Optimization of Ion Assist Beam Deposition of Magnesium Oxide Template Films During Initial Nucleation and Growth

Published online by Cambridge University Press:  01 February 2011

James Groves ,
Robert Hammond ,
Vladimir Matias ,
Liliana Stan ,
Raymond F DePaula  and
Bruce M Clemens
James Groves
Affiliation:
[email protected], Stanford University, Materials Science, 476 Lomita Mall, Stanford, California, 94305, United States, 505 470-3470
Robert Hammond
Affiliation:
[email protected], Stanford University, GLAM, 476 Lomita Mall, Stanford, California, 94305, United States, 650 723-0169
Vladimir Matias
Affiliation:
[email protected], Los Alamos National Laboratory, Superconductivity Technology Center, Mail Stop T004, Los Alamos, New Mexico, 87545, United States
Liliana Stan
Affiliation:
[email protected], Los Alamos National Laboratory, Superconductivity Technology Center, Mail Stop T004, Los Alamos, New Mexico, 87545, United States
Raymond F DePaula
Affiliation:
[email protected], Los Alamos National Laboratory, Superconductivity Technology Center, 87545, New Mexico, United States
Bruce M Clemens
Affiliation:
[email protected], Stanford University, Materials Science and Engineering, 94305, California, United States
Get access

Abstract

Recent efforts in investigating the mechanism of ion beam assisted deposition (IBAD) of biaxially textured thin films of magnesium oxide (MgO) template layers have shown that the texture develops suddenly during the initial 2 nm of deposition. To help understand and tune the behavior during this initial stage, we pre-deposited thin layers of MgO with no ion assist prior to IBAD growth of MgO. We found that biaxial texture develops for pre-deposited thicknesses < 2 nm, and that the thinnest layer tested, at 1 nm, resulted in the best qualitative RHEED image, indicative of good biaxial texture development. The texture developed during IBAD growth on the 1.5 nm pre-deposited layer is slightly worse and IBAD growth on the 2 nm pre-deposited layer produces a fiber texture. Application of these layers on an Al2O3 starting surface, which has been shown to impede texture development, improves the overall quality of the IBAD MgO and has some of the characteristics of a biaxially texture RHEED pattern. It is suggested that the use of thin (<2 nm) pre-deposited layers may eliminate the need for bed layers like Si3N4 and Y2O3 that are currently thought to be required for proper biaxial texture development in IBAD MgO.

Keywords

ion-beam assisted depositionnucleation & growthtexture
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1254: Symposium L – Recent Advances and New Discoveries in High-Temperature Superconductivity , 2010 , 1254-L05-10
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Foltyn, S. R., Civale, L., Macmanus-Driscoll, J. L. et al., Nature Materials 6 (9), 631 (2007).Google Scholar
2 Wang, C. P., Do, K. B., Beasley, M. R. et al., Applied Physics Letters 71 (20), 2955 (1997).Google Scholar
3 Arendt, P. N. and Foltyn, S. R., MRS Bulletin 29 (8), 543 (2004).Google Scholar
4 Selvamanickam, V., Chen, Y., Xiong, X. et al., Physica C: Superconductivity 463–465, 482 (2007).Google Scholar
5 Wang, C. P., Doctor of Philosophy, Stanford University, 1999.Google Scholar
6 Brewer, R. T. and Atwater, H. A., Applied Physics Letters 80 (18), 3388 (2002).Google Scholar
7 Groves, J. R., Hammond, R. H., DePaula, R. F. et al., in MRS Symposium Proceedings, edited by Matias, V., Huhne, R., Moon, S.-H. et al. (Materials Research Society, Boston, MA, 2008), Vol. 1150 pp. 37.Google Scholar
8 Groves, J. R., DePaula, R. F., Stan, L. et al., IEEE Transactions on Applied Superconductivity 19 (3), 3311 (2009).Google Scholar
9 Zepeda-Ruiz, L. A. and Srolovitz, D. J., Journal of Applied Physics 91 (12), 10169 (2002).Google Scholar
10 Groves, J. R., Arendt, P. N., Foltyn, S. R. et al., IEEE Transactions on Applied Superconductivity 13 (2), 2651 (2003).Google Scholar