Microstructure Analysis of Melt-Spun Al3Ti Intermetallics by XRD and EXAFS

Published online by Cambridge University Press:  15 February 2011

Jinmin Chen ,
W. E. Frazier  and
E. V. Barrera
Jinmin Chen
Affiliation:
Department of Mechanical Engineering and Materials Science, Rice University, Houston, TX 77030
W. E. Frazier
Affiliation:
Naval Air Warfare Center-Aircraft Division, 22541 Millstone Road, MS #3, Patuxent River, Maryland 20670
E. V. Barrera
Affiliation:
Department of Mechanical Engineering and Materials Science, Rice University, Houston, TX 77030
Get access

Abstract

In an effort to expand the composition range over which Al3Ti is stable, various amounts of niobium were substituted for titanium and processed by melt-spinning. Several samples were annealed both at 600°C and 1000°C for 24 hours. The effects of processing parameters such as wheel speed, the amount of niobium, and annealing temperatures on the structure were investigated by XRD and EXAFS. XRD showed that for all the samples the only structure present was DO22-The DO22 structure was stable even after the high temperature heat treatments. By means of EXAFS, niobium atoms were observed to occupy titanium sites in the DO22 structure. Furthermore, in the unannealed samples, increasing wheel speed of the melt spinning process or the niobium concentration tended to distort the crystal structure. It was observed that Ti EXAFS had different results from the Nb EXAFS beyond their occupying similar sites, which suggested there may exist some composition zones, i.e. rich Nb zone or rich Ti zones, although the structures present were still DO22. The samples were found to experience different distortions as a function of annealing temperatures.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 460: Symposium Z – High-Temperature Ordered Intermetallic Alloys VII , 1996 , 103
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yamaguchi, M., Umakoshi, Y., and Yamane, T., Phil. Mag. A 55(3), p. 301 (1987).Google Scholar
2. Yamaguchi, M. and Inui, Harujuki, in Intermetallic Compounds: Vol. 2. Practice, edited by Westbrook, J. H. and Fleischer, R.L., John Wiley & Sons Ltd, 1994, p. 147.Google Scholar
3. Pettifor, D. G., Journal of Physics C 19, p. 285 (1986).Google Scholar
4. Zhang, S., Nic, J. P., and Mikkola, D. E., Scripta Metall. 24, p. 57 (1990).Google Scholar
5. Che, Xiaozhou, Wang, Qian, and Hu, Gengxiang, Scirpta Metall, et. Mater., 33, p. 2019 (1995).Google Scholar
6. Stern, E. A. and Heald, S. M., in Handbook on Synchrotron Radiation. Vol. 1, edited by Koch, E. E., North-Holland, Amsterdam, 1983, p. 955.Google Scholar
7. Chen, Jinmin, Frazier, W. E., and Barrera, E. V., accepted by Journal of Materials Research, 1996.Google Scholar
8. Chen, Jinmin, Master Thesis, Rice University, 1997.Google Scholar