Preparation of Bi-2212/Ag Tapes by Electrodeposition

Published online by Cambridge University Press:  18 March 2011

Jun Chen ,
Raghu Bhattachary ,
Ramakrishnan Padmanabhanl  and
Richard Blaugher
Jun Chen
Affiliation:
National Renewable Energy Laboratory, 1617 Cole Blvd, Golden, CO 80401 Department of Physics, Boston College, Chestnut Hill, MA 02467
Raghu Bhattachary
Affiliation:
National Renewable Energy Laboratory, 1617 Cole Blvd, Golden, CO 80401
Ramakrishnan Padmanabhanl
Affiliation:
National Renewable Energy Laboratory, 1617 Cole Blvd, Golden, CO 80401 Department of Physics, University of Colorado at Boulder, Boulder, CO 80309
Richard Blaugher
Affiliation:
National Renewable Energy Laboratory, 1617 Cole Blvd, Golden, CO 80401
Get access

Abstract

Bi-2212 precursor films were deposited on both sides of polycrystalline Ag tapes by electrodeposition. After a melt-solidification process in flowing oxygen atmosphere, c-axis textured Bi-2212 films with Jc( 0T, 4.2K) up to 820,000 A/ cm2 were obtained. A post annealing in flowing nitrogen at 475°C for 25 minutes increased Tc from 72 K to 92 K, and Jc(H=0T) > 17, 000A/ cm2 was observed at 60 K. No scaling behavior of the pinning force was observed, indicating more than one pinning mechanism in thus obtained Bi-2212/Ag tapes.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 689: Symposium E – Materials for High-Temperature Superconductor Technologies , 2001 , E4.5
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Heine, K. et al., Appl. Phys. Lett. 55 (1989) 2441.Google Scholar
[2] Kase, J. et al., Jpn. J. Appl. 29 (1990) L1096.Google Scholar
[3] Togano, K. et al., Adv. Cryo. Eng. Mat. 38 (1992)1081.Google Scholar
[4] Villard, G. et al., IEEE Transaction on Applied Superconductivity 11(2001) 3039.Google Scholar
[5] Miao, H. et al., Physica C 303 (1998)81.Google Scholar
[6] Zuraski, D.J., et al, J. Electrochem. Soc. 135 (1988) 1607.Google Scholar
[7] Maxfield, M. et al., Appl. Phys. Lett. 54 (1989) 1932.Google Scholar
[8] Bhattacharya, R.N. et al., Science and Technology of Thin Film Superconductors, 2 (1991) 243.Google Scholar
[9] Bhattacharya, R.N. et al., Physica C 211 (1993) 475.Google Scholar
[10] Bhattacharya, R.N. et al., Physica C 333 (2000) 59.Google Scholar
[11] Hellstrom, E.E. et al., Physica B 216 (1996) 252.Google Scholar
[12] Koblischika, M.R., Physica C 282–287 (1997) 2193.Google Scholar