A Robust Process for Ion Implant Annealing of SiC in a Low-Pressure Silane Ambient

Published online by Cambridge University Press:  15 March 2011

S. Rao ,
S.E. Saddow ,
F. Bergamini ,
R. Nipoti ,
Y. Emirov  and
Anant Agrawal
S. Rao
Affiliation:
Electrical Engineering, Univ. of South Florida, Tampa, FL 33620, USA
S.E. Saddow
Affiliation:
Electrical Engineering, Univ. of South Florida, Tampa, FL 33620, USA
F. Bergamini
Affiliation:
CNR - IMM Sezione di Bologna, via Gobetti 101, I-40129 Bologna, Italy
R. Nipoti
Affiliation:
CNR - IMM Sezione di Bologna, via Gobetti 101, I-40129 Bologna, Italy
Y. Emirov
Affiliation:
Electrical Engineering, Univ. of South Florida, Tampa, FL 33620, USA
Anant Agrawal
Affiliation:
Cree, Inc., 4600 Silicon Drive, Durham, NC 27703, USA
Get access

Abstract

High-dose Al implants in n-type epitaxial layers have been successfully annealed at 1600°C without any evidence of step bunching. Anneals were conducted in a silane ambient and at a process pressure of 150 Torr. Silane, 3% premixed in 97% UHP Ar, was further diluted in a 6 slm Ar carrier gas and introduced into a CVD reactor where the sample was heated via RF induction. A 30 minute anneal was performed followed by a purge in Ar at which time the RF power was switched off. The samples were then studied via plan-view secondary electron microscopy (SEM) and atomic force microscopy (AFM). The resulting surface morphology was step- free and flat.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 815 , 2004 , J1.5
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Phelps, G. J., Wright, N.G., Chester, E.G., Johnson, C. M. and O'Neil, A.G., “Step bunching fabrication constraints in silicon carbide”, Semicond. Sci. Technol. 17, L17 (2002).Google Scholar
[2] Capano, M., Ryu, S., Melloch, M. R., Cooper, J. A., and Buss, M. R., “Dopant activation and surface morphology of ion implanted 4H- and 6H-Silicon Carbide,” J. Electron. Mater. 27, 370 (1998).Google Scholar
[3] Ahmed, S., Barbero, C.J., and Sigmon, T.W., “Activation of ion implanted dopants in -SiC”, Appl. Phys. Lett. 66, 712 (1995).Google Scholar
[4] Seshadri, S, Eldridge G, W and Agarwal A, K 1998, “Comparison of the annealing behavior of highdose nitrogen-, aluminum-, and boron-implanted 4H–SiC”, Appl. Phys. Lett. 72, 2026 (1998).Google Scholar
[5] Capano, M., Ryu, S., Melloch, M. R., Cooper, J. A., Rottner, K., Karlsson, S., Nordell, N., Powell, A. and Walker, D. E., “Surface roughening in ion implanted 4H-Silicon Carbide”, J. of Electron. Mater. 28, 214 (1999).Google Scholar
[6] Jones, K.A. et al. , “AlN as an encapsulate for annealing SiC,” J. Appl. Phys. 83, 8010 (1998)Google Scholar
[7] Bergamini, F., Rao, S., Poggi, A., Saddow, S.E., Nipoti, R., and Agarwal, A.,“Silane annealing at 1600°C for the electrical activation of Al+ implanted ions: J-V characteristics of p+/n 4H-SiC diodes”, submitted to 5th European Conf. on Silicon Carbide and Related Materials (ECSCRM2004), August 31-Sepetember 4, 2004, Bologna, Italy.Google Scholar
[8] SRIM download at the web page: http://www.srim.org/SRIM Google Scholar