Observation of the Wurtzite Phase in OMVPE Grown ZnSe/GaAs: Effect on Implantation and Rapid Thermal Annealing

Published online by Cambridge University Press:  21 February 2011

K. S. Jones ,
J. Yu ,
P. D. Lowen  and
D. Kisker
K. S. Jones
Affiliation:
Department of Materials Science and Engineering, University of Florida, Gainesville, FL 32611
J. Yu
Affiliation:
Department of Materials Science and Engineering, University of Florida, Gainesville, FL 32611
P. D. Lowen
Affiliation:
Department of Materials Science and Engineering, University of Florida, Gainesville, FL 32611
D. Kisker
Affiliation:
AT&T Bell Laboratories, Crawfords Corner Road, Holmdel, NJ 07733
Get access

Abstract

Transmission electron diffraction patterns of cross-sectional TEM samples of OMVPE ZnSe on GaAs indicate the existence of the hexagonal wurtzite phase in the epitaxial layers. The orientation relationship is (0002)//(111); (1120)//(220). Etching studies indicate the phase is internal not ion milling induced. The average wurtzite particle size is 80Å-120Å. Because of interplanar spacing matches it is easily overlooked. Electrical property measurements show a high resistivity (1010ω/square) which drops by four orders of magnitude upon rapid thermal annealing between 700°C and 900 °C for 3 sec. Implantation of Li and N have little effect on the electrical transport properties. The Li is shown to have a high diffusivity, a solid solubility of ≈1016/cm3 at 800°C and getters to the ZnSeA/aAs interface.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 147: Symposium C – Ion Beam Processing of Advanced Electronic Materials , 1989 , 339
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Skromme, B.J., Stoffel, N.G., Gozdz, A.S., Tamargo, M.C., and Shibli, S.M. in Advances in Materials Processing and Devices in III-V Compound Semiconductors, edited by Sadana, D.K., Eastman, L. and Dupuis, R., (Mater. Res. Soc. Proc. 144 Pittsburg, PA 1988).Google Scholar
2. Yodo, T. and Yamashita, K., Appl. Phys. Lett. 53, 2403 (1988).Google Scholar
3. Wu, Z.L., Merz, J.L., Werkhoven, C.J., Fitzpatrick, B.J., and Bhargava, R.N., Appl. Phys. Lett. 40, 345 (1982).Google Scholar
4. Kosai, K., Fitzpatrick, B.J., Grimmeiss, H.G., Bhargava, R.N., and Neumark, G.F., Appl. Phys. Lett. 35, 194 (1979).Google Scholar
5. Yao, T., Ogura, M., Matsuoka, S., Morishita, T., Jap. J. Appl. Phys. 22, L144 (1983).Google Scholar
6. Shiojiri, M., Kaito, C., Sekimoto, S., and Nakamura, N., Phil. Mag. A 46, 495 (1982).Google Scholar
7. Holt, D.B., J. Mater. Sci. 19, 439 (1984).Google Scholar
8. Austuman, S.B. and Gehman, W.G., J. Mater. Sci. 1, 249 (1966).Google Scholar
9. Park, R.M., Keiman, J. and Mar, H.H., SPIE Conf. on Advances in Semiconductors and Semiconductor Structure, Baypoint, FL, March 22, 1987.Google Scholar
10. Jones, K.S., Prussin, S., and Weber, E.R., Appi. Phys. A 45, 1 (1988).Google Scholar
11. Vermaak, J.S. and Petruzzello, J., J. Appl. Phys. 55, 1215 (1984).Google Scholar
12. Gunshor, R., private communicationsGoogle Scholar