Metallurgical and Corrosion Studies of Modified T91 Grade steel
Published online by Cambridge University Press: 01 February 2011
Abstract
Modified 9Cr-1Mo steels containing different Silicon (Si) content have been tested for evaluation of their metallurgical and corrosion properties. The results of tensile testing indicated reduced failure strain up to 400°C followed by its enhancement at a higher temperature. Stress corrosion cracking tests at constant load did not show any failure in any materials. However, reduced ductility and true failure stress were noted in slow strain rate (SSR) testing, indicating increased cracking susceptibility at elevated temperatures. The corrosion potential became more active with increasing temperature in polarization studies. A combination of intergranular and cleavage failures was observed in specimens tested by the SSR technique.
- Type
- Research Article
- Information
- MRS Online Proceedings Library (OPL) , Volume 929: Symposium II – Materials in Extreme Environments , 2006 , 0929-II05-02
- Copyright
- Copyright © Materials Research Society 2006