Metrology of Very Thin Silicon Epitaxial Films using Spectroscopic Ellipsometry

Published online by Cambridge University Press:  03 September 2012

Weize Chen  and
Rafael Reif
Weize Chen
Affiliation:
Department of Materials Science and Engineering.
Rafael Reif
Affiliation:
Department of Electrical Engineering and Computer Science Massachusetts Institute of Technology, Cambridge, MA 02139.
Get access

Abstract

Non-destructive silicon epitaxial film thickness measurements have been performed using spectroscopic ellipsometry (SE) in the visible to near infrared range. The epitaxial films were grown by CVD at 700 – 900°C. It is shown that SE can simultaneously determine the epitaxial film thickness, the native oxide thickness, and the substrate dopant concentration. The epitaxial film thicknesses measured by SE are in excellent agreement with results of secondary ion mass spectrometry (SIMS). The dopant concentrations measured by SE also agree well with SIMS results for n-type substrates, but are consistently higher than SIMS values for p-type substrates. This study shows that spectroscopic ellipsometry could be used in semiconductor manufacturing environments as a viable non-destructive technique for sub-0.5 μm silicon epitaxial film thickness measurement.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 448: Symposium M – Control of Semiconductor Surfaces and Interfaces , 1996 , 493
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Krishnan, K. and Stout, P. J., in Practical Fourier Transform Infrared Spectroscopy, edited by Ferraro, J. R. and Krishnan, K., (Academic, Orlando 1990).Google Scholar
2 Yang, I., Yu, F. and Reif, R., Zhou, Z. H., J. Appl. Phys., 73, 7331, (1993).Google Scholar
3 Drévillon, B., Prog. Cryst. Growth Charact, 27, 1, (1993).Google Scholar
4 Aspnes, D. E. and Studna, A. A., Appl. Opt. 14, 220, 1975.Google Scholar
5 Palik, E. D., Handbook of Optical Constants of Solids (Academic Press, Inc. New York, 14, 1985) p. 749 p. 547.Google Scholar
6 Jellison, G. E. Jr., Optical Materials, 1, 41 (1992).Google Scholar
7 Beadle, W. E., Tsai, J. C. C. andPlummer, R. D., Quick Reference Manual for Silicon Integrated Circuit Technology, (Wiley, New York, 1992) 2–68.Google Scholar
8 Aspnes, D. E., Studna, A. A., and Kinsbron, E., Phys. Rev. B 29, (1984).Google Scholar
9 Jellison, G. E. Jr., Withrow, S. P., McCamy, J. W., Budai, J. D., Lubben, D., and God-bole, M. J., Phys. Rev. B 52, 14607 (1995).Google Scholar
10 van Driel, H. M., Appl. Phys. Lett. 44, 617 (1984).Google Scholar