.Google Scholar
2. Iacopi, F., Travaly, Y., Stucchi, M., Struyf, H., Peeters, S., Jonckheere, R., Leunissen, L.H.A., Tokei, Zs., Sutcliffe, V., Richard, O., Hove, M. Van, and Maex, K., Proceedings of the 2004 MRS Spring Meeting, San Francisco, CA, (Mater.Res.Soc.Proc. 812, Pittsburgh, PA, 2004) F1.5Google Scholar
3. Abell, T., Shamiryan, D., Schuhmacher, J., Besling, W., Sutcliffe, V., Maex, K. in Advanced Metallization Conference 2002, (MRS, 2003) pp.717–723.Google Scholar
4. Abell, T. and Maex, K., Microelec.Engr., 76, p.16–19, (2004)Google Scholar
5. Lee, J., Moinpour, M., Liu, H. C., Abell, T., Proceedings of the 2003 MRS Spring Meeting, San Francisco, CA, (Mater. Res. Soc. Proc. 767, Pittsburgh, PA, 2003) F7.4Google Scholar
6. Iacopi, F., Degryse, D., Vos, I., Patz, M., and Maex, K., Proceedings of the 2003 MRS Fall Meeting, Boston, MA, (Mater. Res. Soc. Proc. 795, Pittsburgh, PA, 2004) U4.3Google Scholar
7. Iacopi, F.et al., to be published Proceedings of the 2005 MRS Spring Meeting, San Francisco, CA, (Mater.Res.Soc.Proc. tbd, Pittsburgh, PA, 2005) B3.9 Google Scholar
8. Mabboux, P.Y. and Gleason, K.K., Jour. Electrochem. Society, 152, (1) F7–F13 (2005)Google Scholar