Nanocrystalline Ge Synthesis by Reduction of Si1-xGexO2 Formed by High Pressure Oxidation

Published online by Cambridge University Press:  28 February 2011

David C. Paine ,
Christine Caragianis ,
Tae Young Kim  and
Yuzo Shigesato
David C. Paine
Affiliation:
Brown University, Division of Engineering, Providence, RI 02912
Christine Caragianis
Affiliation:
Brown University, Division of Engineering, Providence, RI 02912
Tae Young Kim
Affiliation:
Brown University, Division of Engineering, Providence, RI 02912
Yuzo Shigesato
Affiliation:
Brown University, Division of Engineering, Providence, RI 02912
Get access

Abstract

Nanocrystalline Ge suitable for photoluminescence studies was synthesized from hydrothermally oxidized alloys of Si60Ge40 using steam at 25 MPa and 475°C. Annealing in either an inert atmosphere (UHP N2) or in flowing forming gas (80:20 N2:H2) results in Ge precipitation. In the first case the Ge precipitates are large and concentrated in the bottom portion of the oxide and result from Si reduction of GeO2. In the case of flowing forming gas the Ge precipitates are distributed diroughout die oxide and are formed by reaction between H2 and GeO2. The precipitated samples were analyzed using Raman spectroscopy and cross sectional TEM. Preliminary photoluminescence data reveal that oxide samples excited by the 325 nm line of a HeCd laser after annealing in H2 at both 750 and 800°C for 30 min show strong visible luminescence while unannealed samples do not.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 283: Symposium F – Microcrystalline Semiconductors–Materials Science and Devices , 1992 , 51
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Hayashi, S., Fujii, M., Yamamoto, K., Jap. J. Appl. Phys. 28, L1464 (1989).Google Scholar
2. Maeda, Y., Tsukamoto, N., Yazawaa, Y., Kanemitsu, Y., and Masumoto, Y., Appl. Phys. Lett. 59, 3168 (1992).Google Scholar
3. Fujii, M., Hayashi, S., Yamamoto, K., Jap. J. Appl. Phys. 30, 687 (1991).Google Scholar
4. LeGoues, F. K., Rosenberg, R., and Meyerson, B. S., J. Appl. Phys. 65, 1724 (1989).Google Scholar
5. Paine, D. C., Caragianis, C., and Schwartzman, A. F., J. Appl. Phys. 70, 5076 (1991).Google Scholar
6. Paine, D. C., Caragianis, C., and Shigesato, Y., Appl. Phys. Lett. 60, 2886 (1992).Google Scholar
7. Kim, T. Y., Caragianis, C., Shigesato, Y., and Paine, D. C., to be submitted, (1993).Google Scholar
8. Barin, I., Knacke, O., Thermochemical Properties of Inorganic Substances (Springer-Verlag, Berlin, 1973).Google Scholar
9. Pfeffer, R., Ohring, M., J. Appl. Phys. 52, 777 (1981).Google Scholar
10. Lee, R. W., Frank, R. C., Swets, D. E., J. Chem. Phys. 36, 1062 (1962).Google Scholar