Microstructure-Property Relationships of Two Ti2AlNb-based Intermetallic Alloys: Ti-15Al-33Nb(at.%) and Ti-21Al-29Nb(at.%)

Published online by Cambridge University Press:  26 February 2011

Christopher J. Cowen ,
Dingqiang Li  and
Carl J. Boehlert
Christopher J. Cowen
Affiliation:
School of Engineering, Alfred University, Alfred, NY 14802, U.S.A.
Dingqiang Li
Affiliation:
School of Engineering, Alfred University, Alfred, NY 14802, U.S.A.
Carl J. Boehlert
Affiliation:
School of Engineering, Alfred University, Alfred, NY 14802, U.S.A.
Get access

Abstract

Two Ti2AlNb intermetallic orthorhombic (O) alloys, Ti-15Al-33Nb and Ti-21Al-29Nb(at.%), were subtransus processed into sheets, using pancake forging and hot-pack rolling, and evaluated in tension (25 and 650°C) and creep (650–710°C) and the properties and deformation behavior were related to microstructure. Some of the microstructural features evaluated were grain boundary character, grain size, phase volume fraction, and morphology. The alloy Al content was important to strength and elongation-to-failure (εf), where higher Al contents lead to greater tensile strengths and lower εf values and a corresponding brittle fracture response. However, the room temperature (RT) strengths of Ti-15Al-33Nb, which exhibited greater BCC phase volume fractions than Ti-21Al-29Nb and ductile failure (εf >2%), were always greater than 775 MPa. The creep stress exponents (n) and activation energies (Qapp) suggested that a transition in the dominant creep deformation mechanism exists and is dependent on stress and microstructure. Supertransus heat treatment, which increased the prior-BCC grain size and resulted in a lath-type O+BCC microstructure, resulted in reduced creep strains and strain rates. In fact, the supertransus heat-treated Ti-15Al-33Nb microstructures exhibited greater creep resistance than subtransus heat-treated Ti-21Al-29Nb microstructures. Combining the creep observations with the tensile response, the supertransus heat treated Ti-15Al-33Nb lath O+BCC microstructures exhibited the most attractive combination of tensile strength, εf values, and creep resistance.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 842: Symposium S – Integrative and Interdisciplinary Aspects of Intermetallics , 2004 , S7.9
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Nandy, T.K., Mishra, R.S., and Banerjee, D., Scripta Metall. Mater. 28, 569 (1993).Google Scholar
2. Rowe, R.G. and Larsen, M., Titanium 1995, Vol. 1, pp. 364–371, Ed Blenkinsop, P.A., Evans, W.J., and Flowers, H.M., The University Press, Cambridge, UK, 1996.Google Scholar
3. Boehlert, C.J., Metall. Mater. Trans. 32A, 1977 (2001).Google Scholar
4. Boehlert, C.J. and Miracle, D.B., Metall. Mater. Trans. 30A, 2349 (1999).Google Scholar
5. Muraleedharan, K. and Banerjee, D. , Philos. Mag. A, 71, 1011 (1995).Google Scholar
6. Boehlert, C.J., Cowen, C.J., Jaeger, R., Niinomi, M., Akahori, T., Mater. Sci Eng., C, (in press).Google Scholar
7. Li, D. and Boehlert, C.J., TMS Letters, (in press).Google Scholar
8. Popille, F. and Douin, J., Philos. Mag. A, 73, 1401 (1996).Google Scholar
9. Boehlert, C.J. and Bingert, J.F., J. Mater. Process. Technol. 117, 401 (2001).Google Scholar
10. Hayes, R.W., Scripta Mater. 34, 1005 (1996).Google Scholar