Slip Systems in Ni3 (Al, Ti) At Temperatures Above the Peak in Flow Stress

Published online by Cambridge University Press:  26 February 2011

Y. Q. Sun  and
P. M. Hazzledine
Y. Q. Sun
Affiliation:
Department of Metallurgy and Science of Materials, University of Oxford
P. M. Hazzledine
Affiliation:
Department of Metallurgy and Science of Materials, University of Oxford
Get access

Abstract

Dislocations in single crystals of Ni3 (Al, Ti) deformed at temperatures above the peak in flow stress have been studied by the TEM “weak-beam” technique. <110> dislocations on the primary cube plane are mostly of edge character, and they have been observed to transform into “super” Lomer- Cottrell locks. <100> dislocations, by contrast, are principally of 45° character. They are believed also to become immobilized by dissociation on {111} planes. Properties of both dislocations on cube planes are discussed and are related to the deformation behaviour of L12 ordered intermetallic alloys.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 133: Symposium H – High-Temperature Ordered Intermetallic Alloys III , 1988 , 197
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Pope, D.P. and Ezz, S.S., Int. Metals Rev. 29, 136 (1984).Google Scholar
2. Lamer, W.M., Phil. Mag. 42, 1327 (1951).Google Scholar
3. Cottrell, A.H., Phil. Mag. 43, 645 (1952).CrossRefGoogle Scholar
4. Korner, A., Phil. Mag. 58, 507 (1988).Google Scholar
5. Sun, Y.Q. and Hazzledine, P.M., Phil. Mag. A58, 603 (1988).Google Scholar
6. Veyssiere, P., Horton, J.A., Yoo, M.H. and Liu, C.T., Phil. Mag. Letters, A57, 17 (1988).CrossRefGoogle Scholar
7. Clement, M., Caillard, D., Lours, P. and Coujou, A., ICSMA 7, 205, 1988.Google Scholar
8. Veyssiere, P. and Douin, J., Phil. Mag. A51, L1 (1985).Google Scholar
9. Hirth, J.P. and Lothe, J., The Theory of Dislocations, 2nd ed. (John Wiley & Sons, New York, 1982), p. 800.Google Scholar