Results from Long-Term Dissolution Tests Using Oxidized Spent Fuel

Published online by Cambridge University Press:  28 February 2011

Charles N. Wilson
Charles N. Wilson*
Affiliation:
Pacific Northwest Laboratory, (a) P.O. Box 999, Richland, WA 99352
Get access

Abstract

Two semi-static dissolution tests using oxidized PWR spent fuel specimens are being conducted under ambient hot cell conditions in Nevada Test Site J-13 well water and unsealed fused silica vessels. The test specimens were oxidized at 250°C in air to bulk oxygen-to-metal (O/M) values of 2.21 and 2.33. Following an initial 191-day test cycle, the specimens were restarted in fresh J-13 water for a second long-term test cycle. Results through the first 40 months of Cycle 2 are compared with results from similar tests at 25°C and 85°C using unoxidized spent fuel specimens.

Increased concentrations of U, Am, Cm and Np were measured in 0.4- μm filtered samples from the oxidized fuel tests compared to the unoxidized fuel tested at 25°C; Pu concentrations were not affected by the fuel oxidation state. Most of the Am and Cm, and a portion of the Pu, measured in 0.4-μm filtered samples was removed by 2-nm filtration. Fission product release results were normalized to specimen inventories and reported as fractional release. No attempt was made to normalize the data to surface area. Initial 99Tc release was greatly increased, and prolonged increases in the fractional release rates of 99Tc and 129I occurred as a result of fuel oxidation. Fractional release rates for 137Cs and 90Sr from oxidized fuel eventually decreased to levels similar to those observed with unoxidized fuel after equivalent testing times, suggesting that matrix dissolution rates normalized to fuel mass were not increased as a result of oxidation.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 212: Symposium P – Scientific Basis for Nuclear Waste Management XIV , 1990 , 197
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Rethinking High-Level Radioactive Waste Disposal, National Academy Press, Washington, D.C. (1990).Google Scholar
2. Einziger, R. E. and Buchanan, C. B., Long-Term Low-Temperature Oxidation of PWR Spent Fuel: Interim Transition Report, WHC-EP-0070, Westing-house Hanford Company, Richland, WA (1988).Google Scholar
3. Wilson, C. N., Results from NNWSI Series 2 Bare Fuel Dissolution Tests, PNL-7169, Pacific Northwest Laboratory, Richland, WA (1990).Google Scholar
4. Wilson, C. N., Results from NNWSI Series 3 Spent Fuel Dissolution Tests, PNL-7170, Pacific Northwest Laboratory, Richland, WA (1990).Google Scholar
5. Gray, W. J. and Strachan, D. M., “U02 Matrix Dissolution Rates and Grain Boundary Inventories of Cs, Sr, and Tc in Spent LWR Fuel,” Paper presented at this meeting.Google Scholar
6. Wilson, C. N. and Gray, W. J., “Effects of Water Composition on the Dissolution Rate of U02 Under Oxidizing Conditions,” in proceedings of High Level Radioactive Waste Management Conference, pp 1431–1436, Las Vegas, NV, April 8–12, 1990.Google Scholar